Reclamation of molybdenum or other heavy metals from wastewater treatment skimmings
Assignee: Dravo Corp
•
Filing: 1979-02-27
•
Granted: 1980-09-16
•
Expires: 1999-02-27
Abstract
Abstract Molybdenum or other heavy metal anions and ferric sulfate are reclaimed from wastewater skimmings, that result from treatment of wastewaters through formation of insoluble heavy metal ferric salts and flotation, by treating the skimmings with aqueous caustic at 150°-225° F. to form a solution of the heavy metal anions and a residual solids fraction, separating the solids and contacting the residual solids with sulfuric acid to produce ferric sulfate.
Inventors
- 👤 Ernest R. Ramirez
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 01:44
CPC Classifications
C; C02; C02F; C02F9/00; C02F1/00; C02F1/52; C02F1/5236; C02F1/5245; C22; C22B; C22B34/00; C22B34/30; C22B7/00; C22B7/006; C22B7/007; C22B7/008; C02F1/02; C02F2101/00; C02F2101/10; C02F2101/20; C02F2209/00; C02F2209/02; Y; Y02; Y02P; Y02P10/00; Y02P10/20
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
135 words
A process for the reclamation of heavy metal anions selected from the group consisting of tungsten, molybdenum, chromium, and arsenic anions, and ferric sulfate from wastewater skimmings resulting from the precipitation of said heavy metal anions from wastewater, by contact with ferric sulfate and formation of insoluble ferric heteropoly molybdate, tungstate, chromate and arsenate salts, followed by gas flotation and separation of said wastewater skimmings comprising: (a) contacting said wastewater skimmings with an aqueous caustic at a temperature of 150°-225° F. for a period of time to form a solution of said heavy metal anions and a residual solids fraction which includes the ferric content of the skimmings; (b) separating the solution of heavy metal anions so produced from said residual solids; and (c) contacting said residual solids with sulfuric acid to produce ferric sulfate.
Claim 2
Dependent Claim
135 words
A process for the reclamation of heavy metal anions selected from the group consisting of tungsten, molybdenum, chromium, and arsenic anions, and ferric sulfate from wastewater skimmings resulting from the precipitation of said heavy metal anions from wastewater, by contact with ferric sulfate and formation of insoluble ferric heteropoly molybdate, tungstate, chromate and arsenate salts, followed by gas flotation and separation of said wastewater skimmings comprising: (a) contacting said wastewater skimmings with an aqueous caustic at a temperature of 150°-225° F. for a period of time to form a solution of said heavy metal anions and a residual solids fraction which includes the ferric content of the skimmings; (b) separating the solution of heavy metal anions so produced from said residual solids; and (c) contacting said residual solids with sulfuric acid to produce ferric sulfate.
Claim 3
Dependent Claim
44 words
The process for the reclamation of heavy metal anions and ferric sulfate from wastewater skimmings as defined in claim 1 wherein a portion of the water contained within the wastewater skimmings is removed therefrom prior to contact of the skimmings with the aqueous caustic.
Claim 4
Dependent Claim
42 words
The process for the reclamation of heavy metal anions and ferric sulfate from wastewater skimmings as defined in claim 1 wherein the ferric sulfate produced by said contact of residual solids with sulfuric acid is recycled for production of additional wastewater skimmings.
Claim 5
Dependent Claim
35 words
The process for the reclamation of heavy metal anions and ferric sulfate from wastewater skimmings as defined in claim 1 wherein said aqueous caustic is in the concentration range of 0.5 molar to 1 molar.
Claim 6
Dependent Claim
38 words
The process for the reclamation of heavy metal anions and ferric sulfate from wastewater skimmings as defined in claim 1 wherein said aqueous caustic is contacted with the wastewater skimmings for a period of thirty to sixty minutes.
Claim 7
Dependent Claim
37 words
The process for the reclamation of heavy metal anions and ferric sulfate from wastewater skimmings as defined in claim 1 wherein said sulfuric acid is contacted with the residual solids at a temperature of between 150°-220° F.
Claim 8
Dependent Claim
34 words
The process for the reclamation of heavy metal anions and ferric sulfate from wastewater skimmings as defined in claim 6 wherein said sulfuric acid is at a concentration of about 50 percent by weight.
Claim 9
Dependent Claim
138 words
A process for the reclamation of molybdenum anions and ferric sulfate from wastewater skimmings resulting from the precipitation of said molybdenum from wastewater, by contact with ferric sulfate and formation of insoluble ferric heteropoly molybdate salts followed by gas flotation and separation of said wastewater skimmings comprising: (a) dewatering said wastewater skimmings to remove a portion of water therefrom; (b) contacting said dewatered wastewater skimmings with an aqueous caustic at a temperature of 150°-225° F. for a period of fifteen to sixty minutes to form a solution of said molybdenum anions and a residual solids fraction; (c) separating the solution of molybdenum anions so produced from said residual solids by filtration; and (d) contacting said residual solids with sulfuric acid at a temperature of 180°-220° F. for a period of thirty to ninety minutes to produce ferric sulfate.
Claim 10
Dependent Claim
138 words
A process for the reclamation of molybdenum anions and ferric sulfate from wastewater skimmings resulting from the precipitation of said molybdenum from wastewater, by contact with ferric sulfate and formation of insoluble ferric heteropoly molybdate salts followed by gas flotation and separation of said wastewater skimmings comprising: (a) dewatering said wastewater skimmings to remove a portion of water therefrom; (b) contacting said dewatered wastewater skimmings with an aqueous caustic at a temperature of 150°-225° F. for a period of fifteen to sixty minutes to form a solution of said molybdenum anions and a residual solids fraction; (c) separating the solution of molybdenum anions so produced from said residual solids by filtration; and (d) contacting said residual solids with sulfuric acid at a temperature of 180°-220° F. for a period of thirty to ninety minutes to produce ferric sulfate.
References Cited (Backward Citations)
US1250063A
Cited
US3347786A
Cited
US3268443A
Cited
US3575853A
Cited
US3725266A
Cited
US4036941A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-09-16 | 1984-03-17 | 1984-09-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-09-16 | 1988-03-17 | 1988-09-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-09-16 | 1992-03-17 | 1992-09-16 | $7700.00 | Window Closed / Lapsed |