Adhesion of vinyl plastisol coatings
Assignee: EIDP Inc
•
Filing: 1977-08-12
•
Granted: 1981-03-03
•
Expires: 1997-08-12
Abstract
Abstract Vinyl dispersion coating compositions comprising (A) 10-40 parts by weight particulate vinyl resin; (B) 5-80 parts by weight liquid plasticizer; (C) 1-20 parts by weight adhesion promotor comprising (i) a thermoplastic phenol-formaldehyde condensate made with molar excess of the phenol and (ii) a compound that provides low molecular weight difunctional linking moieties with increase in temperature, wherein the molar ratio of the linking moieties releasable by (ii) to the total of hydrogen substituted ortho and para positions in (i) is at least about 3:4, preferably 1:1 or greater, and the weight ratio of (A) to (C) is about 40:1-1:1. Preferred plastisol sealing compositions can exhibit improvements in adhesion to hydrophilic surfaces such as glass by as much as up to five times or greater than with conventional adhesion promoters.
Inventors
- 👤 Richard E. Robertson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 12:54
CPC Classifications
C; C09; C09D; C09D127/00; C09D127/02; C09D127/04; C09D127/06; C08; C08K; C08K5/00; C08K5/04; C08K5/10; C08K5/11; C08L; C08L61/00; C08L61/04; C08L61/06; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31551; Y10T428/31627
Claims Analysis
Total Claims: 3
Claim 1
Independent Claim
187 words
A method for adhering a vinyl dispersion coating to a hydrophilic substrate wherein at least a portion of the coating comprises a layer up to 20 mils in thickness, comprising applying to the substrate a composition comprising: (A) about 10-40 parts by weight particulate vinyl chloride homopolymer, copolymer or mixture thereof dispersion resin having a majority of particles with diameters below about 10 microns; (B) about 5-80 parts by weight liquid plasticizer; (C) about 1-20 parts by weight of adhesion promotor consisting essentially of: (i) thermoplastic phenol-formaldehyde condensate made having an excess number of moles of the phenol per mole of formaldehyde and having a number average molecular weight between about 500-5000; (ii) a compound that produces low molecular weight difunctional linking moieties with heat selected from the group consisting of hexamethylenetetramine, adducts of hexamethylenetetramine, paraformaldehyde, paraaldehyde and adducts of formaldehyde, wherein the ratio of moles of the linking moieties produced by (ii) to the moles of ortho and para positions to hydroxy in (i) is in a range of about 3:4-10:1 and the weight ratio of (A) to (C) is in a range between about 40:1-1:1.
Claim 2
Independent Claim
187 words
A method for adhering a vinyl dispersion coating to a hydrophilic substrate wherein at least a portion of the coating comprises a layer up to 20 mils in thickness, comprising applying to the substrate a composition comprising: (A) about 10-40 parts by weight particulate vinyl chloride homopolymer, copolymer or mixture thereof dispersion resin having a majority of particles with diameters below about 10 microns; (B) about 5-80 parts by weight liquid plasticizer; (C) about 1-20 parts by weight of adhesion promotor consisting essentially of: (i) thermoplastic phenol-formaldehyde condensate made having an excess number of moles of the phenol per mole of formaldehyde and having a number average molecular weight between about 500-5000; (ii) a compound that produces low molecular weight difunctional linking moieties with heat selected from the group consisting of hexamethylenetetramine, adducts of hexamethylenetetramine, paraformaldehyde, paraaldehyde and adducts of formaldehyde, wherein the ratio of moles of the linking moieties produced by (ii) to the moles of ortho and para positions to hydroxy in (i) is in a range of about 3:4-10:1 and the weight ratio of (A) to (C) is in a range between about 40:1-1:1.
Claim 3
Dependent Claim
29 words
The method in accordance with claim 1, wherein (i) comprises a crosslinkable thermoplastic having a number average molecular weight in a range between about 600-1500 and (ii) comprises hexamethylenetetramine.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-03-02 | 1984-09-01 | 1985-03-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-03-02 | 1988-09-01 | 1989-03-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-03-02 | 1992-09-01 | 1993-03-03 | $7700.00 | Window Closed / Lapsed |