Method of manufacturing of honeycomb noise attenuation structure and the structure resulting therefrom
Assignee: Rohr Inc
•
Filing: 1979-10-29
•
Granted: 1981-05-26
•
Expires: 1999-10-29
Abstract
Abstract Method of fabricating attenuation sandwich panels having a central cellular core positioned between and bonded to an imperforate facing sheet on one surface thereof and a perforate facing sheet with an outer layer of porous fibrous material adhered to the other surface. The combined perforate sheet and porous fibrous material have a predetermined open surface area prior to attenuation panel fabrication. The perforation exposed surface of the combined perforate sheet and porous fibrous material is covered with a maskant material which covers the surface only. The porous fibrous surface is then saturated with a liquidous anti-wetting solution which coats substantially all of the fibers. The solution is allowed to dry and the maskant is then removed from the opposite surface. The components making up the panel are then assembled and bonded together to form the attenuation panel.
Inventors
- 👤 Robert M. Carrillo
- 👤 Muriel L. Koss
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 23:41
CPC Classifications
B; B32; B32B; B32B3/00; B32B3/10; B32B3/12; G; G10; G10K; G10K11/00; G10K11/16; G10K11/172; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24149; Y10T428/24165; Y10T428/24273; Y10T428/24322; Y10T428/24331; Y10T428/24802; Y10T428/24826; Y10T428/249921; Y10T428/249953; Y10T428/249962
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
135 words
A process for manufacturing an improved acoustic sandwich panel for attenuating a wide range of noise frequencies which is suitable structurally for use in a severe environment, said sandwich panel including a central cellular core positioned between an imperforate facing sheet and a perforated facing sheet having a plurality of perforations therethrough, the opposite side of the perforated sheet from said central cellular core having a single thin layer of porous fibrous material bonded thereto wherein a predetermined flow through resistance from the outer surface of said sandwich panel to cells of said central cellular core is established, the steps of the process comprising: (a) cleaning and degreasing the imperforate sheet, central cellular core, perforate facing sheet and single thin layer of porous fibrous material; (b) applying a non-conductive coating on the perforate sheet surfaces;
Claim 2
Dependent Claim
135 words
A process for manufacturing an improved acoustic sandwich panel for attenuating a wide range of noise frequencies which is suitable structurally for use in a severe environment, said sandwich panel including a central cellular core positioned between an imperforate facing sheet and a perforated facing sheet having a plurality of perforations therethrough, the opposite side of the perforated sheet from said central cellular core having a single thin layer of porous fibrous material bonded thereto wherein a predetermined flow through resistance from the outer surface of said sandwich panel to cells of said central cellular core is established, the steps of the process comprising: (a) cleaning and degreasing the imperforate sheet, central cellular core, perforate facing sheet and single thin layer of porous fibrous material; (b) applying a non-conductive coating on the perforate sheet surfaces;
Claim 3
Dependent Claim
198 words
(c) applying a layer of a solvent base first adhesive to one side of the perforated sheet; (d) removing the solvent from the layer of said solvent base first adhesive; (e) securing together the solvent base first adhesive coated surface of the perforate sheet and the thin sheet of porous fibrous material under a positive pressure; (f) curing the solvent base first adhesive and removing the positive pressure; (g) covering the perforation exposed surface including the perforations of the combined perforated facing sheet and single thin sheet of porous fibrous material with a maskant; (h) coating the fibers of the thin sheet of porous fibrous material and the perforated sheet surface adjacent thereto with an anti-wetting agent; (i) removing the maskant; (j) applying a layer of a second adhesive between the imperforate sheet and the central cellular core and between the perforation exposed surface of the combined perforated sheet and thin layer of porous fibrous material and the central cellular core; (k) securing together the imperforate sheet, central cellular core and combined perforated facing sheet and thin single sheet of porous fibrous material under a positive pressure; and (l) curing the second adhesive and removing the positive pressure.
Claim 4
Dependent Claim
198 words
(c) applying a layer of a solvent base first adhesive to one side of the perforated sheet; (d) removing the solvent from the layer of said solvent base first adhesive; (e) securing together the solvent base first adhesive coated surface of the perforate sheet and the thin sheet of porous fibrous material under a positive pressure; (f) curing the solvent base first adhesive and removing the positive pressure; (g) covering the perforation exposed surface including the perforations of the combined perforated facing sheet and single thin sheet of porous fibrous material with a maskant; (h) coating the fibers of the thin sheet of porous fibrous material and the perforated sheet surface adjacent thereto with an anti-wetting agent; (i) removing the maskant; (j) applying a layer of a second adhesive between the imperforate sheet and the central cellular core and between the perforation exposed surface of the combined perforated sheet and thin layer of porous fibrous material and the central cellular core; (k) securing together the imperforate sheet, central cellular core and combined perforated facing sheet and thin single sheet of porous fibrous material under a positive pressure; and (l) curing the second adhesive and removing the positive pressure.
Claim 5
Dependent Claim
32 words
The process for manufacture as defined in claim 1, wherein the step of applying a non-conductive coating comprises the steps of first anodizing and then priming the surfaces of the perforated sheet.
Claim 6
Dependent Claim
25 words
The process for manufacture as defined in claim 1, wherein the coating as set forth in step (h), including coating the walls of the perforations.
Claim 7
Dependent Claim
11 words
The product produced from the process of claims 1 or 2.
References Cited (Backward Citations)
US3166149A
Cited
US3088859A
Cited
US3502171A
Cited
US3821999A
Cited
US4025681A
Cited
US4054477A
Cited
US4084367A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-05-25 | 1984-11-24 | 1985-05-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-05-25 | 1988-11-24 | 1989-05-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-05-25 | 1992-11-24 | 1993-05-26 | $7700.00 | Window Closed / Lapsed |