US4271044A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Carrier matrix for catalysts and process for its production
Assignee: Evonik Operations GmbH
•
Filing: 1979-12-11
•
Granted: 1981-06-02
•
Expires: 1999-12-11
Abstract
Abstract Monolithic carrier matrixes are formed from high grade steel, consisting of alternating smooth and corrugated layers of sheet metal and/or screen cloth, which may be combined with layers of smooth screen cloth or of smooth or corrugated sheet metal, wherein the layers may be coated on their surfaces with a catalysis-promoting carrier material. These carrier matrixes may be used to produce catalysts for the purification of exhaust gases.
Inventors
- 👤 Gerhard Fratzer
- 👤 Bernhard Beck
- 👤 Erwin Dold
- 👤 Hans Klebe
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 10:50
CPC Classifications
B; B01; B01D; B01D53/00; B01D53/34; B01D53/92; B01D53/94; B01D53/9445; B01D53/9454; B01J; B01J35/00; B01J35/50; B01J35/58; F; F01; F01N; F01N3/00; F01N3/08; F01N3/10; F01N3/24; F01N3/28; F01N3/2803; F01N3/2807; F01N3/2839; F01N3/2853; B01J35/56; F01N2330/00; F01N2330/02; F01N2330/12; Y; Y02; Y02T; Y02T10/00; Y02T10/10; Y02T10/12
Claims Analysis
Total Claims: 48
Claim 1
Independent Claim
93 words
A carrier matrix for catalysts with flow-channels passing there through, with cross-flow effect as well as with enlarged geometric surface and improved retaining capacity as compared to catalysis-promoting carrier materials present in dip dispersion, comprising alternately smooth and corrugated, superposed layers of high temperature resistant and scale-resistant steel, wherein a layer of corrugated sheet metal alternates with a layer of smooth screen cloth, or one layer of smooth sheet metal alternates with a layer of corrugated screen cloth, or a layer of corrugated screen cloth alternates with a layer of smooth screen cloth.
Claim 2
Dependent Claim
93 words
A carrier matrix for catalysts with flow-channels passing there through, with cross-flow effect as well as with enlarged geometric surface and improved retaining capacity as compared to catalysis-promoting carrier materials present in dip dispersion, comprising alternately smooth and corrugated, superposed layers of high temperature resistant and scale-resistant steel, wherein a layer of corrugated sheet metal alternates with a layer of smooth screen cloth, or one layer of smooth sheet metal alternates with a layer of corrugated screen cloth, or a layer of corrugated screen cloth alternates with a layer of smooth screen cloth.
Claim 3
Dependent Claim
17 words
A carrier matrix as in claim 1, wherein the sheet metal has a thickness below 0.15 mm.
Claim 4
Dependent Claim
31 words
A carrier matrix as in claim 1 or 2, wherein the screen cloth has a mesh size of 0.18 to 0.025 mm and a wire gauge of 0.15 to 0.025 mm.
Claim 5
Dependent Claim
31 words
A carrier matrix as in claims 1 or 2, wherein the individual flow channels, formed by the smooth and corrugated layers, have a cross section of below 1.5 mm 2 .
Claim 6
Dependent Claim
28 words
A carrier matrix as in claims 1 or 2 wherein the smooth and corrugated layers are wound into a cylinder with spiral-shaped cross section, having numerous flow channels.
Claim 7
Dependent Claim
109 words
A carrier matrix for catalysts with cross flow effect as well as with an enlarged geometric surface and improved retaining capacity as compared to catalysis promoting metal oxides present in dip dispersions, comprising superposed layers of high temperature and scale resistant steel, wherein the layers are formed of a smooth screen cloth, into which supporting wires of a larger cross section that the screen cloth are woven on or in at parallel distances in the direction of the desired flow channels, or in that layers of smooth screen cloth, or smooth corrugated sheet metal alternate with layers of smooth screen cloth with supporting wires woven correspondingly in or on.
Claim 8
Dependent Claim
109 words
A carrier matrix for catalysts with cross flow effect as well as with an enlarged geometric surface and improved retaining capacity as compared to catalysis promoting metal oxides present in dip dispersions, comprising superposed layers of high temperature and scale resistant steel, wherein the layers are formed of a smooth screen cloth, into which supporting wires of a larger cross section that the screen cloth are woven on or in at parallel distances in the direction of the desired flow channels, or in that layers of smooth screen cloth, or smooth corrugated sheet metal alternate with layers of smooth screen cloth with supporting wires woven correspondingly in or on.
Claim 9
Dependent Claim
47 words
A carrier matrix as in claim 6, wherein a web of screen cloth provided with the supporting wires, possibly with an additional smooth or corrugated web of screen cloth or sheet metal, is wound into a cylinder with a spiral-shaped cross section and having numerous flow channels.
Claim 10
Dependent Claim
35 words
A carrier matrix as in claim 6 or 7, wherein the screen cloth represents a web with a mesh size of 0.18 to 0.025 mm, and with a wire gauge of 0.15 to 0.025 mm.
Claim 11
Dependent Claim
44 words
A carrier matrix as in claims 6 or 7 wherein the supporting wires have a thickness of at least 0.2 mm whereby the pertinent thickness is determined by the desired dimensions of the flow channels, and by the wire gauge of the screen cloth.
Claim 12
Dependent Claim
33 words
A carrier matrix as in claims 6 or 7 wherein the individual flow channels, formed by the spacing-producing, woven-in or on supporting wires, have a cross section of below 5 mm 2 .
Claim 13
Dependent Claim
34 words
A carrier matrix as in claims 6 or 7 wherein the supporting wires are at least 1 mm and at most 5 mm apart in the plane of the web of the screen cloth.
Claim 14
Dependent Claim
32 words
A carrier matrix as in claims 1, 2, 6 or 7, wherein sheet metal, screen cloth and supporting wires comprise an alloy of iron, chromium, aluminum and possibly also cerium or yttrium.
Claim 15
Dependent Claim
27 words
A carrier matrix as in claim 12, wherein the alloy consists of 15% by weight of chromium, 5% by weight of aluminum and the balance of iron.
Claim 16
Dependent Claim
40 words
A carrier matrix as in claim 12, wherein the alloy consists of up to 15% by weight of chromium, 0.5 to 12% by weight of aluminum, 0.1 to 3% by weight of cerium or yttrium and the balance of iron.
Claim 17
Dependent Claim
42 words
A carrier matrix as in claims 1, 2, 6 or 7 wherein the individual layers are spot welded or altogether welded mutually on the periphery and/or the front face, or in that the last layer is welded together with the preceding layer.
Claim 18
Dependent Claim
16 words
A carrier matrix as in claim 15, wherein the layers are welded together by electron beams.
Claim 19
Dependent Claim
25 words
A carrier matrix as in claims 1, 2, 6 or 7 wherein the layers are coated on their surface with a catalysis promoting carrier material.
Claim 20
Dependent Claim
28 words
A carrier matrix as in claims 1, 2, 6 or 7 disposed as a wound cylinder with spiral-shaped cross-section held in a steel jacket, and/or welded onto it.
Claim 21
Dependent Claim
35 words
A carrier matrix as in claims 1, 2, 6 or 7 wherein the individual layers wound up sprial-shaped are secured against shifting by mooring rings fixedly disposed at the front faces of the steel jacket.
Claim 22
Dependent Claim
48 words
A process for the production of a carrier matrix as in claims 17 wherein the surface of the smooth and corrugated layers or the web of the screen cloth provided with the supporting wires are coated with a catalysis-promoting carrier material prior to winding up into a cylinder.
Claim 23
Dependent Claim
48 words
A process for the production of a carrier matrix as in claim 18 wherein the surface of the smooth and corrugated layers or the web of the screen cloth provided with the supporting wires are coated with a catalysis-promoting carrier material prior to winding up into a cylinder.
Claim 24
Dependent Claim
50 words
A process as in claim 20, wherein the smooth and corrugated layers or the web of screen cloth provided with the supporting wires are heated in an oxygen-containing gas under conditions of temperature and time, whereby a surface-layer of aluminum oxide is developed from the aluminum contained in the alloy.
Claim 25
Dependent Claim
49 words
A process as in claim 22 wherein the smooth and corrugated layers or the web of screen cloth provided with supporting wires after development of the aluminum oxide coating is coated additionally by the wash-coat process with additional catalysis promoting carrier material of the same or different chemical composition.
Claim 26
Dependent Claim
65 words
A process as in claim 20, wherein the smooth and corrugated layers or the web of screen cloth provided with supporting wires is first coated by the wash-coat process with catalysis promoting carrier material and the coated material is then heated in an oxygen-containing gas under conditions of time and temperature under which aluminum oxide is oxidized out from the aluminum contained in the alloy.
Claim 27
Dependent Claim
28 words
A process as in claims 22, 23 or 24 wherein aluminum oxide is oxidized out of the alloy by heating in the air at temperatures of 750°-1100° C.
Claim 28
Dependent Claim
56 words
A process as in claims 20, 22, 23 or 24 wherein the smooth and corrugated layers or the web of screen cloth provided with supporting wires are wound up into the cylinder with spiral-shaped cross section, and in that the latter is pressed under pre-stress into a steel jacket and is possibly welded on in it.
Claim 29
Dependent Claim
50 words
A process as in claim 21, wherein the smooth and corrugated layers or the web of screen cloth provided with the supporting wires are heated in an oxygen-containing gas under conditions of temperature and time, whereby a surface-layer of aluminum oxide is developed from the aluminum contained in the alloy.
Claim 30
Dependent Claim
49 words
A process as in claim 27 wherein the smooth and corrugated layers or the web of screen cloth provided with supporting wires after development of the aluminum oxide coating is coated additionally by the wash-coat process with additional catalysis promoting carrier material of the same or different chemical composition.
Claim 31
Dependent Claim
65 words
A process as in claim 21, wherein the smooth and corrugated layers or the web of screen cloth provided with supporting wires is first coated by the wash-coat process with catalysis promoting carrier material and the coated material is then heated in an oxygen-containing gas under conditions of time and temperature under which aluminum oxide is oxidized out from the aluminum contained in the alloy.
Claim 32
Dependent Claim
28 words
A process as in claims 27, 28 or 29 wherein aluminum oxide is oxidized out of the alloy by heating in the air at temperatures of 750°-1100° C.
Claim 33
Dependent Claim
55 words
A process as in claims 27, 28 or 29 wherein the smooth and corrugated layers or the web of screen cloth provided with supporting wires are wound up into the cylinder with spiral-shaped cross section, and in that the latter is pressed under prestress into a steel jacket and is possibly welded on in it.
Claim 34
Dependent Claim
38 words
A cylinder shaped carrier matrix coated adhesively with at least one catalysis promoting metal oxide and possibly sheathed with a steel jacket, with a spiral-shaped cross section, formed according to the process claims 20, 22, 23 or 24.
Claim 35
Dependent Claim
45 words
Use of a carrier matrix as defined in claims 1, 2, 6 or 7 for the production of catalysts which are deposited on catalysis promoting carrier material as intermediate carriers, especially for the purification of the exhaust gases of internal combustion engines and industrial installations.
Claim 36
Dependent Claim
39 words
A cylinder shaped carrier matrix coated adhesively with at least one catalysis promoting metal oxide and possibly sheathed with a steel jacket, with a spiral-shaped cross section, formed according to the process of claims 21, 27, 28 or 29.
Claim 37
Dependent Claim
37 words
A carrier matrix as in claims 1, 2, 6 or 7 having deposited thereon a sufficient amount of a catalytically active material so that the matrix may function as a catalyst for the purification of exhaust gases.
Claim 38
Dependent Claim
34 words
A carrier matrix as in claim 17 which additionally has deposited thereon a catalytically active material in sufficient amount so that the matrix may function as a catalyst for the purification of exhaust gases.
Claim 39
Dependent Claim
30 words
A carrier matrix as defined in claim 3 wherein the screen cloth has a mesh size of 0.1 to 0.05 mm and a wire gauge of 0.1 to 0.05 mm.
Claim 40
Dependent Claim
26 words
A carrier matrix as defined in claim 3 wherein the screen cloth has a mesh size of 0.073 mm and a wire gauge of 0.07 mm.
Claim 41
Dependent Claim
30 words
A carrier matrix as defined in claim 8 wherein the screen cloth has a mesh size of 0.1 to 0.05 mm and a wire gauge of 0.1 to 0.05 mm.
Claim 42
Dependent Claim
26 words
A carrier matrix as defined in claim 8 wherein the screen cloth has a mesh size of 0.073 mm and a wire gauge of 0.07 mm.
Claim 43
Dependent Claim
20 words
A carrier matrix as defined in claim 9 wherein the supporting wires have a thickness of 0.4 to 1.5 mm.
Claim 44
Dependent Claim
26 words
A process as defined in claim 25 wherein the temperature is 900° to 1,000° C. and the process is carried out for 1 to 7 hours.
Claim 45
Dependent Claim
24 words
The process as defined in claim 30 wherein the aluminum oxide is heated at 900° C. to 1,000° C. for 1 to 7 hours.
Claim 46
Dependent Claim
32 words
A carrier matrix provided on the surface thereof with a coating of a catalysis promoting high surface area carrier material, said matrix being defined as in claims 1, 2, 6 or 7.
Claim 47
Dependent Claim
43 words
A carrier matrix as defined in claims 1, 2, 6 or 7 having formed on the surfaces thereof a layer of a catalytically active aluminum oxide which functions to promote catalysis in the conversion of harmful components in exhaust gases into harmless components.
Claim 48
Dependent Claim
49 words
A carrier matrix defined in claims 1, 2, 6 or 7 which has formed on the surfaces thereof a catalysis promoting material which is formed on the surfaces thereof by heating, and which additionally has an aluminum oxide coating applied from an aqueous dispersion containing catalytically active aluminum oxide.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-06-01 | 1984-12-01 | 1985-06-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-06-01 | 1988-12-01 | 1989-06-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-06-01 | 1992-12-01 | 1993-06-02 | $7700.00 | Window Closed / Lapsed |