Polysiloxane-modified paint binders and process for producing the binders
Assignee: Allnex Austria GmbH
•
Filing: 1978-12-19
•
Granted: 1981-07-14
•
Expires: 1998-12-19
Abstract
Abstract Paint binders having an intrinsic viscosity of from 8-15 ml/g which are water soluble upon neutralization with bases comprising the condensation reaction product of (A) 50-85% by weight of a polyester resin modified with 5-40% by weight of a polysiloxane of the general formula ##STR1## wherein R is an alkyl, cycloalkyl, aryl or alkoxy radical, R 1 is hydrogen or an alkyl radical and n is an integer of from 0-40; said modified polyester having a hydroxyl number of from about 50-400 mg KOH/g, an acid value of below about 10 mg KOH/g, and an intrinsic viscosity of from about 6-11 ml/g, measured in dimethylformamide at 20° C.; and (B) 15-50% by weight of a film forming resin containing carboxyl groups to provide an acid value of from about 100-300 mg KOH/g and an intrinsic viscosity of from about 5-9 ml/g, measured in dimethylformamide at 20° C.; the ratio of the intrinsic viscosity values of components (A) and (B) being governed by the relation ηA/ηB=1.2 to 2.2. The paint binders, at a high solids content and with a high water to organic solvent ratio, have a viscosity sufficiently low to be suitable for spray applications. The paint binders in paint formulations provide paint films having good physical characteristics.
Inventors
- 👤 Gert Dworak
- 👤 Hansjorg Aigner
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 14:25
CPC Classifications
C; C08; C08G; C08G63/00; C08G63/68; C08G63/695; C09; C09D; C09D167/00
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
242 words
A process for producing paint binders water soluble upon neutralization with bases wherein (A) 50-85% by weight of a polyester resin containing chemically bonded thereto from 5-40% by weight of a polysiloxane of the general formula ##STR4## wherein R is an alkyl, cycloalkyl, aryl or alkoxy radical, R 1 is hydrogen or an alkyl radical and n is an integer of from 0-40; said polyester having a hydroxyl number of from about 50-400 mg KOH/g, an acid value of below about 10 mg KOH/g, and an intrinsic viscosity of from about 6-11 ml/g, measured in dimethylformamide at 20° C.; and (B) 15-50% by weight of a film forming resin selected from the group consisting of (a) addition products of maleic anhydride to unsaturated fatty acids or their esters of their dehydrated or isomerized derivatives, (b) copolymers of maleic anhydride with other alpha, beta-ethylenically unsaturated monomers, and (c) polyester resins prepared by using a stoichiometric excess of polycarboxylic acids, whereby the anhydride groups of (a) and (b) are opened by hydrolysis or semiester formation with monohydric alcohols; said resin containing carboxyl groups to provide an acid value of from about 100-300 mg KOH/g and an intrinsic viscosity of from about 5-9 ml/g, measured in dimethylformamide at 20° C.; the ratio of the intrinsic viscosity values of components (A) and (B) being governed by the relation ηA/ηB=1.2 to 2.2, are condensed at about 80°-150° C. to an intrinsic viscosity of from about 8-15 ml/g.
Claim 2
Dependent Claim
242 words
A process for producing paint binders water soluble upon neutralization with bases wherein (A) 50-85% by weight of a polyester resin containing chemically bonded thereto from 5-40% by weight of a polysiloxane of the general formula ##STR4## wherein R is an alkyl, cycloalkyl, aryl or alkoxy radical, R 1 is hydrogen or an alkyl radical and n is an integer of from 0-40; said polyester having a hydroxyl number of from about 50-400 mg KOH/g, an acid value of below about 10 mg KOH/g, and an intrinsic viscosity of from about 6-11 ml/g, measured in dimethylformamide at 20° C.; and (B) 15-50% by weight of a film forming resin selected from the group consisting of (a) addition products of maleic anhydride to unsaturated fatty acids or their esters of their dehydrated or isomerized derivatives, (b) copolymers of maleic anhydride with other alpha, beta-ethylenically unsaturated monomers, and (c) polyester resins prepared by using a stoichiometric excess of polycarboxylic acids, whereby the anhydride groups of (a) and (b) are opened by hydrolysis or semiester formation with monohydric alcohols; said resin containing carboxyl groups to provide an acid value of from about 100-300 mg KOH/g and an intrinsic viscosity of from about 5-9 ml/g, measured in dimethylformamide at 20° C.; the ratio of the intrinsic viscosity values of components (A) and (B) being governed by the relation ηA/ηB=1.2 to 2.2, are condensed at about 80°-150° C. to an intrinsic viscosity of from about 8-15 ml/g.
Claim 3
Dependent Claim
22 words
Process according to claim 1 wherein components (A) and (B) are used in amounts of from about 65-80% to about 20-35%, respectively.
Claim 4
Dependent Claim
21 words
Process according to claim 1 wherein component (A) is an alkyd resin modified with alkylphenylsiloxanes containing from 10-20% of methoxy groups.
Claim 5
Dependent Claim
15 words
Process according to claim 3 wherein said alkylphenylsiloxanes further contain from 5-10% of butoxy groups.
Claim 6
Dependent Claim
19 words
Process according to claim 1 wherein component (B) is an addition product of maleic anhydride and unsaturated fatty acids.
Claim 7
Dependent Claim
18 words
Process according to claim 1 wherein component (B) is an addition product of natural oils and their derivatives.
Claim 8
Dependent Claim
28 words
Process according to claim 1 wherein component (B) is a copolymer of maleic anhydride and a member of the group consisting of (meth)acrylate; styrene, vinyltoluene, and mixtures thereof.
Claim 9
Dependent Claim
15 words
Process according to claim 1 wherein component (B) is a polyester with free carboxy groups.
Claim 10
Dependent Claim
28 words
Process according to claim 1 wherein the acid value of the blend of components (A) and (B) during condensation falls by a maximum of 15 acid value units.
Claim 11
Dependent Claim
237 words
Paint binders having an intrinsic viscosity of from about 8-15 ml/g water soluble upon neutralization with bases comprising the condensation reaction product of (A) 50-85% by weight of a polyester resin containing chemically bonded thereto from 5-40% by weight of a polysiloxane of the general formula ##STR5## wherein R is an alkyl, cycloalkyl, aryl or alkoxy radical, R 1 is hydrogen or an alkyl radical and n is an integer of from 0-40; said polyester having a hydroxyl number of from about 50-400 mg KOH/g, an acid value of below about 10 mg KOH/g, and an intrinsic viscosity of from about 6-11 ml/g, measured in dimethylformamide at 20° C.; and (B) 15-50% by weight of a film forming resin selected from the group consisting of (a) addition products of maleic anhydride to unsaturated fatty acids or their esters of their dehydrated or isomerized derivatives, (b) copolymers of maleic anhydride with other alpha, beta-ethylenically unsaturated monomers, and (c) polyester resins prepared by using a stoichiometric excess of polycarboxylic acids, whereby the anhydride groups of (a) and (b) are opened by hydrolysis or semiester formation with monohydric alcohols; said resin containing carboxyl groups to provide an acid value of from about 100-300 mg KOH/g and an intrinsic viscosity of from about 5-9 ml/g, measured in dimethylformamide at 20° C.; the ratio of the intrinsic viscosity values of components (A) and (B) being governed by the relation ηa/ηB=1.2 to 2.2.
Claim 12
Dependent Claim
237 words
Paint binders having an intrinsic viscosity of from about 8-15 ml/g water soluble upon neutralization with bases comprising the condensation reaction product of (A) 50-85% by weight of a polyester resin containing chemically bonded thereto from 5-40% by weight of a polysiloxane of the general formula ##STR5## wherein R is an alkyl, cycloalkyl, aryl or alkoxy radical, R 1 is hydrogen or an alkyl radical and n is an integer of from 0-40; said polyester having a hydroxyl number of from about 50-400 mg KOH/g, an acid value of below about 10 mg KOH/g, and an intrinsic viscosity of from about 6-11 ml/g, measured in dimethylformamide at 20° C.; and (B) 15-50% by weight of a film forming resin selected from the group consisting of (a) addition products of maleic anhydride to unsaturated fatty acids or their esters of their dehydrated or isomerized derivatives, (b) copolymers of maleic anhydride with other alpha, beta-ethylenically unsaturated monomers, and (c) polyester resins prepared by using a stoichiometric excess of polycarboxylic acids, whereby the anhydride groups of (a) and (b) are opened by hydrolysis or semiester formation with monohydric alcohols; said resin containing carboxyl groups to provide an acid value of from about 100-300 mg KOH/g and an intrinsic viscosity of from about 5-9 ml/g, measured in dimethylformamide at 20° C.; the ratio of the intrinsic viscosity values of components (A) and (B) being governed by the relation ηa/ηB=1.2 to 2.2.
Claim 13
Dependent Claim
22 words
Paint binders of claim 10 wherein components (A) and (B) are reacted in amounts of from about 65-80% to about 20-35%, respectively.
Claim 14
Dependent Claim
21 words
Paint binders of claim 10 wherein component (A) is an alkyd resin modified with alkylphenylsiloxanes containing from 10-20% of methoxy groups.
Claim 15
Dependent Claim
15 words
Paint binders of claim 12 wherein said alkylphenylsiloxanes further contain from 5-10% of butoxy groups.
Claim 16
Dependent Claim
19 words
Paint binders of claim 10 wherein component (B) is an addition product of maleic anhydride and unsaturated fatty acids.
Claim 17
Dependent Claim
18 words
Paint binders of claim 10 wherein component (B) is an addition product of natural oils and their derivatives.
Claim 18
Dependent Claim
28 words
Paint binders of claim 10 wherein component (B) is a copolymer of maleic anhydride and a member of the group consisting of (meth)acrylate; styrene, vinyltoluene, and mixtures thereof.
Claim 19
Dependent Claim
15 words
Paint binders of claim 10 wherein component (B) is a polyester with free carboxy groups.
References Cited (Backward Citations)
CA542265A
Cited
US3015637A
Cited
US3655602A
Cited
US3894978A
Cited
US4069178A
Cited
US4032494A
Cited
US4105607A
Cited
US4076666A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-07-13 | 1985-01-12 | 1985-07-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-07-13 | 1989-01-12 | 1989-07-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-07-13 | 1993-01-12 | 1993-07-14 | $7700.00 | Window Closed / Lapsed |