Protective coating for cathodically protected metal surfaces
Assignee: Individual
•
Filing: 1979-12-04
•
Granted: 1981-07-21
•
Expires: 1999-12-04
Abstract
Abstract To provide a cover coating for metal surfaces subject to corrosion by water, typically steel surfaces in salt water, for ships, structural components, and the like, in which cathodic protection by application of a negative voltage to the metal is provided, a two-layer coating is applied in which the base coating applied to the metal comprises a mixture of finely divided zinc and polyisocyanate prepolymers capable of hardening or curing under ambient humidity, with dryers, gelling, and pigment agents, and high boiling point solvents, covered by a cover coating, preferably in two to three layers, of a mixture of tar with polyisocyanates, fillers, dryers, solvents, and micaceous iron ore or hematite powder.
Inventors
- 👤 Rainer-Leo Meyer
- 👤 Rainmar John
- 👤 Bernhard Eisenhauer
- 👤 Herta Baumstark
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 14:20
CPC Classifications
C; C09; C09D; C09D5/00; C09D5/08; C09D5/10; C09D5/106; C08; C08G; C08G18/00; C08G18/06; C08G18/08; C08G18/088; C08G18/0885; C09D175/00; C08G2150/00; C08G2150/90; Y; Y10; Y10T; Y10T428/00; Y10T428/26; Y10T428/29; Y10T428/2982; Y10T428/31504; Y10T428/31511; Y10T428/31515; Y10T428/31529; Y10T428/31551; Y10T428/31554; Y10T428/31609; Y10T428/31678; Y10T428/31717
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
180 words
Protective coating on a cathodically protected metal surface comprising a base coating and a cover coating, in which the base coating includes a zinc powder capable of hardening or curing under ambient air humidity and having a composition, all parts being approximate and by weight, comprising: 6-10 parts polyisocyanate-prepolymer with an NCO content of about 16% and capable of hardening under ambient humidity, 7-9 parts high boiling point aromatic solvent, 0.01-0.03 parts deaeration substance, 0.3-0.8 parts drying and stabilizing substance, 3-6 parts gelling substance, 0.3-0.5 parts wetting agent, 4-7 parts pigment in flake form and 65-75 parts zinc powder and a cover coating which comprises a polyurethane-tar coating capable of hardening under ambient air humidity comprising: 16-20 parts aromatic polyisocyanate with an NCO content of 5-7%, 1-3 parts liquid higher molecular polyisocyanate with an NCO content of 3-4%, 5-20 parts tar with a viscosity of 5600 to 6400 poise/25° C., 6.5-8 parts drying agent, 0.05-0.1 parts deaeration agent, 3.5-4.5 parts precipitation prevention agent, 30-40 parts micaceous iron ore or hematite powder, 5-10 parts inorganic filler, and 2-5 parts stabilizing agent.
Claim 2
Dependent Claim
180 words
Protective coating on a cathodically protected metal surface comprising a base coating and a cover coating, in which the base coating includes a zinc powder capable of hardening or curing under ambient air humidity and having a composition, all parts being approximate and by weight, comprising: 6-10 parts polyisocyanate-prepolymer with an NCO content of about 16% and capable of hardening under ambient humidity, 7-9 parts high boiling point aromatic solvent, 0.01-0.03 parts deaeration substance, 0.3-0.8 parts drying and stabilizing substance, 3-6 parts gelling substance, 0.3-0.5 parts wetting agent, 4-7 parts pigment in flake form and 65-75 parts zinc powder and a cover coating which comprises a polyurethane-tar coating capable of hardening under ambient air humidity comprising: 16-20 parts aromatic polyisocyanate with an NCO content of 5-7%, 1-3 parts liquid higher molecular polyisocyanate with an NCO content of 3-4%, 5-20 parts tar with a viscosity of 5600 to 6400 poise/25° C., 6.5-8 parts drying agent, 0.05-0.1 parts deaeration agent, 3.5-4.5 parts precipitation prevention agent, 30-40 parts micaceous iron ore or hematite powder, 5-10 parts inorganic filler, and 2-5 parts stabilizing agent.
Claim 3
Dependent Claim
42 words
Coating according to claim 1, wherein the gelling substance in the zinc-based coating comprises at least one of the materials selected from the group consisting of: dimethyldioctadecyclammonium-montmorillonite; an organic derivative of montmorillonite derived from montmorillonite by iron exchange reaction with alkylammonium bases.
Claim 4
Dependent Claim
28 words
Coating according to claim 1, wherein the flaked pigment in the zinc-based coating is a finely ground flour of a naturally occurring mixture of muscovite, chlorite and quartz.
Claim 5
Dependent Claim
18 words
Coating according to claim 1, wherein the precipitation prevention agent of the cover coating is finely dispersed clay.
Claim 6
Dependent Claim
15 words
Coating according to claim 1, wherein the filler in the cover coating is microfine talcum.
Claim 7
Dependent Claim
42 words
Coating according to claim 1, wherein the base coating comprises a two-layer coating, each having a dry film thickness of about 75 μm, and the top coating comprises at least two layers, each with a dry film thickness of about 125 μm.
Claim 8
Dependent Claim
14 words
Coating according to claim 1, wherein the tar is present in about 10-12 parts.
Claim 9
Dependent Claim
16 words
Coating according to claim 1, wherein the cover coating includes up to about 10 parts solvent.
Claim 10
Dependent Claim
21 words
Coating according to claim 1, wherein the components are present in quantities approximately midway within the ranges recited in claim 1.
Claim 11
Dependent Claim
159 words
Protective coating on cathodically protected surface comprising a base coating and a cover coating, in which the base coating includes a zinc powder capable of hardening or curing under ambient air humidity and having a composition, all parts being approximate and by weight, comprising: 6-10 parts of an epoxy-type resin, 7-9 parts high boiling point aromatic solvent, 0.01-0.03 parts deaeration substance, 0.03-0.8 parts drying and stabilizing substance, 3-6 parts gelling substance, 0.3-0.5 parts wetting agent, 4-7 parts pigment in flake form and 65-75 parts zinc powder and a cover coating which comprises a polyurethane-tar coating capable of hardening comprising 16-20 parts of an epoxy-type resin, 1-3 parts liquid higher molecular polyisocyanate with an NCO content of 3-4%, 5-20 parts tar with a viscosity of 5600 to 6400 poise/25° C., 6.5-8 parts drying agent, 0.05-0.1 parts deaeration agent, 3.5-4.5 parts precipitation prevention agent, 30-40 parts micaceous iron ore or hematite powder, 5-10 parts inorganic filler, and 2-5 parts stabilizing agent.
Claim 12
Dependent Claim
159 words
Protective coating on cathodically protected surface comprising a base coating and a cover coating, in which the base coating includes a zinc powder capable of hardening or curing under ambient air humidity and having a composition, all parts being approximate and by weight, comprising: 6-10 parts of an epoxy-type resin, 7-9 parts high boiling point aromatic solvent, 0.01-0.03 parts deaeration substance, 0.03-0.8 parts drying and stabilizing substance, 3-6 parts gelling substance, 0.3-0.5 parts wetting agent, 4-7 parts pigment in flake form and 65-75 parts zinc powder and a cover coating which comprises a polyurethane-tar coating capable of hardening comprising 16-20 parts of an epoxy-type resin, 1-3 parts liquid higher molecular polyisocyanate with an NCO content of 3-4%, 5-20 parts tar with a viscosity of 5600 to 6400 poise/25° C., 6.5-8 parts drying agent, 0.05-0.1 parts deaeration agent, 3.5-4.5 parts precipitation prevention agent, 30-40 parts micaceous iron ore or hematite powder, 5-10 parts inorganic filler, and 2-5 parts stabilizing agent.
Claim 13
Dependent Claim
17 words
Coating according to claim 10, wherein at least one of the epoxy resins is a two-component resin.
Claim 14
Dependent Claim
25 words
Coating according to claim 10, wherein at least one of the epoxy resins is a one-component resin capable of hardening under ambient air humidity condition.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-07-20 | 1985-01-19 | 1985-07-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-07-20 | 1989-01-19 | 1989-07-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-07-20 | 1993-01-19 | 1993-07-21 | $7700.00 | Window Closed / Lapsed |