Assignee: General Electric Co
•
Filing: 1979-07-26
•
Granted: 1981-08-25
•
Expires: 1999-07-26
Abstract
Abstract A method for producing varistors and varistor powder is disclosed in which the zinc oxide powder is predoped with certain desired impurities in order to keep these impurities out of the intergranular phase which is known to exist in sintered metal oxide varistors. In particular, certain trivalent dopants are added to increase the zinc oxide grain conductivity without the usually concomitant increase in higher leakage current. In particular, the method disclosed herein is especially important for the doping of varistor material with aluminum at low levels of concentration.
Inventors
- 👤 Joe Wong
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 16:32
CPC Classifications
H; H01; H01B; H01B1/00; H01B1/06; H01B1/08; C; C04; C04B; C04B35/00; C04B35/01; C04B35/453; C04B35/622; C04B35/626; C04B35/628; C04B35/62802; C04B35/62805; C04B35/62813; C04B35/62815; H01C; H01C7/00; H01C7/10; H01C7/105; H01C7/108; H01C7/112; C04B2235/00; C04B2235/02; C04B2235/30; C04B2235/32; C04B2235/3217; C04B2235/3224; C04B2235/3262; C04B2235/327; C04B2235/3275; C04B2235/3284; C04B2235/3286; C04B2235/3293; C04B2235/3294; C04B2235/3298; C04B2235/34; C04B2235/3418; C04B2235/44; C04B2235/443; C04B2235/65; C04B2235/656; C04B2235/6567; C04B2235/70; C04B2235/72; C04B2235/80; C04B2235/85; C04B35/62605; C04B35/62645; C04B35/62655
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
115 words
A method of producing doped zinc oxide varistor powder useful in forming sintered varistors comprising the steps of: (A) dissolving a conductivity increasing dopant in a solvent; (B) forming a slurry by thoroughly mixing zinc oxide powder with the solvent containing the dopant to the extent necessary to achieve the selected concentration of dopant; (C) removing the solvent from the slurry, whereby the zinc oxide powder particles are coated with the dopant; and (D) heating the coated zinc oxide powder particles for a time and at a temperature sufficient to cause thermal diffusion of the dopant into the zinc oxide powder particles, but not at a temperature high enough to initiate zinc oxide grain growth.
Claim 2
Independent Claim
115 words
A method of producing doped zinc oxide varistor powder useful in forming sintered varistors comprising the steps of: (A) dissolving a conductivity increasing dopant in a solvent; (B) forming a slurry by thoroughly mixing zinc oxide powder with the solvent containing the dopant to the extent necessary to achieve the selected concentration of dopant; (C) removing the solvent from the slurry, whereby the zinc oxide powder particles are coated with the dopant; and (D) heating the coated zinc oxide powder particles for a time and at a temperature sufficient to cause thermal diffusion of the dopant into the zinc oxide powder particles, but not at a temperature high enough to initiate zinc oxide grain growth.
Claim 3
Dependent Claim
16 words
The method of claim 1 in which the solvent is removed through evaporation by vacuum suctioning.
Claim 4
Dependent Claim
14 words
The method of claim 1 in which the solvent is removed by thermal evaporation.
Claim 5
Dependent Claim
14 words
The method of claim 1 in which the solvent is removed by spray drying.
Claim 6
Dependent Claim
27 words
The method of claim 1 in which the dopant is a trivalent material selected from the group consisting of aluminum, gallium, indium, and the trivalent rare earths.
Claim 7
Dependent Claim
23 words
The method of claim 1 in which the dopant is aluminum in the form of hydrated aluminum nitrate and the solvent is water.
Claim 8
Dependent Claim
35 words
The method of claim 6 in which the amounts of aluminum nitrate and zinc oxide are chosen to produce a concentration of aluminum of between approximately 5 and approximately 15 parts per million by atom.
Claim 9
Dependent Claim
35 words
The method of claim 1 in which the slurry in step D is heated to a temperature of between approximately 500° C. and approximately 700° C. for between approximately one-half hour to approximately eight hours.
Claim 10
Dependent Claim
28 words
The method of claim 1 further comprising the step of: (E) mixing the dopant diffused zinc oxide powder particles with selected amounts of selected metal oxide varistor additives.
Claim 11
Dependent Claim
32 words
The method of claim 1 in which the metal oxide varistor additives are selected from the group consisting of silicon dioxide, bismuth oxide, cobalt oxide, manganese oxide, tin oxide, and antimony oxide.
Claim 12
Dependent Claim
12 words
The predoped zinc oxide varistor powder made in accordance with claim 8.
Claim 13
Dependent Claim
12 words
The predoped zinc oxide varistor powder made in accordance with claim 1.
Claim 14
Independent Claim
154 words
A method of producing doped metal oxide varistors comprising the steps of: (A) dissolving a conductivity-increasing dopant in a solvent; (B) forming a slurry by thoroughly mixing zinc oxide powder with the solvent containing the dopant to the extent necessary to achieve the selected concentration of dopant; (C) removing the solvent from the slurry, whereby the zinc oxide powder particles are coated with the dopant; (D) heating the coated zinc oxide powder particles for a time and at a temperature sufficient to cause thermal diffusion of the dopant into the zinc oxide powder particles, but not at a temperature high enough to initiate zinc oxide grain growth; (E) mixing the dopant diffused zinc oxide powder particles with selected amounts of selected metal oxide varistor additives; and (F) sintering the varistor powder from step E at a temperature of between approximately 900° C. and approximately 1000° C. for between approximately one and approximately twelve hours.
Claim 15
Independent Claim
154 words
A method of producing doped metal oxide varistors comprising the steps of: (A) dissolving a conductivity-increasing dopant in a solvent; (B) forming a slurry by thoroughly mixing zinc oxide powder with the solvent containing the dopant to the extent necessary to achieve the selected concentration of dopant; (C) removing the solvent from the slurry, whereby the zinc oxide powder particles are coated with the dopant; (D) heating the coated zinc oxide powder particles for a time and at a temperature sufficient to cause thermal diffusion of the dopant into the zinc oxide powder particles, but not at a temperature high enough to initiate zinc oxide grain growth; (E) mixing the dopant diffused zinc oxide powder particles with selected amounts of selected metal oxide varistor additives; and (F) sintering the varistor powder from step E at a temperature of between approximately 900° C. and approximately 1000° C. for between approximately one and approximately twelve hours.
Claim 16
Dependent Claim
11 words
The varistor produced in accordance with the method of claim 13.
Claim 17
Dependent Claim
36 words
A sintered zinc oxide varistor comprising: a granular phase composed substantially of zinc oxide grains; an intergranular phase; and a conductivity-increasing dopant contained substantially within said granular phase and being substantially absent from said intergranular phase.
Claim 18
Dependent Claim
36 words
A sintered zinc oxide varistor comprising: a granular phase composed substantially of zinc oxide grains; an intergranular phase; and a conductivity-increasing dopant contained substantially within said granular phase and being substantially absent from said intergranular phase.
Claim 19
Dependent Claim
20 words
The varistor of claim 15 in which the dopant is selected from the group consisting of aluminum, indium, and gallium.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-08-24 | 1985-02-23 | 1985-08-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-08-24 | 1989-02-23 | 1989-08-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-08-24 | 1993-02-23 | 1993-08-25 | $7700.00 | Window Closed / Lapsed |