US4304849A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Methods of depositing metallic copper on substrates
Assignee: AT&T Inc
•
Filing: 1980-05-16
•
Granted: 1981-12-08
•
Expires: 2000-05-16
Abstract
Abstract In an improved method for depositing a metal on a substrate of the type in which a dielectric coated substrate is coated with a sensitizing solution containing a reductible metal salt, a primary reducing agent comprising 2,7 anthraquinone disulfonic acid and a secondary reducing agent, the substrate is exposed to ultraviolet light in an atmosphere having a temperature of at least 117 DEG F. (42 DEG C.) and a mass of water vapor of at least 3.8 mg of water per liter of dry air for at least 15 seconds. In an embodiment of the method the substrate is aerated in a moisture controlled atmosphere at room temperature for at least 30 minutes prior to exposing the substrate to ultraviolet light.
Inventors
- 👤 William M. Beckenbaugh
- 👤 Theodore D. Polakowski, Jr.
- 👤 Donald Dinella
- 👤 Patricia J. Goldman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 16:20
CPC Classifications
H; H05; H05K; H05K3/00; H05K3/10; H05K3/18; H05K3/181; H05K3/182; H05K3/185; C; C23; C23C; C23C18/00; C23C18/16; C23C18/1601; C23C18/1603; C23C18/1607; C23C18/1608; C23C18/1612; C23C18/18; C23C18/1803; C23C18/1824; C23C18/1837; C23C18/1844
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
141 words
An improved method for depositing a metal on a substrate of the type in which a dielectric coated substrate is coated with a sensitizing solution containing a reductible metal salt, a primary reducing agent comprising 2, 7 anthraquinone disulfonic acid or an alkali metal salt thereof, and a secondary reducing agent, and in which the coated substrate is dried and thereafter exposed to ultraviolet radiation to form catalytic metal sites at regions where metal is to be deposited, wherein the improvement comprises: during the exposing step exposing the substrate to ultraviolet light having an intensity of at least 360 mw/cm 2 for not less than 15 seconds in an atmosphere having a temperature between 117° F. (47° C.) and 260° F. (127° C.) and a mass of water vapor of at least 3.8 mg of water per liter of dry air.
Claim 2
Dependent Claim
141 words
An improved method for depositing a metal on a substrate of the type in which a dielectric coated substrate is coated with a sensitizing solution containing a reductible metal salt, a primary reducing agent comprising 2, 7 anthraquinone disulfonic acid or an alkali metal salt thereof, and a secondary reducing agent, and in which the coated substrate is dried and thereafter exposed to ultraviolet radiation to form catalytic metal sites at regions where metal is to be deposited, wherein the improvement comprises: during the exposing step exposing the substrate to ultraviolet light having an intensity of at least 360 mw/cm 2 for not less than 15 seconds in an atmosphere having a temperature between 117° F. (47° C.) and 260° F. (127° C.) and a mass of water vapor of at least 3.8 mg of water per liter of dry air.
Claim 3
Dependent Claim
30 words
The improved method as recited in claim 1, wherein the secondary reducing agent is selected from a group of polyols consisting of sorbitol and a mixture of sorbitol and lactose.
Claim 4
Dependent Claim
50 words
The improved method as recited in any of the preceding claims wherein, prior to the exposing step, the substrate is aerated in an atmosphere having a temperature of at least 60° F. and containing at least 2.6 milligrams of water per liter of dry air for at least 30 minutes.
Claim 5
Dependent Claim
144 words
An improved method for depositing a metal on a substrate, of the type in which a dielectric coated substrate is coated with a sensitizing solution containing a reducible metal salt of a non-noble metal, a primary reducing agent selected from the group consisting of 2,7 anthraquinone disulfonic acid, alkali metal salts of 2,7 anthraquinone disulfonic acid, and mixtures thereof, and a second reducing agent, and in which the coated substrate is dried and thereafter exposed to ultraviolet radiation to form catalytic metal sites at regions where metal is to be deposited, wherein the improvement comprises: performing the exposing step for at least 25 seconds in an atmosphere having at least 5.0 mg of water per liter of dry air and a temperature of at least 145° F. (63° C.), and wherein the intensity of the ultraviolet radiation is at least 450 mw/cm 2 .
Claim 6
Dependent Claim
144 words
An improved method for depositing a metal on a substrate, of the type in which a dielectric coated substrate is coated with a sensitizing solution containing a reducible metal salt of a non-noble metal, a primary reducing agent selected from the group consisting of 2,7 anthraquinone disulfonic acid, alkali metal salts of 2,7 anthraquinone disulfonic acid, and mixtures thereof, and a second reducing agent, and in which the coated substrate is dried and thereafter exposed to ultraviolet radiation to form catalytic metal sites at regions where metal is to be deposited, wherein the improvement comprises: performing the exposing step for at least 25 seconds in an atmosphere having at least 5.0 mg of water per liter of dry air and a temperature of at least 145° F. (63° C.), and wherein the intensity of the ultraviolet radiation is at least 450 mw/cm 2 .
Claim 7
Dependent Claim
47 words
The improved method as recited in claim 4, wherein prior to the exposing step, the coated substrate is aerated in an atmosphere having a mass of water vapor of not less than 5.3 mg per liter of dry air at room temperature for at least 30 minutes.
References Cited (Backward Citations)
US3492135A
Cited
USRE29015E
Cited
US3697319A
Cited
US3925578A
Cited
US3758332A
Cited
US3949121A
Cited
US4098922A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-12-07 | 1985-06-08 | 1985-12-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-12-07 | 1989-06-08 | 1989-12-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-12-07 | 1993-06-08 | 1993-12-08 | $7700.00 | Window Closed / Lapsed |