US4311535A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Composition for forming zinc phosphate coating over metal surface
Assignee: Henkel Corp
•
Filing: 1980-05-01
•
Granted: 1982-01-19
•
Expires: 2000-05-01
Abstract
Abstract An acidic aqueous zinc-containing coating solution containing about 0.08 to about 0.2 weight percent of zinc, about 0.8 to about 3 weight percent of phosphate, about 0.05 to about 0.35 weight percent of chlorate, about 0.001 to about 0.1 weight percent of nitrite, and a complex fluoride ion having the following concentration: 0.4≧y≧0.63x-0.042 wherein x is the concentration of the zinc in weight percent and y is the concentration of the complex fluoride ion in weight percent. The coating solution is useful for forming on metal surfaces zinc phosphate coatings that exhibit excellent alkali resistance, good adhesion to a paint film, and good corrosion resistance after painting when used as an undercoat for the cationic electrodeposition of a paint film.
Inventors
- 👤 Kiyotada Yasuhara
- 👤 Masashi Takahashi
- 👤 Ryoichi Murakami
- 👤 Takashi Senzaki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 12:40
CPC Classifications
C; C23; C23C; C23C22/00; C23C22/05; C23C22/06; C23C22/34; C23C22/36; C23C22/362; C25; C25D; C25D13/00; C25D13/20
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
91 words
An acidic, aqueous coating solution for forming a zinc phosphate coating on a metal surface comprising about 0.08 to about 0.2 weight percent of zinc ion, about 0.8 to about 3 weight percent of phosphate ion, about 0.05 to about 0.35 weight percent of chlorate ion, about 0.001 to about 0.1 weight percent of nitrite ion, and a complex fluoride ion having the following concentration: 0.4≧y≧0.63x-0.042 wherein x is the concentration of the zinc ion in weight percent and y is the concentration of the complex fluoride ion in weight percent.
Claim 2
Dependent Claim
91 words
An acidic, aqueous coating solution for forming a zinc phosphate coating on a metal surface comprising about 0.08 to about 0.2 weight percent of zinc ion, about 0.8 to about 3 weight percent of phosphate ion, about 0.05 to about 0.35 weight percent of chlorate ion, about 0.001 to about 0.1 weight percent of nitrite ion, and a complex fluoride ion having the following concentration: 0.4≧y≧0.63x-0.042 wherein x is the concentration of the zinc ion in weight percent and y is the concentration of the complex fluoride ion in weight percent.
Claim 3
Dependent Claim
32 words
The coating solution of claim 1 wherein the concentration of phosphate is from about 0.8 to about 2 weight percent, and the concentration of complex fluoride ion is about 0.2 weight percent.
Claim 4
Dependent Claim
40 words
The coating solution of claim 1 wherein the zinc ion is supplied in the form of a soluble zinc containing compound selected from the group consisting of zinc phosphate, zinc nitrate, zinc carbonate, zinc hydroxide, zinc oxide and zinc metal.
Claim 5
Dependent Claim
36 words
The coating solution of claim 1 wherein the phosphate ion is supplied in the form of a compound selected from the group consisting of phosphoric acid, alakli metal phosphates, nickel phosphate, zinc phosphate and mixtures thereof.
Claim 6
Dependent Claim
32 words
The coating solution of claim 1 wherein the chlorate ion is supplied in the form of a compound selected from the group consisting of chloric acid, alkali metal chlorates, and mixtures thereof.
Claim 7
Dependent Claim
32 words
The coating solution of claim 1 wherein the nitrite ion is supplied in the form of a compound selected from the group consisting of nitrous acid, alkali metal nitrites, and mixtures thereof.
Claim 8
Dependent Claim
23 words
The coating solution of claim 1 wherein the complex fluoride ion is selected from the group consisting of fluoborate, fluosilicate, and mixtures thereof.
Claim 9
Dependent Claim
31 words
The coating solution of claim 7 wherein the fluoborate is supplied in the form of a compound selected from the group consisting of fluoboric acid, alkali metal fluoborates, and mixtures thereof.
Claim 10
Dependent Claim
31 words
The coating solution of claim 7 wherein the fluosilicate is supplied in the form of a compound selected from the group consisting of fluosilicic acid, alkali metal fluosilicates, and mixtures thereof.
Claim 11
Dependent Claim
16 words
The coating solution of claim 1 including at least about 0.005 weight percent of nickel ion.
Claim 12
Dependent Claim
21 words
The coating solution of claim 10 wherein the concentration of the nickel ion is about 0.005 to about 0.1 weight percent.
Claim 13
Dependent Claim
34 words
The coating solution of claim 10 wherein the nickel ion is supplied in the form of a soluble salt selected from the group consisting of nickel phosphate, nickel nitrate, nickel carbonate and nickel oxide.
Claim 14
Dependent Claim
17 words
The coating solution of claim 1 including about 0.3 to about 0.8 weight percent of nitrate ion.
Claim 15
Dependent Claim
32 words
The coating solution of claim 13 wherein the nitrate ion is supplied in the form of a compound selected from the group consisting of nitric acid, alkali metal nitrates, and mixtures thereof.
Claim 16
Dependent Claim
122 words
An acidic aqueous coating composition for forming a zinc phosphate coating on a metal surface comprising about 0.08 to about 0.2 weight percent of zinc ion, about 0.8 to about 2 weight percent of phosphate ion, about 0.05 to about 0.35 weight percent of chlorate ion, about 0.001 to about 0.1 weight percent of nitrite ion, about 0.005 to about 0.1 weight percent of nickel ion, about 0.3 to about 0.8 weight percent of nitrate ion, and a complex fluoride ion selected from the group consisting of fluoborate, fluosilicate, and mixtures thereof, having the following concentration: 0.4≧y≧0.63x-0.042 where x is the concentration of the zinc ion in weight percent and y is the concentration of the complex fluoride ion in weight percent.
Claim 17
Dependent Claim
122 words
An acidic aqueous coating composition for forming a zinc phosphate coating on a metal surface comprising about 0.08 to about 0.2 weight percent of zinc ion, about 0.8 to about 2 weight percent of phosphate ion, about 0.05 to about 0.35 weight percent of chlorate ion, about 0.001 to about 0.1 weight percent of nitrite ion, about 0.005 to about 0.1 weight percent of nickel ion, about 0.3 to about 0.8 weight percent of nitrate ion, and a complex fluoride ion selected from the group consisting of fluoborate, fluosilicate, and mixtures thereof, having the following concentration: 0.4≧y≧0.63x-0.042 where x is the concentration of the zinc ion in weight percent and y is the concentration of the complex fluoride ion in weight percent.
Claim 18
Dependent Claim
99 words
A process for forming a zinc phosphate coating on a metal surface comprising contacting the metal surface with an acidic aqueous coating composition comprising about 0.08 to about 0.2 weight percent of zinc ion, about 0.8 to about 3 weight percent of phosphate ion, about 0.05 to about 0.35 weight percent of chlorate ion, about 0.001 to about 0.1 weight percent of nitrite ion, and a complex fluoride ion having the following concentration: 0.4≧y≧0.63x-0.042 wherein x is the concentration of the zinc ion in weight percent and y is the concentration of the complex fluoride ion in weight percent.
Claim 19
Dependent Claim
99 words
A process for forming a zinc phosphate coating on a metal surface comprising contacting the metal surface with an acidic aqueous coating composition comprising about 0.08 to about 0.2 weight percent of zinc ion, about 0.8 to about 3 weight percent of phosphate ion, about 0.05 to about 0.35 weight percent of chlorate ion, about 0.001 to about 0.1 weight percent of nitrite ion, and a complex fluoride ion having the following concentration: 0.4≧y≧0.63x-0.042 wherein x is the concentration of the zinc ion in weight percent and y is the concentration of the complex fluoride ion in weight percent.
Claim 20
Dependent Claim
14 words
The process of claim 16 wherein the coating composition is sprayed on the surface.
Claim 21
Dependent Claim
17 words
The process of claim 17 wherein the metal surface is sprayed for longer than about 30 seconds.
Claim 22
Dependent Claim
15 words
The process of claim 18 wherein the metal surface is sprayed for about 2 minutes.
Claim 23
Dependent Claim
19 words
The process of claim 16 wherein the temperature of the coating composition is about 35° to about 65° C.
Claim 24
Dependent Claim
22 words
The process of claim 17, 18, 19 or 20 including applying to said zinc phosphate coating a paint film by cationic electrodeposition.
Claim 25
Dependent Claim
16 words
A metal surface having thereon a zinc phosphate coating formed by the process of claim 16.
Claim 26
Dependent Claim
120 words
A process for coating a metal surface comprising: (A) forming on the metal surface a zinc phosphate coating by contacting the metal surface with an acidic, aqueous coating solution consisting essentially of about 0.08 to about 0.2 weight percent of zinc ion, about 0.8 to about 3 weight percent of phosphate ion, about 0.05 to about 0.35 weight percent of chlorate ion, about 0.001 to about 0.1 weight percent of nitrite ion, and a complex fluoride ion having the following concentration: 0.4≧y≧0.63x-0.042 wherein x is the concentration of the zinc ion in weight percent and y is the concentration of the complex fluoride ion in weight percent; and (B) forming on the coated surface a paint film by cationic electrodeposition.
Claim 27
Dependent Claim
120 words
A process for coating a metal surface comprising: (A) forming on the metal surface a zinc phosphate coating by contacting the metal surface with an acidic, aqueous coating solution consisting essentially of about 0.08 to about 0.2 weight percent of zinc ion, about 0.8 to about 3 weight percent of phosphate ion, about 0.05 to about 0.35 weight percent of chlorate ion, about 0.001 to about 0.1 weight percent of nitrite ion, and a complex fluoride ion having the following concentration: 0.4≧y≧0.63x-0.042 wherein x is the concentration of the zinc ion in weight percent and y is the concentration of the complex fluoride ion in weight percent; and (B) forming on the coated surface a paint film by cationic electrodeposition.
Claim 28
Dependent Claim
30 words
A process according to claim 23 wherein the coating solution is as defined in claim 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14 or 15.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-01-18 | 1985-07-20 | 1986-01-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-01-18 | 1989-07-20 | 1990-01-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-01-18 | 1993-07-20 | 1994-01-19 | $7700.00 | Window Closed / Lapsed |