US4311822A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Interfacial production of poly(ester carbonate) or polyester including acid chloride synthesis
Assignee: Honeywell International Inc
•
Filing: 1980-05-02
•
Granted: 1982-01-19
•
Expires: 2000-05-02
Abstract
Abstract A process for producing poly(ester carbonates) and polyesters by reacting an aromatic or cycloaliphatic dicarboxylate salt such as sodium terephthalate with phosgene in an organic solvent in the presence of a catalytic amount of a tertiary nitrogen compound such as pyridine, optionally separating the suspended by-product inorganic salt and then interfacially reacting with a bisphenol such as bisphenol A. Excess phosgene in the diacid chloride synthesis can be carried over to the polymerization if a poly(ester carbonate) is to be produced or removed if a polyester is to be produced. Certain low levels of a tertiary nitrogen compound with a pyridine nucleus in the organic solution do not interfere with the interfacial polymerization.
Inventors
- 👤 Gerald J. Dege
- 👤 Leon Segal
- 👤 Bruce T. DeBona
- 👤 Robert S. Cooke
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 20:48
CPC Classifications
C; C08; C08G; C08G63/00; C08G63/64; C07; C07C; C07C51/00; C07C51/58; C07C51/60
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
118 words
A process for the production of a poly(ester carbonate) which comprises: (a) reacting an alkali metal or alkaline earth metal salt of an aromatic or cycloaliphatic dicarboxylic acid in an inert organic solvent with phosgene in the presence of at least one tertiary nitrogen compound to form a corresponding aromatic or cycloaliphatic dicarboxylic acid chloride dissolved in the organic solvent, carbon dioxide and an alkali metal or alkaline earth metal chloride salt suspended in the organic solution; and (b) mixing the organic solution with an aqueous solution of an alkali metal or alkaline earth metal salt of a bisphenol under sufficient agitation and with sufficient phosgene and tertiary nitrogen polymerization catalyst present to form a poly(ester carbonate) polymer.
Claim 2
Dependent Claim
118 words
A process for the production of a poly(ester carbonate) which comprises: (a) reacting an alkali metal or alkaline earth metal salt of an aromatic or cycloaliphatic dicarboxylic acid in an inert organic solvent with phosgene in the presence of at least one tertiary nitrogen compound to form a corresponding aromatic or cycloaliphatic dicarboxylic acid chloride dissolved in the organic solvent, carbon dioxide and an alkali metal or alkaline earth metal chloride salt suspended in the organic solution; and (b) mixing the organic solution with an aqueous solution of an alkali metal or alkaline earth metal salt of a bisphenol under sufficient agitation and with sufficient phosgene and tertiary nitrogen polymerization catalyst present to form a poly(ester carbonate) polymer.
Claim 3
Dependent Claim
30 words
The process of claim 1 further comprising separating the suspended alkali metal or alkaline earth metal chloride from the organic solution before mixing the organic solution with the aqueous solution.
Claim 4
Dependent Claim
34 words
The process of claim 1 or 2 wherein said alkali metal or alkaline earth metal salt of an aromatic or cycloaliphatic dicarboxylic acid is a sodium or potassium salt of isophthalic or terephthalic acid.
Claim 5
Dependent Claim
30 words
The process of claim 1 or 2 wherein said alkali metal or alkaline earth metal salt of an aromatic or cycloaliphatic dicarboxylic acid is the sodium salt of terephthalic acid.
Claim 6
Dependent Claim
19 words
The process of claim 1 or 2 wherein said at least one tertiary nitrogen compound contains a pyridine nucleus.
Claim 7
Dependent Claim
31 words
The process of claim 1 or 2 wherein said at least one tertiary nitrogen compound is pyridine, present in the amount between about 0.1 and about 10%, by moles of carboxylate.
Claim 8
Dependent Claim
22 words
The process of claim 6 wherein pyridine is present in an amount between about 0.2 and about 5%, by moles of carboxylate.
Claim 9
Dependent Claim
33 words
The process of claim 1 or 2 wherein phosgene is present in said reacting step (a) in an amount at least 10% in excess of the stoichiometric amount of phosgene compared to carboxylate.
Claim 10
Dependent Claim
29 words
The process of claim 1 or 2 wherein said alkali metal or alkaline earth metal salt of a bisphenol is a sodium or potassium salt of a bisphenol A.
Claim 11
Dependent Claim
24 words
The process of claim 1 or 2 wherein the phosgene present during said mixing step (c) is all introduced in said reacting step (a).
Claim 12
Dependent Claim
136 words
A process for interfacially producing a poly(ester carbonate) which comprises: (a) mixing an organic solution of an inert organic solvent containing an aromatic or cycloaliphatic dicarboxylic acid halide and a tertiary nitrogen compound containing a pyridine nucleus in an amount between about 0.1 and about 10%, by moles of carbonyl halide, with an aqueous solution of an alkali metal salt of an bisphenol in the presence of a catalytic amount of a tertiary amine polymerization catalyst, with phosgene also being present, to form a poly(ester carbonate) with carbonate moieties and moieties derived from the aromatic or cycloaliphatic dicarboxylic acid halide and from the bisphenol, (b) separating aqueous and organic phases after the poly(ester carbonate) is formed, (c) washing the organic phase substantially free of halide, and (d) recovering the poly(ester carbonate) from the washed organic phase.
Claim 13
Dependent Claim
136 words
A process for interfacially producing a poly(ester carbonate) which comprises: (a) mixing an organic solution of an inert organic solvent containing an aromatic or cycloaliphatic dicarboxylic acid halide and a tertiary nitrogen compound containing a pyridine nucleus in an amount between about 0.1 and about 10%, by moles of carbonyl halide, with an aqueous solution of an alkali metal salt of an bisphenol in the presence of a catalytic amount of a tertiary amine polymerization catalyst, with phosgene also being present, to form a poly(ester carbonate) with carbonate moieties and moieties derived from the aromatic or cycloaliphatic dicarboxylic acid halide and from the bisphenol, (b) separating aqueous and organic phases after the poly(ester carbonate) is formed, (c) washing the organic phase substantially free of halide, and (d) recovering the poly(ester carbonate) from the washed organic phase.
Claim 14
Dependent Claim
18 words
The process of claim 11 wherein the phosgene is substantially all present in the organic solution before mixing.
Claim 15
Dependent Claim
19 words
The process of claim 11 wherein the aromatic or cycloaliphatic dicarboxylic acid halide is terephthalic or isophthalic acid chloride.
Claim 16
Dependent Claim
11 words
The process of claim 11 wherein the bisphenol is bisphenol A.
Claim 17
Dependent Claim
27 words
The process of claim 11 wherein the tertiary nitrogen compound is pyridine present in an amount between about 0.2 and about 5% by moles of carbonyl halide.
Claim 18
Dependent Claim
123 words
A process for the production of a polyester which comprises: (a) reacting an alkali metal or alkaline earth metal salt of an aromatic or cycloaliphatic dicarboxylic acid in an inert organic solvent with phosgene in the presence of at least one tertiary nitrogen compound to form a corresponding aromatic or cycloaliphatic dicarboxylic acid chloride dissolved in the organic solvent, carbon dioxide and an alkali metal or alkaline earth metal chloride salt suspended in the organic solution; (b) removing any unreacted phosgene from the organic solution; and (c) mixing the organic solution with an aqueous solution of an alkali metal or alkaline earth metal salt of a bisphenol under sufficient agitation and with sufficient tertiary nitrogen polymerization catalyst present to form a polyester polymer.
Claim 19
Dependent Claim
123 words
A process for the production of a polyester which comprises: (a) reacting an alkali metal or alkaline earth metal salt of an aromatic or cycloaliphatic dicarboxylic acid in an inert organic solvent with phosgene in the presence of at least one tertiary nitrogen compound to form a corresponding aromatic or cycloaliphatic dicarboxylic acid chloride dissolved in the organic solvent, carbon dioxide and an alkali metal or alkaline earth metal chloride salt suspended in the organic solution; (b) removing any unreacted phosgene from the organic solution; and (c) mixing the organic solution with an aqueous solution of an alkali metal or alkaline earth metal salt of a bisphenol under sufficient agitation and with sufficient tertiary nitrogen polymerization catalyst present to form a polyester polymer.
Claim 20
Dependent Claim
30 words
The process of claim 16 further comprising separating the suspended alkali metal or alkaline earth metal chloride from the organic solution before mixing the organic solution with the aqueous solution.
Claim 21
Dependent Claim
36 words
The process of claim 16 or 17 wherein said alkali metal alkaline earth metal salt of an aromatic or cycloaliphatic dicarboxylic acid is a sodium or potassium salt of isophthalic or terephthalic acid, or mixtures thereof.
Claim 22
Dependent Claim
19 words
The process of claim 16 or 17 wherein said at least one tertiary nitrogen compound contains a pyridine nucleus.
Claim 23
Dependent Claim
17 words
The process of claim 16 or 17 wherein said at least one tertiary nitrogen compound includes pyridine.
References Cited (Backward Citations)
US3637841A
Cited
US3776886A
Cited
US3629328A
Cited
US3869485A
Cited
US3875226A
Cited
UST886004I4
Cited
US3878244A
Cited
US3888921A
Cited
US4156069A
Cited
US4129594A
Cited
US4173708A
Cited
US4194038A
Cited
US4255556A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-01-18 | 1985-07-20 | 1986-01-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-01-18 | 1989-07-20 | 1990-01-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-01-18 | 1993-07-20 | 1994-01-19 | $7700.00 | Window Closed / Lapsed |