Bodies composed of at least two parts, sealing glass and method for bonding parts
Assignee: US Philips Corp
•
Filing: 1980-11-24
•
Granted: 1982-05-18
•
Expires: 2000-11-24
Abstract
Abstract In practice no sealing glasses are known with which glass or ceramic material having a coefficient of thermal expansion α 30 °-300° C. in the range between 31 to 36×10 -7 per °C. can be sealed together. The invention provides bodies which are composed of at least two parts, these parts having been made from a material having a coefficient of expansion as mentioned above, the parts having been sealed together by means of a sealing glass containing 8-10 weight % vanadium pentoxide, 1.5-3.0 weight % copper (II) oxide, 1-3 weight % lead (II) oxide, 0-1 weight % silicon oxide, 0-5 weight % aluminium oxide, 26-28 weight % boron oxide and 58-61 weight % zinc oxide. The weight ratio of boron oxide to zinc oxide is in the range from 0.45 to 0.47. The body is composed of parts (1 and 3), which have been sealed together by means of the sealing glass (2).
Inventors
- 👤 Paul J. Van Assche
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 11:41
CPC Classifications
C; C03; C03C; C03C8/00; C03C8/24; C03C27/00; C03C27/06; C04; C04B; C04B37/00; C04B37/003; C04B37/005; C04B2237/00; C04B2237/02; C04B2237/10; C04B2237/30; C04B2237/32; C04B2237/50; C04B2237/76
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
120 words
Bodies composed of at least two parts produced of a glass or a ceramic material having a coefficient of thermal expansion α 30 °-300° C. in the range 31 to 36×10 -7 per °C., these parts having been sealed together by means of a sealing glass having a coefficient of expansion of less than 40×10 -7 per °C. characterized in that the sealing glass consists essentially of 8-10 weight % vanadium pentoxide, 1.5-3.0 weight % copper (II) oxide, 1-3 weight % lead (II) oxide, 0-1 weight % silicon (IV) oxide, 0-5 weight % aluminium oxide, 26-28 weight % boron (III) oxide and 58-61 weight % zinc oxide, the weight ratio boron oxide to zinc oxide being from 0.45 to 0.47.
Claim 2
Dependent Claim
120 words
Bodies composed of at least two parts produced of a glass or a ceramic material having a coefficient of thermal expansion α 30 °-300° C. in the range 31 to 36×10 -7 per °C., these parts having been sealed together by means of a sealing glass having a coefficient of expansion of less than 40×10 -7 per °C. characterized in that the sealing glass consists essentially of 8-10 weight % vanadium pentoxide, 1.5-3.0 weight % copper (II) oxide, 1-3 weight % lead (II) oxide, 0-1 weight % silicon (IV) oxide, 0-5 weight % aluminium oxide, 26-28 weight % boron (III) oxide and 58-61 weight % zinc oxide, the weight ratio boron oxide to zinc oxide being from 0.45 to 0.47.
Claim 3
Dependent Claim
44 words
A body is claimed in claim 1, characterized in that the sealing glass contains 9.0 weight % vanadium-pentoxide, 27.2 weight % boron oxide, 59.3 weight % zinc oxide, 2.3 weight % copper oxide, 1.8 weight % lead oxide and 0.4 weight % silicon oxide.
Claim 4
Dependent Claim
75 words
A sealing glass having a coefficient of expansion of less than 40×10 -7 per °C. characterized in that the sealing glass consists essentially of 8-10 weight % vanadium pentoxide, 1.5-3.0 weight % copper (II) oxide, 1-3 weight % lead (II) oxide, 0-1 weight % silicon oxide, 0-5 weight % aluminium oxide, 26-28 weight % boron oxide, and 58-61 weight % zinc oxide, the weight ratio boron oxide to zinc oxide being from 0.45 to 0.47.
Claim 5
Dependent Claim
75 words
A sealing glass having a coefficient of expansion of less than 40×10 -7 per °C. characterized in that the sealing glass consists essentially of 8-10 weight % vanadium pentoxide, 1.5-3.0 weight % copper (II) oxide, 1-3 weight % lead (II) oxide, 0-1 weight % silicon oxide, 0-5 weight % aluminium oxide, 26-28 weight % boron oxide, and 58-61 weight % zinc oxide, the weight ratio boron oxide to zinc oxide being from 0.45 to 0.47.
Claim 6
Dependent Claim
46 words
A sealing glass as claimed in claim 3, characterized in that the sealing glass contains 9.0 weight % vanadium pentoxide, 27.2 weight % boron oxide, 59.3 weight % zinc oxide, 2.3 weight % copper oxide, 1.8 weight % lead oxide and 0.4 weight % silicon oxide.
References Cited (Backward Citations)
US3446695A
Cited
US3970464A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-05-17 | 1985-11-16 | 1986-05-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-05-17 | 1989-11-16 | 1990-05-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-05-17 | 1993-11-16 | 1994-05-18 | $7700.00 | Window Closed / Lapsed |