Process for preparing polybutadiene having a 1,2-configuration content of 5-40% and a cis-1,4-configuration content of 60% or more
Assignee: JSR Corp
•
Filing: 1981-01-26
•
Granted: 1982-07-20
•
Expires: 2001-01-26
Abstract
Abstract A process for preparing polybutadiene having a 1,2-configuration content of 5-40% and a cis-1,4-configuration content of 60% or more, which comprises polymerizing 1,3-butadiene in the presence of a catalyst consisting of: (A) a cobalt compound, (B) at least one member selected from the group consisting of: (i) a trialkylaluminum, (ii) a reaction product of a trialkylaluminum and an alcohol or water, (iii) a mixture of a trialkylaluminum and a dialkylaluminum halide, (iv) a dialkylaluminum hydride, and (v) an organolithium compound, and (C) at least one compound selected from the group consisting of phenyl isothiocyanate and carbon disulfide, in a hydrocarbon or halogenated hydrocarbon solution of a high cis-1,4-polybutadiene obtained by polymerizing 1,3-butadiene with a catalyst consisting of: (D) at least one compound selected from the group consisting of the organocarboxylates of nickel and organic complex compounds of nickel, (E) at least one compound selected from the group consisting of boron trifluoride, boron trifluoride complex compounds and hydrogen fluoride, and (F) at least one compound selected from the group consisting of the organometallic compounds of the alkali metals of the Group II or III metals of the Periodic Table. The polybutadiene produced by this process has an improved tear strength and improved flexural fatigue properties.
Inventors
- 👤 Yasumasa Takeuchi
- 👤 Yutaka Obata
- 👤 Noboru Ohshima
- 👤 Tooru Shibata
- 👤 Kaoru Nakako
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 07:07
CPC Classifications
C; C08; C08F; C08F136/00; C08F136/02; C08F136/04; C08F136/06
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
236 words
A process for preparing a polybutadiene with a 1,2-configuration content of 5-40%, a Mooney viscosity of 20 to 150 and a melting point 1,2-configuration portion of 180° C. to 220° C., and a cis-1,4-configuration content of at least 60%, which comprises polymerizing 1,3-butadiene in the presence of a 1,2 syndiotactic polymerization catalyst consisting of: (A) a cobalt compound, (B) at least one member selected from the group consisting of: (i) a trialkylaluminum, (ii) a reaction product of a trialkylaluminum and an alcohol or water, (iii) a mixture of a trialkylaluminum and a dialkylaluminum halide, (iv) a dialkylaluminum hydride, and (v) an organolithium compound, and (C) at least one compound selected from the group consisting of phenyl isothiocyanate and carbon disulfide in a hydrocarbon or halogenated hydrocarbon solution of a high cis-1,4-polybutadiene obtained by polymerizing 1,3-butadiene with a catalyst consisting of: (D) at least one compound selected from the group consisting of organocarboxylates of nickel and organic complex compounds of nickel, (E) at least one compound selected from the group consisting of boron trifluoride, boron trifluoride complex compounds and hydrogen fluoride, and (F) at least one compound selected from the group consisting of the organometallic compounds of the alkali metals and the Group II or III metals of the Periodic Table, wherein the amount of the high cis-1,4-polymerization catalyst used is that corresponding to 0.02-2.5 mg atom nickel of the component (D) per 100 g of 1,3-butadiene.
Claim 2
Dependent Claim
236 words
A process for preparing a polybutadiene with a 1,2-configuration content of 5-40%, a Mooney viscosity of 20 to 150 and a melting point 1,2-configuration portion of 180° C. to 220° C., and a cis-1,4-configuration content of at least 60%, which comprises polymerizing 1,3-butadiene in the presence of a 1,2 syndiotactic polymerization catalyst consisting of: (A) a cobalt compound, (B) at least one member selected from the group consisting of: (i) a trialkylaluminum, (ii) a reaction product of a trialkylaluminum and an alcohol or water, (iii) a mixture of a trialkylaluminum and a dialkylaluminum halide, (iv) a dialkylaluminum hydride, and (v) an organolithium compound, and (C) at least one compound selected from the group consisting of phenyl isothiocyanate and carbon disulfide in a hydrocarbon or halogenated hydrocarbon solution of a high cis-1,4-polybutadiene obtained by polymerizing 1,3-butadiene with a catalyst consisting of: (D) at least one compound selected from the group consisting of organocarboxylates of nickel and organic complex compounds of nickel, (E) at least one compound selected from the group consisting of boron trifluoride, boron trifluoride complex compounds and hydrogen fluoride, and (F) at least one compound selected from the group consisting of the organometallic compounds of the alkali metals and the Group II or III metals of the Periodic Table, wherein the amount of the high cis-1,4-polymerization catalyst used is that corresponding to 0.02-2.5 mg atom nickel of the component (D) per 100 g of 1,3-butadiene.
Claim 3
Dependent Claim
28 words
The process according to claim 1, wherein the component (D)/component (F) molar ratio is 0.02/1 to 2/1, and the component (E)/component (F) molar ratio is 0.2/1 to 15/1.
Claim 4
Dependent Claim
40 words
The process according to claim 2, wherein the high cis-1,4-polybutadiene has a cis-1,4 content of 90% or more and a 1,2 content of 3% or less and an intrinsic viscosity of 1.2-10 dl/g as measured in toluene at 30° C.
Claim 5
Dependent Claim
30 words
The process according to claim 3, wherein the hydrocarbon solution of high cis-1,4-polybutadiene is a solution in an aromatic hydrocarbon or a solution in a solvent containing an aromatic hydrocarbon.
Claim 6
Dependent Claim
15 words
The process according to claim 4, wherein the aromatic hydrocarbon is benzene, toluene or xylene.
Claim 7
Dependent Claim
45 words
The process according to claim 5, wherein the component (A) of the 1,2-polymerization catalyst is a cobalt organocarboxylate, a cobalt organosulfonate, a β-diketone complex compound of cobalt, a tertiary amine complex compound of a cobalt halide or a phosphine complex compound of a cobalt halide.
Claim 8
Dependent Claim
38 words
The process according to claim 5, wherein the component (A) of the 1,2-polymerization catalyst is cobalt naphthenate, cobalt octanoate, cobalt stearate, cobalt acetate, cobalt benzoate, cobalt salicylate, cobalt dodecylbenzenesulfonate, bis(ethyl acetoacetate)cobalt, bis(acetylacetonato)cobalt, tris(acetylacetonato)cobalt, dichlorobis(pyridine)cobalt, dichlorobis(triphenylphosphine)cobalt, dibromobis(triphenylphosphine)cobalt or dibromobis(triethylphosphine)cobalt.
Claim 9
Dependent Claim
16 words
The process according to claim 7, wherein the component (B) is trimethylaluminum, triethylaluminum, triisobutylaluminum or trihexylaluminum.
Claim 10
Dependent Claim
77 words
The process according to claim 7, wherein the component (B) is a product obtained by reacting 1 mole of a trialkylaluminum selected from the group consisting of trimethylaluminum, triethylaluminum, isobutylaluminum and trihexylaluminum with 0.2-0.9 hydroxy equivalent of methyl alcohol, ethyl alcohol, propyl alcohol, butyl alcohol, 2-ethylhexyl alcohol, decyl alcohol, lauryl alcohol, cyclohexyl alcohol, benzyl alcohol, furfuryl alcohol or cinnamyl alcohol, or a reaction product of 1 mole of said trialkylaluminum and less than 1.5 mole of water.
Claim 11
Dependent Claim
39 words
The process according to claim 7, wherein the component (B) is a mixture of 10-90 mol% of a trialkylaluminum selected from the group consisting of trimethylaluminum, triethylaluminum, triisobutylaluminum and trihexylaluminum and 10-90 mol% of diethylaluminum chloride or dibutylaluminum chloride.
Claim 12
Dependent Claim
16 words
The process according to claim 7, wherein the component (B) is diethylaluminum hydride or diisobutylaluminum hydride.
Claim 13
Dependent Claim
16 words
The process according to claim 7, wherein the component (B) is ethyllithium, propyllithium, butyllithium or dilithiobutane.
Claim 14
Dependent Claim
33 words
The process according to claim 8, 9, 10, 11 or 12, wherein the component (B)/component (A) molar ratio is 1/1 to 100/1 and the component (C)/component (A) molar ratio is 0.005/1 to 100/1.
Claim 15
Dependent Claim
21 words
The process according to claim 13, wherein the 1,2-polymerization of 1,3-butadiene is effected at a temperature of -20° to +80° C.
Claim 16
Dependent Claim
21 words
The process according to claim 14, wherein the 1,2-polymerization of 1,3-butadiene is effected at a temperature of 0° to 50° C.
Claim 17
Dependent Claim
18 words
The process according to claim 15, wherein the concentration of 1,3-butadiene in the polymerization system is 2-50% weight.
Claim 18
Dependent Claim
22 words
The process according to claim 16, wherein the whole amounts of 1,3-butadiene and solvent are added at the stage of high cis-1,4-polymerization.
Claim 19
Dependent Claim
29 words
The process according to claim 16, wherein a part of the 1,3-butadiene and/or solvent is added for high cis-1,4-polymerization and the remaining 1,3-butadiene and/or solvent is added for 1,2-polymerization.
References Cited (Backward Citations)
No citation records indexed.
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-07-19 | 1986-01-18 | 1986-07-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-07-19 | 1990-01-18 | 1990-07-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-07-19 | 1994-01-18 | 1994-07-20 | $7700.00 | Window Closed / Lapsed |