Method for manufacturing glass fibers from an infrared ray-transmitting glass fiber material
Assignee: NTT Inc
•
Filing: 1981-01-21
•
Granted: 1982-08-10
•
Expires: 2001-01-21
Abstract
Abstract Glass material for infrared ray-transmitting optical fibers comprises a three-component material made of a 28 mol % to 38 mol % BaF2-2 mol % to 7 mol % GdF3-58 mol % to 69 mol % ZrF4-based composition. The glass material is cast in a metal mold with a hollow section which is preheated to a temperature of at least 100 DEG C. but below the glass deformation temperature and annealing the melt in the metal mold to form a glass rod. The glass rod forming step includes heating the melt in the temperature range of between about 200 DEG C. and less than the glass deformation temperature and cooling the melt. The glass rod is removed from the metal mold and optically polished at the ends and sides and is then drawn into a fiber while applying tension to the tip of the glass rod while the glass rod is being heated. The glass rod is drawn into a glass fiber while maintaining the temperature at the end portion of the glass rod constant.
Inventors
- 👤 Seiko Mitachi
- 👤 Shuichi Shibata
- 👤 Terutoshi Kanamori
- 👤 Toyotaka Manabe
- 👤 Mitsuho Yasu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 07:47
CPC Classifications
C; C03; C03B; C03B37/00; C03B37/01; C03B37/012; C03B37/01265; C03B37/01268; C03B37/02; C03B37/025; C03B37/027; C03B37/02736; C03B37/029; C03C; C03C13/00; C03C13/04; C03C13/041; C03C13/042; C03C3/00; C03C3/32; C03C3/325; C03C4/00; C03C4/10; C03B2201/00; C03B2201/80; C03B2201/82; C03B2205/00; C03B2205/60; C03B2205/62; C03B2205/63; C03B2205/74; Y; Y10; Y10S; Y10S501/00; Y10S501/90; Y10S501/904
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
93 words
A method for manufacturing glass fibers using an infrared ray-transmitting glass fiber material, comprising the steps of (1) mixing BaF 2 , GdF 3 and ZrF 4 in a ratio of 28 mol% to 38 mol%, 2 mol% to 7 mol% and 58 mol% to 69 mol%, respectively, to obtain a mixture; (2) melting the mixture to provide a melt; (3) casting the melt in a metal mold with a hollow section which is preheated at a temperature of 100° C. or more, but at a temperature less than a glass deformation temperature;
Claim 2
Independent Claim
93 words
A method for manufacturing glass fibers using an infrared ray-transmitting glass fiber material, comprising the steps of (1) mixing BaF 2 , GdF 3 and ZrF 4 in a ratio of 28 mol% to 38 mol%, 2 mol% to 7 mol% and 58 mol% to 69 mol%, respectively, to obtain a mixture; (2) melting the mixture to provide a melt; (3) casting the melt in a metal mold with a hollow section which is preheated at a temperature of 100° C. or more, but at a temperature less than a glass deformation temperature;
Claim 3
Dependent Claim
115 words
(4) annealing said melt in said metal mold to form a glass rod, said glass rod forming step including heating the melt in the temperature range of about 200° C. to less than the glass deformation temperature and cooling said melt; (5) removing said glass rod from said metal mold and optically polishing it at the ends and the sides; and drawing the tip of the glass rod while applying tension to the tip of said glass rod, said drawing step including heating the tip of said glass rod and drawing the heated portion of said glass rod into a glass fiber while maintaining the temperature of the end portion of said glass rod constant.
Claim 4
Dependent Claim
115 words
(4) annealing said melt in said metal mold to form a glass rod, said glass rod forming step including heating the melt in the temperature range of about 200° C. to less than the glass deformation temperature and cooling said melt; (5) removing said glass rod from said metal mold and optically polishing it at the ends and the sides; and drawing the tip of the glass rod while applying tension to the tip of said glass rod, said drawing step including heating the tip of said glass rod and drawing the heated portion of said glass rod into a glass fiber while maintaining the temperature of the end portion of said glass rod constant.
Claim 5
Dependent Claim
28 words
A method according to claim 1, in which said step of obtaining said melt comprises melting said melt in a temperature range of 800° C. to 1000° C.
Claim 6
Dependent Claim
49 words
A method according to claim 1 or 2, in which said casting step comprises casting said melt into a metal mold made of one metal selected from the group of copper, brass, iron and aluminium, the inner surface of said mold being coated with vapor deposited gold or silver.
Claim 7
Dependent Claim
45 words
A method according to claim 1 or 2, in which said glass rod heating step of said drawing step comprises causing the temperature of the glass rod to be raised from about 300° C. at a temperature rise speed of 1° C./min to 5° C./min.
Claim 8
Dependent Claim
33 words
A method according to claim 1 or 2, in which said drawing step comprises drawing the tip of said glass rod under a tension of 1.0 mg/mm 2 to 50 mg/mm 2 .
Claim 9
Dependent Claim
31 words
A method according to claim 4, in which said drawing step comprises drawing the tip of said glass rod under a tension of 1.0 mg/mm 2 to 50 mg/mm 2 .
Claim 10
Dependent Claim
47 words
A method according to claim 4, in which said casting step comprises casting said melt into a metal mold made of one metal selected from the group of copper, brass, iron and aluminium, the inner surface of said mold being coated with vapor deposited gold or silver.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-08-09 | 1986-02-08 | 1986-08-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-08-09 | 1990-02-08 | 1990-08-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-08-09 | 1994-02-08 | 1994-08-10 | $7700.00 | Window Closed / Lapsed |