Assignee: Saint Gobain Performance Plastics Corp
•
Filing: 1980-10-24
•
Granted: 1982-08-31
•
Expires: 2000-10-24
Abstract
Abstract A laminated tubular structure is obtained by a process in which a fabric sleeve is applied about a tube of thermoplastic polymer, following which plugs are inserted into the opposing ends of the liner. A liquid, such as water, is then introduced to the liner, and the liner is rotated about a horizontal axis while heat is applied to the exterior surface of the liner, causing the surface to become molten. The heat also causes vaporization of some of the liquid in the liner and the resulting vapor pressure causes the molten surface of the liner to expand radially into the interstices of the fabric sleeve. The inner surface of the liner remains solid and form-maintaining by reason of the liquid within the liner and heat absorbed on vaporization of liquid. Upon cooling there is obtained a good mechanical bond between the liner and sleeve. The liner-sleeve composite can be further reinforced by a surrounding layer of a thermosetting resin containing reinforcing fibers, the resin layer being bonded to the composite by means of the sleeve.
Inventors
- 👤 Edward P. Anderson
- 👤 Donald G. Curran
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 16:16
CPC Classifications
F; F16; F16L; F16L9/00; F16L9/12; F16L9/121; B; B29; B29B; B29B13/00; B29B13/02; B29B13/023; B29B13/024; B29C; B29C35/00; B29C35/02; B29C35/04; B29C55/00; B29C55/22; B29C55/24; B29C63/00; B29C63/02; B29C63/04; B29C63/06; B29C70/00; B29C70/68; B29C70/82; B29L; B29L2009/00; B29L2023/00; B29L2023/22; Y; Y10; Y10T; Y10T428/00; Y10T428/13; Y10T428/131; Y10T428/1314; Y10T428/1352; Y10T428/1362; Y10T428/31504; Y10T428/3154; Y10T428/31544; Y10T428/31551; Y10T428/31645; Y10T428/31649
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
260 words
A process for forming a laminated tubular structure which comprises: (a) applying a sleeve of a fabric about a tube of thermoplastic polymer, (b) inserting a plug into each end of said liner to seal the interior of said liner from the surrounding atmosphere, at least one of said plugs having pressure relief valve means to prevent the pressure of vaporized liquid within said liner from exceeding a given value upon heating said liner and sleeve to elevated temperatures, (c) introducing to said liner a liquid which is chemically inert with respect to said liner and has a boiling point substantially below the melting point of said thermoplastic polymer, (d) applying heat to an arcuate portion of the outer surface of said liner through said sleeve while rotating said liner and sleeve, the time of heating and the rates of application of heat and rotation of said liner and sleeve being such as to cause the exterior surface of said liner to melt and volatilization of a portion of said liquid to create a pressure within said liner which exceeds the pressure of the atmosphere external of said liner to cause said liner to expand radially whereby the molten exterior surface thereof enters into the interstices of said fabric, said liquid within said liner providing a temperature gradient across the wall of said liner whereby the inner surface thereof remains solid and self-supporting, and (e) cooling said liner to solidify the exterior surface thereof to produce a permanent mechanical bond between said sleeve and the outer surface of said liner.
Claim 2
Dependent Claim
260 words
A process for forming a laminated tubular structure which comprises: (a) applying a sleeve of a fabric about a tube of thermoplastic polymer, (b) inserting a plug into each end of said liner to seal the interior of said liner from the surrounding atmosphere, at least one of said plugs having pressure relief valve means to prevent the pressure of vaporized liquid within said liner from exceeding a given value upon heating said liner and sleeve to elevated temperatures, (c) introducing to said liner a liquid which is chemically inert with respect to said liner and has a boiling point substantially below the melting point of said thermoplastic polymer, (d) applying heat to an arcuate portion of the outer surface of said liner through said sleeve while rotating said liner and sleeve, the time of heating and the rates of application of heat and rotation of said liner and sleeve being such as to cause the exterior surface of said liner to melt and volatilization of a portion of said liquid to create a pressure within said liner which exceeds the pressure of the atmosphere external of said liner to cause said liner to expand radially whereby the molten exterior surface thereof enters into the interstices of said fabric, said liquid within said liner providing a temperature gradient across the wall of said liner whereby the inner surface thereof remains solid and self-supporting, and (e) cooling said liner to solidify the exterior surface thereof to produce a permanent mechanical bond between said sleeve and the outer surface of said liner.
Claim 3
Dependent Claim
16 words
The process according to claim 1 in which the fabric sleeve is made of glass fibers.
Claim 4
Dependent Claim
24 words
The process according to claim 2 in which said sleeve is formed by wrapping a layer of woven glass fiber tape about said liner.
Claim 5
Dependent Claim
41 words
The process according to claim 2 in which said sleeve comprises a tubular knitted fabric over which is applied a reinforcing sleeve which prevents said tubular knitted fabric from expanding to the same degree as said liner upon heating said liner.
Claim 6
Dependent Claim
15 words
The process according to claim 1 in which said thermoplastic polymer is a fluorinated polymer.
Claim 7
Dependent Claim
15 words
The process according to claim 5 in which said fluorinated polymer is a tetrafluoroethylene/hexafluoropropylene copolymer.
Claim 8
Dependent Claim
14 words
The process according to claim 1 in which said thermoplastic polymer is a polyolefin.
Claim 9
Dependent Claim
20 words
The process according to claim 7 in which said polyolefin is selected from the group consisting of polyethylene and polypropylene.
Claim 10
Dependent Claim
12 words
The process according to claim 1 in which said liquid is water.
Claim 11
Dependent Claim
25 words
The process according to claim 1 in which the pressure within said liner during said heating step is from about 0.1 to about 10 psig.
Claim 12
Dependent Claim
49 words
The process according to claim 1 in which said liner is rotated about its axis by a pair of spaced rolls which extend substantially the entire length of and support said liner and sleeve, said rolls rotating about axes substantially parallel with the axis of said liner and sleeve.
Claim 13
Dependent Claim
28 words
The process according to claim 11 in which said rolls are heated to a temperature sufficient to render the exterior surface of said liner in a molten condition.
Claim 14
Dependent Claim
43 words
The process according to claim 11 in which said heat is provided by means of a hot gas which is caused to impinge upon an arcuate portion of said liner above said spaced rolls and the surface of the liquid in said liner.
Claim 15
Dependent Claim
17 words
The process according to claim 1 in which said liner is heated by means of radiant energy.
Claim 16
Dependent Claim
241 words
A process for forming a corrosion-resistant laminated tubular structure which comprises: (a) applying a sleeve of glass fabric about a seamless tube of thermoplastic fluorinated polymer, (b) inserting a plug into each end of said liner to seal the interior of said liner from the surrounding atmosphere, at least one of said plugs having pressure relief valve means to prevent the pressure of vaporized liquid within said liner from exceeding a predetermined value upon heating said liner and sleeve to elevated temperatures, (c) introducing water to said liner, (d) rotating said liner and sleeve about a substantially horizontal axis, and applying heat to an arcuate portion of the outer surface of said liner through said sleeve, the time of heating and the rates of application of heat and rotation of said liner and sleeve being such as to cause the exterior surface of said liner to melt the volatilization of a portion of said water to create a pressure of from about 0.1 to about 10 psig within said liner, to cause said liner to expand radially whereby the molten exterior surface thereof enters into the interstices of said fabric, said water within said liner providing a temperature gradient across the wall of said liner whereby the inner surface thereof remains solid and self-supporting, and (e) cooling said liner to solidify the exterior surface thereof to produce a permanent mechanical bond between said sleeve and the outer surface of said liner.
Claim 17
Dependent Claim
241 words
A process for forming a corrosion-resistant laminated tubular structure which comprises: (a) applying a sleeve of glass fabric about a seamless tube of thermoplastic fluorinated polymer, (b) inserting a plug into each end of said liner to seal the interior of said liner from the surrounding atmosphere, at least one of said plugs having pressure relief valve means to prevent the pressure of vaporized liquid within said liner from exceeding a predetermined value upon heating said liner and sleeve to elevated temperatures, (c) introducing water to said liner, (d) rotating said liner and sleeve about a substantially horizontal axis, and applying heat to an arcuate portion of the outer surface of said liner through said sleeve, the time of heating and the rates of application of heat and rotation of said liner and sleeve being such as to cause the exterior surface of said liner to melt the volatilization of a portion of said water to create a pressure of from about 0.1 to about 10 psig within said liner, to cause said liner to expand radially whereby the molten exterior surface thereof enters into the interstices of said fabric, said water within said liner providing a temperature gradient across the wall of said liner whereby the inner surface thereof remains solid and self-supporting, and (e) cooling said liner to solidify the exterior surface thereof to produce a permanent mechanical bond between said sleeve and the outer surface of said liner.
Claim 18
Dependent Claim
15 words
The process according to claim 15 in which said fluorinated polymer is a tetrafluoroethylene/hexafluoropropylene copolymer.
Claim 19
Dependent Claim
49 words
The process according to claim 15 in which said liner and sleeve are supported and rotated by a pair of spaced rolls which extend substantially the entire length of said liner and sleeve, said rolls having axes of rotation substantially parallel to the axis of said liner and sleeve.
Claim 20
Dependent Claim
28 words
The process according to claim 17 in which said rolls are heated to a temperature sufficient to render the exterior surface of said liner in a molten condition.
Claim 21
Dependent Claim
44 words
The process according to claim 17 in which said heat is provided by means of a hot gas which is caused to impinge upon an arcuate portion of said liner above said said spaced rolls and the surface of the liquid in said liner.
Claim 22
Dependent Claim
17 words
The process according to claim 15 in which said liner is heated by means of radiant energy.
References Cited (Backward Citations)
US1798798A
Cited
US2752952A
Cited
US2783173A
Cited
US2888042A
Cited
US2974713A
Cited
US3414448A
Cited
US4104095A
Cited
US4282905A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-08-30 | 1986-03-01 | 1986-08-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-08-30 | 1990-03-01 | 1990-08-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-08-30 | 1994-03-01 | 1994-08-31 | $7700.00 | Window Closed / Lapsed |