Oxygen content exhaust gas sensor, and method of its manufacture
Assignee: Robert Bosch GmbH
•
Filing: 1980-03-25
•
Granted: 1982-08-31
•
Expires: 2000-03-25
Abstract
Abstract To improve operation and output voltage, particularly at 400° C. and less, an oxygen sensor, especially adapted to determine oxygen content of automotive exhaust gases, is constructed by utilizing two electrodes applied on a body of stabilized zirconium dioxide, for example a closed tube, by making an electrode exposed to the exhaust gases in form of a mixture of finely dispersed ceramic material and a platinum-rhodium alloy, the ceramic material being present at about 40% (by volume) and 60% (by volume) platinum-rhodium alloy of 50-94% platinum and 50-6% rhodium (by weight). The second electrode, exposed to a reference gas comprises an alloy of palladium and another noble metal in a ratio of about 19-90% (by weight) Pd and 81-10% (by weight) noble metal. This electrode may also contain up to 40% (by volume) finely dispersed ceramic material. The electrode exposed to the exhaust gases is covered with a porous coating. The electrodes can be applied as aqueous or organic solutions of soluble noble metal compounds or suspensions, colloidal suspensions, with organic solvents, and the like, and subsequent sintering.
Inventors
- 👤 Hermann Fischer
- 👤 Karl-Hermann Friese
- 👤 Hans-Ulrich Gruber
- 👤 Wolfgang Heinemann
- 👤 Gunter Knoll
- 👤 Ernst Linder
- 👤 Helmut Maurer
- 👤 Rainer Noack
- 👤 Leo Steinke
- 👤 Lothar Weber
- 👤 Helmut Weyl
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 13:48
CPC Classifications
G; G01; G01N; G01N27/00; G01N27/26; G01N27/403; G01N27/406; G01N27/407; G01N27/4075; G01N27/4078; H; H01; H01M; H01M4/00; H01M4/86; H01M4/88; H01M4/8803; H01M4/881; H01M4/8878; H01M4/8882; H01M4/8885; H01M4/90; H01M4/9041; H01M4/905; H01M4/9066; H01M8/00; H01M8/10; H01M8/12; H01M8/1213; Y; Y02; Y02E; Y02E60/00; Y02E60/30; Y02E60/50; Y02P; Y02P70/00; Y02P70/50
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
135 words
Electrochemical sensor to determine the oxygen content in gases resulting from a combustion process, particularly exhaust gases from an internal combustion engine having a solid electrolyte body (1) comprising stabilized zirconium dioxide, having a first surface portion exposed to the combustion gases, and a second surface portion exposed to a reference substance of known oxygen concentration; a first electrode (12) applied to said first surface portion; a second electrode (13) applied to said second surface portion; and a porous ceramic protective cover layer (112) covering the first electrode, and wherein, in accordance with the invention, the electrodes are characterized in that the first electrode comprises a mixture of powdery ceramic material, forming a support structure or support lattice, and a platinum-rhodium alloy; and the second electrode comprises an alloy of palladium and another noble metal.
Claim 2
Dependent Claim
135 words
Electrochemical sensor to determine the oxygen content in gases resulting from a combustion process, particularly exhaust gases from an internal combustion engine having a solid electrolyte body (1) comprising stabilized zirconium dioxide, having a first surface portion exposed to the combustion gases, and a second surface portion exposed to a reference substance of known oxygen concentration; a first electrode (12) applied to said first surface portion; a second electrode (13) applied to said second surface portion; and a porous ceramic protective cover layer (112) covering the first electrode, and wherein, in accordance with the invention, the electrodes are characterized in that the first electrode comprises a mixture of powdery ceramic material, forming a support structure or support lattice, and a platinum-rhodium alloy; and the second electrode comprises an alloy of palladium and another noble metal.
Claim 3
Dependent Claim
48 words
Sensor according to claim 1, wherein the platinum-rhodium alloy of the first electrode comprises an alloy of between 50 to 94% platinum and 50 to 6% rhodium, both by weight; and wherein the second electrode comprises 19 to 90% palladium and 81 to 10% platinum, both by weight.
Claim 4
Dependent Claim
40 words
Sensor according to claim 2, wherein the alloy of the first electrode comprises about 88% platinum and 12% rhodium, both by weight; and wherein the alloy of the second electrode comprises about 69% palladium and 31% platinum, both by weight.
Claim 5
Dependent Claim
14 words
Sensor according to claim 1, wherein the second electrode additionally include powdery ceramic material.
Claim 6
Dependent Claim
27 words
Sensor according to claim 4, wherein the ceramic material comprises at least one of the materials of the group consisting of: stabilized zirconium dioxide and aluminum oxide.
Claim 7
Dependent Claim
39 words
Sensor according to claim 5, wherein the first electrode has about 60% platinum-rhodium alloy and 40% stabilized zirconium dioxide powder; and the second electrode has about 60% palladium-platinum alloy and 40% stabilized zirconium dioxide powder; all proportions by volume.
Claim 8
Dependent Claim
27 words
Sensor according to claim 1, wherein the ceramic material comprises at least one of the materials of the group consisting of: stabilized zirconium dioxide and aluminum oxide.
Claim 9
Dependent Claim
19 words
Sensor according to claim 1, wherein the second electrode comprises a palladium-silver alloy having about 9 to 70%--by weight-silver.
Claim 10
Dependent Claim
37 words
Sensor according to claim 8, wherein the second electrode comprises a mixture of zirconium dioxide powder forming a support structure or lattice; and the ratio of alloy to zirconium dioxide is about 60 to 40% by volume.
Claim 11
Dependent Claim
67 words
Sensor according to claim 1, wherein at least one of the electrodes has the form of a conductive track or path; and a layer of noble metal applied to the solid electrolyte body and over the at least one electrode comprising a noble metal or a mixture of noble metals capable of catalyzing the thermodynamic equilibrium of gases to which the electrode and said layer are exposed.
Claim 12
Dependent Claim
276 words
Method to make an electrochemical sensor to determine the oxygen content in gases resulting from a combustion process, particularly the exhaust gases from an internal combustion engine, having a solid electrolyte body (1) comprising stabilized zirconium dioxide and having a first surface portion exposed to the gases and a second surface portion exposed to a reference substance of known oxygen concentration; a first electrode (12) applied to said first surface portion; a second electrode (13) applied to the second surface portion; and a porous ceramic protective cover layer (112) covering the first electrode, said method comprising the steps of 1. providing a presintered solid electrolyte body comprising stabilized zirconium dioxide; 1.1 applying a platinum-rhodium alloy and powdery ceramic material to said first surface to form the first electrode, shaped in form of a conductive track; 1.2 applying a palladium-platinum alloy on the second surface to form the second electrode, shaped in form of a conductive track; 2. sintering the solid electrolyte body with the electrode layers applied thereto at a temperature of between about 1400° to 1700° C.; 3. supplying a layer of a noble metal or a mixture of noble metals over at least said second electrode and covering the second electrode at least in part, said noble metal or mixture of noble metals comprising at least one of the materials of the group of consisting of 3.1 noble metal alloys dissolved in water or organic solvents; 3.2 colloidal noble metal suspension; 3.3 powdered noble metal suspension; 4. sintering the layer of step 3 at a temperature of between about 800° C. to 1300° C.; and 5. applying the porous ceramic protective covering layer (112).
Claim 13
Dependent Claim
276 words
Method to make an electrochemical sensor to determine the oxygen content in gases resulting from a combustion process, particularly the exhaust gases from an internal combustion engine, having a solid electrolyte body (1) comprising stabilized zirconium dioxide and having a first surface portion exposed to the gases and a second surface portion exposed to a reference substance of known oxygen concentration; a first electrode (12) applied to said first surface portion; a second electrode (13) applied to the second surface portion; and a porous ceramic protective cover layer (112) covering the first electrode, said method comprising the steps of 1. providing a presintered solid electrolyte body comprising stabilized zirconium dioxide; 1.1 applying a platinum-rhodium alloy and powdery ceramic material to said first surface to form the first electrode, shaped in form of a conductive track; 1.2 applying a palladium-platinum alloy on the second surface to form the second electrode, shaped in form of a conductive track; 2. sintering the solid electrolyte body with the electrode layers applied thereto at a temperature of between about 1400° to 1700° C.; 3. supplying a layer of a noble metal or a mixture of noble metals over at least said second electrode and covering the second electrode at least in part, said noble metal or mixture of noble metals comprising at least one of the materials of the group of consisting of 3.1 noble metal alloys dissolved in water or organic solvents; 3.2 colloidal noble metal suspension; 3.3 powdered noble metal suspension; 4. sintering the layer of step 3 at a temperature of between about 800° C. to 1300° C.; and 5. applying the porous ceramic protective covering layer (112).
Claim 14
Dependent Claim
28 words
Method according to claim 11, wherein the step 1.2 comprises applying a mixture of a powdery ceramic material together with the palladium-platinum alloy to form the second electrode.
Claim 15
Dependent Claim
38 words
Method according to claim 11, further including the step of dispersing the layer applied in step 3 on the respective surface of the solid electrolyte body with a stream or blast of air before the sintering step 4.
Claim 16
Dependent Claim
82 words
Method according to claim 11, wherein the noble metal or noble metal layer applied in step 3 is applied to both surface portions of the solid electrolyte body covering, at least in part, both of the electrodes; and the step of applying the porous ceramic layer is carried out after step 4 by applying the material of said porous layer on the noble metal or noble metal mixture layer applied in step 3 and over the electrode at said first surface portion.
Claim 17
Dependent Claim
78 words
Method according to claim 11, wherein the step of applying the layer of noble metal or mixture of noble metals of step 3 comprises applying said layer only on the second surface portion of the solid electrolyte body and over the second electrode (13); and the step of applying the porous ceramic protective cover layer (112) is carried out in advance of the sintering step, step 2, to sinter the porous ceramic layer and the electrode layer together.
Claim 18
Dependent Claim
40 words
Method according to claim 15, wherein the step of applying the porous ceramic protective cover layer comprises applying a layer of pulverized material comprising at least one of the materials of the group consisting of magnesium spinel and aluminum oxide.
Claim 19
Dependent Claim
30 words
Method according to claim 16, further including the step of adding a pore forming substance to said material forming the porous ceramic protective cover layer (112) prior to sintering thereof.
Claim 20
Dependent Claim
60 words
Method according to claim 11, wherein the step of applying the noble metal or mixture of noble metals of step 3 comprises applying to the respective surface portion of the solid electrolyte body at least one of the materials of the group consisting of: noble metal resin ester; noble metal acetylacetonate in an organic binder and a noble metal suspension.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-08-30 | 1986-03-01 | 1986-08-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-08-30 | 1990-03-01 | 1990-08-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-08-30 | 1994-03-01 | 1994-08-31 | $7700.00 | Window Closed / Lapsed |