Curable aqueous silicate composition, uses thereof, and coatings or layers made therefrom

Claim 2

An aqueous silicate composition which is curable at room temperature and which comprises: (a) an aqueous solution or colloidal dispersion of an alkali metal silicate; (b) an aqueous latex comprising elastomeric latex particles stably distributed in an aqueous medium; (c) at least one metal salt of a divalent metal, said metal salt being a coreactant for said alkali metal silicate at room temperature, having a reactivity with alkali metal silicates at least equal to the cations of metals of Group II, A or B, of the Periodic Table, and having a water solubility ranging from about 10 -1 to 10 -4 weight-% at a pH of 7 and room temperature; provided that: if said water solubility is greater than 10 -2 weight-%, any divalent metal cation of said metal salt is less reactive with alkali metal silicates than Ca ++ , and if said water solubility is less than 10 -3 weight-%, a divalent cation of said metal salt is more reactive with alkali metal silicates than -325 U.S. mesh ZnO; said component (c) being selected to provide a sufficiently complete curing of said alkali metal silicate to impart, to a 10 mm-thick coating of said composition after 14 days of curing at room temperature, water resistance and a Barcol hardness of at least 10 at the exposed or top surface of the coating; said component (c) also being selected to permit a pot life for said composition of at least 15 minutes at room temperature.

Claim 3

An aqueous silicate composition according to claim 1 wherein said component (c) includes a phosphate salt.

Claim 4

An aqueous silicate composition according to claim 1 wherein said component (c) comprises a plurality of salts of Group II, A or B, of the Periodic Table, at least one of said salts being a magnesium salt.

Claim 5

An aqueous silicate composition according to claim 1 wherein said component (c) includes a salt of the formula Mg 3 (PO 4 ) 2 .xH 2 O, wherein x is a number ranging from 0 to 8, said salt having a water solubility at room temperature which is greater than 10 -3 weight-% but less than 10 -1 weight-%.

Claim 6

A curable composition according to claim 1 wherein said component (a) comprises a colloidal dispersion of a sodium or potassium silicate of the formula M 2 O.nSiO 2 , wherein M represents sodium or potassium and n is a number of moles ranging from 1.6 to about 4.

Claim 7

A composition according to claim 5 wherein said component (c) comprises a combination of a carbonate salt and a phosphate salt, at least one of said salts being a salt of magnesium.

Claim 8

A cured layer at least about 1.5 mm. thick on a substrate wherein the layer comprises the composition of claim 1 which has been cured to a crosslinked solid upon the substrate.

Claim 9

An aqueous silicate composition according to claim 1 which dries and cures to a solid, crosslinked mass at room temperature, said composition comprising: (a) an aqueous colloidal dispersion comprising about 5 to about 65% by weight of a dispersed colloidal silicate of the formula M 2 O.nSiO 2 , wherein M represents sodium or potassium and n is a number of moles ranging from about 1.6 to about 4; (b) about 5 to about 25 parts by weight, per 100 parts by weight of said aqueous colloidal dispersion, of an aqueous latex comprising about 10 to about 80% by weight of elastomeric latex particles stably distributed in an aqueous medium; (c) about 1 to about 50 parts by weight, per 100 parts by weight of said aqueous colloidal dispersion, of tri-magnesium phosphate; (1) about 1 to about 50 parts by weight, per 100 parts by weight of said aqueous colloidal dispersion, of magnesium carbonate; and (e) an amount of water sufficient to make said aqueous silicate composition sprayable.

Claim 10

A cured coating on a substrate comprising the composition of claim 1 which has been coated onto and cured upon said substrate.

Claim 11

A method of applying an insulative, fireretardant coating to a substrate comprising the steps of: (a) blending the composition of claim 1 with a non-flammable inorganic filler to obtain a sprayable coating composition; (b) spraying said sprayable coating composition onto a substrate to form a coating thereon; and (c) permitting the resulting coating to dry and cure for at least 16 hours at ambient temperatures.

Claim 12

A two-part curable composition which is curable at room temperature when the two parts are blended together, said composition comprising: in a first part, an aqueous solution or dispersion of an alkali metal silicate, in a second part, a coreactant for said alkali metal silicate comprising a phosphate salt of a divalent metal of Group II of the Periodic Table, said phosphate salt having a water solubility ranging from 10 -1 to 10 -4 weight-% at room temperature; provided that: if said water solubility is greater than 10 -2 weight-%, any divalent metal cation of said metal salt is less reactive with alkali metal silicates than Ca ++ , and if said water solubility is less than 10 -3 weight-%, a divalent cation of said metal salt is more reactive with alkali metal silicates than -325 U.S. mesh ZnO; said coreactant being selected to provide a sufficiently complete curing of said alkali metal silicate to impart, to a 10 mm-thick coating of said composition after 14 days of curing at room temperature, water resistance and a Barcol hardness of at least 10 at the exposed or top surface of the coating; said coreactant also being selected to permit a pot life for said composition of at least 15 minutes at room temperature.

Claim 13

A two-part curable composition which is curable at room temperature when the two parts are blended together, said composition comprising: in a first part, an aqueous solution or dispersion of an alkali metal silicate, in a second part, a coreactant for said alkali metal silicate comprising a phosphate salt of a divalent metal of Group II of the Periodic Table, said phosphate salt having a water solubility ranging from 10 -1 to 10 -4 weight-% at room temperature; provided that: if said water solubility is greater than 10 -2 weight-%, any divalent metal cation of said metal salt is less reactive with alkali metal silicates than Ca ++ , and if said water solubility is less than 10 -3 weight-%, a divalent cation of said metal salt is more reactive with alkali metal silicates than -325 U.S. mesh ZnO; said coreactant being selected to provide a sufficiently complete curing of said alkali metal silicate to impart, to a 10 mm-thick coating of said composition after 14 days of curing at room temperature, water resistance and a Barcol hardness of at least 10 at the exposed or top surface of the coating; said coreactant also being selected to permit a pot life for said composition of at least 15 minutes at room temperature.

Claim 14

A two-part composition according to claim 11 wherein said phosphate salt is an orthophosphate.

Claim 15

A two-part composition according to claim 11 wherein said coreactant comprises the combination of a tri-magnesium phosphate hydrate with magnesium carbonate.

Claim 16

A two-part composition according to claim 11 which further includes an aqueous elastomer latex in at least one of the two parts.

Claim 17

A two-part composition according to claim 11 comprising: in the first part, an aqueous colloidal dispersion comprising about 5 to about 65% by weight of a dispersed colloidal silicate of the formula M 2 O.nSiO 2 , wherein M represents sodium or potassium and n is a number of moles ranging from about 1.6 to about 4; in the second part, about 1 to about 50 parts by weight of magnesium carbonate, on the basis of each 100 parts by weight of the aqueous colloidal dispersion in said first part, and about 1 to about 50 parts by weight, on the same basis, of tribasic magnesium phosphate; and an amount of water in said second part which is sufficient to make said two-part composition sprayable when the two parts have been blended together.

Claim 18

A method for applying an insulative, fireretardant coating to a substrate comprising the steps of: (a) blending together the first and second parts of the composition of claim 11, and blending the resulting curable mixture with a nonflammable inorganic filler to obtain a sprayable coating composition; (b) spraying said sprayable coating composition onto a substrate to form a coating thereon; and (c) drying and curing the resulting coating for at least about 16 hours at ambient temperatures.

Claim 19

An aqueous silicate composition which is curable at room temperature and which comprises: (a) an aqueous solution or colloidal dispersion of an alkali metal silicate; (b) a combination of a divalent metal carbonate and a divalent metal phosphate or borate, wherein said metal salts are coreactants for said alkali metal silicate at room temperature, having a reactivity with alkali metal silicates at least equal to the cations of metals of Group II, A or B, of the Periodic Table, and having a water solubility ranging from about 10 -1 to 10 -4 weight-% at a pH of 7 and room temperature; provided that: if said water solubility is greater than 10 -2 weight-%, any divalent metal cation of said metal salts is less reactive with alkali metal silicates than Ca ++ , and if said water solubility is less than 10 -3 weight-%, a divalent cation of said metal salts is more reactive with alkali metal silicates than -325 U.S. mesh ZnO; said component (b) being selected to provide a sufficiently complete curing of said alkali metal silicate to impart, to a 10 mm-thick coating of said composition after 14 days of curing at room temperature, water resistance and a Barcol hardness of at least 10 at the exposed or top surface of the coating; said component (b) also being selected to permit a pot life for said composition of at least 15 minutes at room temperature.

Claim 20

An aqueous silicate composition which is curable at room temperature and which comprises: (a) an aqueous solution or colloidal dispersion of an alkali metal silicate; (b) a combination of a divalent metal carbonate and a divalent metal phosphate or borate, wherein said metal salts are coreactants for said alkali metal silicate at room temperature, having a reactivity with alkali metal silicates at least equal to the cations of metals of Group II, A or B, of the Periodic Table, and having a water solubility ranging from about 10 -1 to 10 -4 weight-% at a pH of 7 and room temperature; provided that: if said water solubility is greater than 10 -2 weight-%, any divalent metal cation of said metal salts is less reactive with alkali metal silicates than Ca ++ , and if said water solubility is less than 10 -3 weight-%, a divalent cation of said metal salts is more reactive with alkali metal silicates than -325 U.S. mesh ZnO; said component (b) being selected to provide a sufficiently complete curing of said alkali metal silicate to impart, to a 10 mm-thick coating of said composition after 14 days of curing at room temperature, water resistance and a Barcol hardness of at least 10 at the exposed or top surface of the coating; said component (b) also being selected to permit a pot life for said composition of at least 15 minutes at room temperature.

Claim 21

An aqueous silicate insulation composition which is curable at room temperature and which comprises: (a) an aqueous solution or colloidal dispersion of an alkali metal silicate; (b) a combination of a divalent metal carbonate and a divalent metal phosphate or borate, wherein said metal salts are coreactants for said alkali metal silicate at room temperature, having a reactivity with alkali metal silicates at least equal to the cations of metals of Group II, A or B, of the Periodic Table, and having a water solubility ranging from about 10 -1 to 10 -4 weight-% at a pH of 7 and room temperature; provided that: if said water solubility is greater than 10 -2 weight-%, any divalent metal cation of said metal salts is less reactive with alkali metal silicates than Ca ++ , and if said water solubility is less than 10 -3 weight-%, a divalent cation of said metal salts is more reactive with alkali metal silicates than -325 U.S. mesh ZnO; said component (b) being selected to provide a sufficiently complete curing of said alkali metal silicate to impart, to a 10 mm-thick coating of said composition after 14 days of curing at room temperature, water resistance and a Barcol hardness of at least 10 at the exposed or top surface of the coating; said component (b) also being selected to permit a pot life for said composition of at least 15 minutes at room temperature, and (c) a filler comprising a particulate aggregate.

Claim 22

An aqueous silicate insulation composition which is curable at room temperature and which comprises: (a) an aqueous solution or colloidal dispersion of an alkali metal silicate; (b) a combination of a divalent metal carbonate and a divalent metal phosphate or borate, wherein said metal salts are coreactants for said alkali metal silicate at room temperature, having a reactivity with alkali metal silicates at least equal to the cations of metals of Group II, A or B, of the Periodic Table, and having a water solubility ranging from about 10 -1 to 10 -4 weight-% at a pH of 7 and room temperature; provided that: if said water solubility is greater than 10 -2 weight-%, any divalent metal cation of said metal salts is less reactive with alkali metal silicates than Ca ++ , and if said water solubility is less than 10 -3 weight-%, a divalent cation of said metal salts is more reactive with alkali metal silicates than -325 U.S. mesh ZnO; said component (b) being selected to provide a sufficiently complete curing of said alkali metal silicate to impart, to a 10 mm-thick coating of said composition after 14 days of curing at room temperature, water resistance and a Barcol hardness of at least 10 at the exposed or top surface of the coating; said component (b) also being selected to permit a pot life for said composition of at least 15 minutes at room temperature, and (c) a filler comprising a particulate aggregate.

Claim 23

The composition of claim 17 or 18 wherein the divalent metal phosphate of component (b) comprises magnesium phosphate.

Claim 24

The composition of claim 17 or 18 wherein the divalent metal phosphate of component (b) comprises zinc phosphate.

Claim 25

The composition of claim 17 or 18 wherein the divalent metal phosphate of component (b) comprises a divalent metal pyrophosphate.

Claim 26

The composition of claim 17 or 18 wherein the divalent metal phosphate of component (b) comprises a divalent metal orthophosphate.

Claim 27

The composition of claim 17 or 18 wherein the divalent metal phosphate of component (b) comprises zinc pyrophosphate.

Claim 28

The composition of claim 17 or 18 wherein the divalent metal phosphate of component (b) comprises Mg 3 (PO 4 ) 2 .XH 2 O, wherein X is a number ranging from 0 to 8, said salt having a water solubility at room temperature which is greater than 10 -3 weight-% but less than 10 -1 weight-%.

Claim 29

The composition of claim 17 or 18 wherein the divalent metal borate of component (b) comprises magnesium borate.

Claim 30

The composition of claim 17 or 18 wherein the divalent metal borate of component (b) comprises zinc borate.

Claim 31

The composition of claim 17 or 18 wherein the divalent metal carbonate of component (b) comprises magnesium carbonate.

Claim 32

The composition of claim 17 or 18 wherein the divalent metal carbonate of component (b) comprises zinc carbonate.

Claim 33

The composition of claim 17 or 18 wherein the combination of divalent metal carbonate and divalent metal phosphate or borate in component (b) comprises a trimagnesium phosphate hydrate and magnesium carbonate.

Claim 34

The composition of claim 17 or 18 wherein the combination of divalent metal carbonate and divalent metal phosphate or borate in component (b) comprises magnesium carbonate and zinc borate.

Claim 35

The composition of claim 17 or 18 wherein component (a) comprises a colloidal dispersion of a sodium or potassium silicate of the formula M 2 O.nSiO 2 , wherein M represents sodium or potassium and n is a number of moles ranging from 1.6 to about 4.

Claim 36

The composition of claim 17 or 18 which further comprises an aqueous latex comprising elastomeric latex particles stably distributed in an aqueous medium.

Claim 37

The composition of claim 17 or 18 wherein: component (a) comprises an aqueous colloidal dispersion comprising about 5 to about 65% by weight of a dispersed colloidal silicate of the formula M 2 O.nSiO 2 , wherein M represents sodium or potassium and n is a number of moles ranging from about 1.6 to about 4; component (b) comprises about 1 to about 50 parts by weight of magnesium carbonate, on the basis of each 100 parts by weight of the aqueous colloidal dispersion in component (a), and about 1 to about 50 parts by weight, on the same basis, of tribasic magnesium phosphate; and an amount of water in component (b) which is sufficient to make said composition sprayable when the parts have been blended together.

Claim 38

A coating composition which dries and cures to a solid, crosslinked mass at room temperature, which comprises: (a) an aqueous colloidal dispersion comprising about 5 to about 65% by weight of a dispersed colloidal silicate of the formula M 2 O.nSiO 2 , wherein M represents sodium or potassium and n is a number of moles ranging from about 1.6 to about 4; (b) about 5 to about 25 parts by weight, per 100 parts by weight of said aqueous colloidal dispersion, of an aqueous latex comprising about 10 to about 80% by weight of elastomeric latex particles stably distributed in an aqueous medium; (c) about 1 to about 50 parts by weight, per 100 parts by weight of said aqueous colloidal dispersion, of trimagnesium phosphate; (d) about 1 to about 50 parts by weight, per 100 parts by weight of said aqueous colloidal dispersion, of magnesium carbonate; and (e) an amount of water sufficient to make said aqueous silicate composition sprayable.

Claim 39

A coating composition which dries and cures to a solid, crosslinked mass at room temperature, which comprises: (a) an aqueous colloidal dispersion comprising about 5 to about 65% by weight of a dispersed colloidal silicate of the formula M 2 O.nSiO 2 , wherein M represents sodium or potassium and n is a number of moles ranging from about 1.6 to about 4; (b) about 5 to about 25 parts by weight, per 100 parts by weight of said aqueous colloidal dispersion, of an aqueous latex comprising about 10 to about 80% by weight of elastomeric latex particles stably distributed in an aqueous medium; (c) about 1 to about 50 parts by weight, per 100 parts by weight of said aqueous colloidal dispersion, of trimagnesium phosphate; (d) about 1 to about 50 parts by weight, per 100 parts by weight of said aqueous colloidal dispersion, of magnesium carbonate; and (e) an amount of water sufficient to make said aqueous silicate composition sprayable.

Claim 40

The composition of claim 17, 18, or 34 which further comprises an amount of ZnO sufficient to impart additional water resistance to the composition when cured.

Claim 41

A method of applying an insulative, fire-retardant coating to a substrate which comprises the steps of: (a) blending the composition of claim 19 or 36 with a non-flammable inorganic filler to obtain a sprayable coating composition; (b) spraying said sprayable coating composition onto a substrate to form a coating thereon; and (c) permitting the resulting coating to dry and cure for at least 16 hours at ambient temperatures.

Claim 42

A cured coating on a substrate comprising the composition of claim 17, 18, or 34 which has been coated onto and cured upon said substrate.

Claim 43

A cured layer on a substrate wherein the layer is at least about 1.5 mm thick and comprises the composition of claim 17, 18, or 34 which has been cured to a crosslinked solid upon the substrate.

Claim 44

The composition of claim 18 wherein the inorganic aggregate comprises an inorganic aggregate.

Claim 45

The composition of claim 18 wherein the inorganic aggregate comprises cellulosic material.

Claim 46

The composition of claim 39 wherein the inorganic aggregate comprises an expanded rock.

Claim 47

The composition of claim 39 wherein the inorganic aggregate comprises perlite.

Claim 48

The composition of claim 39 wherein the inorganic aggregate comprises vermiculite.

Claim 49

The composition of claim 39 wherein the inorganic aggregate comprises mineral wool.

Claim 50

The composition of claim 39 wherein the inorganic aggregate comprises glass foam.

Claim 51

The composition of claim 39 wherein the inorganic aggregate comprises glass fibers.

Claim 52

The composition of claim 18 wherein the aggregate comprises an aggregate having a particulate size suitable for spraying.

Claim 53

The composition of claim 47 wherein the aggregate having a particulate size suitable for spraying comprises an aggregate having a particulate mesh size of about -4 mesh to -8+100 mesh, and having a bulk or apparent density less than about 0.4 grams/cc.

Claim 54

A method of applying an insulation coating wherein the particulate aggregate of claim 18 is cosprayed.