Starch based adhesives and method therefor
Assignee: HARPER-LOVE ADHESIVES Corp 319 CROMPTON STREET CHARLOTTE NC 28220 A CORP OF
•
Filing: 1981-11-27
•
Granted: 1982-11-16
•
Expires: 2001-11-27
Abstract
Abstract A process for preparing a carrier type starch which is characterized by the steps of mixing two starch portions having different gelatinization temperatures with water to form a slurry and causing gelatinization of the starch portion having the lower gelatinization temperature to thereby form a stable gelatinized carrier for the raw starch portion having the higher gelatinization temperature. The ratio of the starch portion having the lower gelatinization temperature to the starch portion having the higher gelatinization temperature is preferably of the order of from 1:10 to 1:4 and the ratio by weight of the starch portions to water is of the order of from 1:2 to 1:4, preferably about 1:3. A carrier type starch based adhesive comprising a mixture of a gelatinized carrier starch portion and a raw starch portion having a higher gelatinization temperature dispersed in the carrier portion is also disclosed.
Inventors
- 👤 Leon A. Allen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 03:45
CPC Classifications
C; C09; C09J; C09J103/00; C09J103/02; C08; C08L; C08L2666/00; C08L2666/02; C08L2666/54
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
186 words
A process for preparing a carrier-type starch adhesive comprising the steps of: (a) preparing a mixture of first and second starch portions, a suitable alkali, and water to form a slurry, the first starch portion having a gelatinisation temperature at least about 2° C. lower than the second starch portion, said mixing comprising mixing the first starch portion in a weight ratio of from about 1 to 10 to about 1 to 50 relative the water, and the second starch portion in a weight ratio of from about 1 to 2 to about 1 to 8 relative the water, and the total starch portion in a weight ratio of from about 1 to 2 to about 1 to 4 relative the water; and (c) causing gelatinisation of the starch portion having the lower gelatinisation temperature to thereby form a stable gelatinised carrier for the raw starch portion having the higher gelatinisation temperature, said causing of gelatinisation including maintaining the slurry at a temperature below the gelatinisation temperature of the second starch portion but at least as high as the gelatinisation temperature of the first starch portion.
Claim 2
Dependent Claim
186 words
A process for preparing a carrier-type starch adhesive comprising the steps of: (a) preparing a mixture of first and second starch portions, a suitable alkali, and water to form a slurry, the first starch portion having a gelatinisation temperature at least about 2° C. lower than the second starch portion, said mixing comprising mixing the first starch portion in a weight ratio of from about 1 to 10 to about 1 to 50 relative the water, and the second starch portion in a weight ratio of from about 1 to 2 to about 1 to 8 relative the water, and the total starch portion in a weight ratio of from about 1 to 2 to about 1 to 4 relative the water; and (c) causing gelatinisation of the starch portion having the lower gelatinisation temperature to thereby form a stable gelatinised carrier for the raw starch portion having the higher gelatinisation temperature, said causing of gelatinisation including maintaining the slurry at a temperature below the gelatinisation temperature of the second starch portion but at least as high as the gelatinisation temperature of the first starch portion.
Claim 3
Dependent Claim
26 words
The process of claim 1 and further comprising the step of adding a suitable buffering material to the slurry following gelatinisation of the first starch portion.
Claim 4
Dependent Claim
41 words
The process of claim 1, wherein gelatinisation of said first starch portion having the lower gelatinisation temperature is achieved by heating said slurry of step a. at least until the lower gelatinisation temperature is reached but below the higher gelatinisation temperature.
Claim 5
Dependent Claim
26 words
The process of claim 3 and further comprising the step of adding a suitable buffering material to the slurry following gelatinisation of the first starch portion.
Claim 6
Dependent Claim
20 words
The process of claim 4 wherein said alkali is caustic soda and said buffering material is borax or boric acid.
Claim 7
Dependent Claim
30 words
The process of claim 3 in which the first starch portion has a gelatinisation temperature at least about 5° C. lower than the gel temperature of the second starch portion.
Claim 8
Dependent Claim
68 words
The process of claim 6 in which the weight ratio of the first starch portion to the water is from about 1 to 25 to about 1 to 35, the weight ratio of the second starch portion to the water is from about 1 to 3 to about 1 to 5, and the weight ratio of the two starch portions to the water is about 1 to 3.
Claim 9
Dependent Claim
35 words
The process of claim 7 wherein the ratio of the first starch portion having the lower gelatinisation temperature to the second starch portion having the higher gelatinisation temperature is from about 1:10 to about 1:4.
Claim 10
Dependent Claim
44 words
The process of claim 8 wherein the starch portion having the lower gelatinisation temperature is selected from the group consisting of wheat, tapicoa and potato, and the starch having the higher gelatinisation temperature is selected from the group consisting of corn, tapioca and wheat.
Claim 11
Dependent Claim
84 words
The process of claim 1, wherein step a. comprises mixing the alkali with water prior to addition of the first starch portion, and in which said causing of gelatinisation of said first starch portion having the lower gelatinisation temperature comprises mixing said first starch portion with the alkaline water maintained at a temperature high enough to cause the starch portion for the lower gelatinisation temperature to gelatinise as said slurry is mixed but low enough to prevent significant gelatinisation of the second starch portion.
Claim 12
Dependent Claim
26 words
The process of claim 10 and further comprising the step of adding a suitable buffering material to the slurry following gelatinisation of the first starch portion.
Claim 13
Dependent Claim
20 words
The process of claim 11 wherein said alkali is caustic soda and said buffering material is borax or boric acid.
Claim 14
Dependent Claim
185 words
A process for preparing a carrier-type starch adhesive comprising the steps of: (a) preparing a mixture of first and second starch portions and water to form a slurry, the first starch portion having a gelatinisation temperature at least about 2° C. lower than the second starch portion, said mixing comprising mixing the first starch portion in a weight ratio of from about 1 to 10 to about 1 to 50 relative the water, and the second starch portion in a weight ratio of from about 1 to 2 to about 1 to 8 relative the water, and the total starch portion in a weight ratio of from about 1 to 2 to about 1 to 4 relative to the water, and (b) heating said slurry to a temperature below the gel temperature of the second starch portion at the specific alkaline conditions depending on the quantity of alkaly to be added under (c) but at least as high as the gel temperature of the first starch portion; and (c) adding to the heated slurry a suitable alkaline to cause gelatinisation of the first starch portion.
Claim 15
Dependent Claim
185 words
A process for preparing a carrier-type starch adhesive comprising the steps of: (a) preparing a mixture of first and second starch portions and water to form a slurry, the first starch portion having a gelatinisation temperature at least about 2° C. lower than the second starch portion, said mixing comprising mixing the first starch portion in a weight ratio of from about 1 to 10 to about 1 to 50 relative the water, and the second starch portion in a weight ratio of from about 1 to 2 to about 1 to 8 relative the water, and the total starch portion in a weight ratio of from about 1 to 2 to about 1 to 4 relative to the water, and (b) heating said slurry to a temperature below the gel temperature of the second starch portion at the specific alkaline conditions depending on the quantity of alkaly to be added under (c) but at least as high as the gel temperature of the first starch portion; and (c) adding to the heated slurry a suitable alkaline to cause gelatinisation of the first starch portion.
Claim 16
Dependent Claim
188 words
A carrier type starch based adhesive prepared by the process comprising the steps of: (a) preparing a mixture of first and second starch portions, a suitable alkali, and water to form a slurry, the first starch portion having a gelatinisation temperature at least about 2° C. lower than the second starch portion, said mixing comprising mixing the first starch portion in a weight ratio of from about 1 to 10 to about 1 to 50 relative the water, and the second starch portion in a weight ratio of from about 1 to 2 to about 1 to 8 relative the water, and the total starch portion in a weight ratio of from about 1 to 2 to about 1 to 4 relative the water; and (b) causing gelatinisation of the starch portion having the lower gelatinisation temperature to thereby form a stable gelatinised carrier for the raw starch portion having the higher gelatinisation temperature, said causing of gelatinisation including maintaining the slurry at a temperature below the gelatinisation temperature of the second starch portion but at least as high as the gelatinisation temperature of the first starch portion.
Claim 17
Dependent Claim
188 words
A carrier type starch based adhesive prepared by the process comprising the steps of: (a) preparing a mixture of first and second starch portions, a suitable alkali, and water to form a slurry, the first starch portion having a gelatinisation temperature at least about 2° C. lower than the second starch portion, said mixing comprising mixing the first starch portion in a weight ratio of from about 1 to 10 to about 1 to 50 relative the water, and the second starch portion in a weight ratio of from about 1 to 2 to about 1 to 8 relative the water, and the total starch portion in a weight ratio of from about 1 to 2 to about 1 to 4 relative the water; and (b) causing gelatinisation of the starch portion having the lower gelatinisation temperature to thereby form a stable gelatinised carrier for the raw starch portion having the higher gelatinisation temperature, said causing of gelatinisation including maintaining the slurry at a temperature below the gelatinisation temperature of the second starch portion but at least as high as the gelatinisation temperature of the first starch portion.
Claim 18
Dependent Claim
35 words
The adhesive of claim 14 wherein the ratio of the first starch portion having the lower gelatinisation temperature to the second starch portion having the higher gelatinisation temperature is from about 1:10 to about 1:4.
Claim 19
Dependent Claim
47 words
The adhesive of claim 14 wherein the first starch portion having the lower gelatinisation temperature is selected from the group consisting of wheat, tapioca and potato, and the second starch portion having the higher gelatinisation temperature is selected from the group consisting of corn, tapioca and wheat.
Claim 20
Dependent Claim
23 words
The adhesive of claim 16 wherein the ratio by weight of total starch portions to water is from about 1:2 to about 1:4.
Claim 21
Dependent Claim
17 words
The adhesive of claim 17 wherein said ratio of total starch portions to water is about 1:3.
Claim 22
Dependent Claim
68 words
The adhesive of claim 17 in which the weight ratio of the first starch portion to the water is from about 1 to 25 to about 1 to 35, the weight ratio of the second starch portion to the water is from about 1 to 3 to about 1 to 5, and the weight ratio of the two starch portions of the water is about 1 to 3.
Claim 23
Dependent Claim
35 words
The adhesive of claim 16 wherein the ratio of the first starch portion having the lower gelatinisation temperature to the second starch portion having the higher gelatinisation temperature is from about 1:10 to about 1:4.
References Cited (Backward Citations)
CA645979A
Cited
US2105052A
Cited
US3015572A
Cited
US3355307A
Cited
AU1414770A
Cited
AU1414970A
Cited
GB1340199A
Cited
US4014727A
Cited
AU8069575A
Cited
US4157318A
Cited
US4272295A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-11-15 | 1986-05-17 | 1986-11-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-11-15 | 1990-05-17 | 1990-11-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-11-15 | 1994-05-17 | 1994-11-16 | $7700.00 | Window Closed / Lapsed |