Process for production of molded articles of acetylene polymer
Assignee: Resonac Holdings Corp
•
Filing: 1981-01-05
•
Granted: 1982-12-07
•
Expires: 2001-01-05
Abstract
Abstract A process for producing a molded article of a high polymer of acetylene, which comprises press-forming a gel-like material or swollen material composed of 5 to 95% by weight of a high polymer of acetylene having a cis content of at least 50% and 95 to 5% by weight of an organic solvent at a temperature of not more than 50° C. and a pressure of 10 to 1,000 kg/cm 2 with or without prior treatment with an electron acceptor or donor substance, and when the treatment with the electron acceptor or donor substance is not performed, calendering or monoaxially stretching the resulting molded article, and if a molded article of an especially high electrical conductivity is desired, treating the molded article further with an electron acceptor or donor substance.
Inventors
- 👤 Yukio Kobayashi
- 👤 Masaaki Kira
- 👤 Kinya Yamaguchi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 15:16
CPC Classifications
H; H01; H01B; H01B1/00; H01B1/06; H01B1/12; H01B1/124; H01B1/125; C; C08; C08J; C08J5/00; C08J5/18; C08K; C08K5/00; C08K5/01; H10; H10K; H10K85/00; H10K85/10; H10K85/141; H10K85/143; C08J2349/00
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
95 words
A process for producing a molded article of a high polymer of acetylene having a high electrical conductivity, which comprises treating a gel-like material or swollen material composed of 5 to 95% by weight of a high polymer of acetylene having a cis content of at least 50% and a fibrous microcrystal structure and 95 to 5% by weight of an organic solvent with an electron acceptor or donor substance, and thereafter press-forming said treated material at a temperature of not more then 50° C. and a pressure of 10 to 1,000 kg/cm 2 .
Claim 2
Dependent Claim
95 words
A process for producing a molded article of a high polymer of acetylene having a high electrical conductivity, which comprises treating a gel-like material or swollen material composed of 5 to 95% by weight of a high polymer of acetylene having a cis content of at least 50% and a fibrous microcrystal structure and 95 to 5% by weight of an organic solvent with an electron acceptor or donor substance, and thereafter press-forming said treated material at a temperature of not more then 50° C. and a pressure of 10 to 1,000 kg/cm 2 .
Claim 3
Dependent Claim
87 words
A process for producing a molded article of a high polymer of acetylene, which comprises press-forming a gel-like material or swollen material composed of 5 to 95% by weight of a high polymer of acetylene having a cis content of at least 50% and a fibrous microcrystal structure and 95 to 5% by weight of an organic solvent at a temperature of not more than 50° C. and a pressure of 10 to 1,000 kg/cm 2 , and thereafter calendering or monoaxially stretching the resulting molded article.
Claim 4
Dependent Claim
87 words
A process for producing a molded article of a high polymer of acetylene, which comprises press-forming a gel-like material or swollen material composed of 5 to 95% by weight of a high polymer of acetylene having a cis content of at least 50% and a fibrous microcrystal structure and 95 to 5% by weight of an organic solvent at a temperature of not more than 50° C. and a pressure of 10 to 1,000 kg/cm 2 , and thereafter calendering or monoaxially stretching the resulting molded article.
Claim 5
Dependent Claim
105 words
A process for producing a molded article of a high polymer of acetylene having a high electrical conductivity, which comprises press-forming a gel-like material or swollen material composed of 5 to 95% by weight of a high polymer of acetylene having a cis content of at least 50% and a fibrous microcrystal structure and 95 to 5% by weight of an organic solvent at a temperature of not more than 50° C. and a pressure of 10 to 1,000 kg/cm 2 , thereafter calendering or monoaxially stretching the resulting molded article and thereafter treating the molded article further with an electron acceptor or donor substance.
Claim 6
Dependent Claim
105 words
A process for producing a molded article of a high polymer of acetylene having a high electrical conductivity, which comprises press-forming a gel-like material or swollen material composed of 5 to 95% by weight of a high polymer of acetylene having a cis content of at least 50% and a fibrous microcrystal structure and 95 to 5% by weight of an organic solvent at a temperature of not more than 50° C. and a pressure of 10 to 1,000 kg/cm 2 , thereafter calendering or monoaxially stretching the resulting molded article and thereafter treating the molded article further with an electron acceptor or donor substance.
Claim 7
Dependent Claim
27 words
The process of claim 2 or 3 wherein the press-formed article is calendered while the organic solvent still remains in the press-formed article of the acetylene polymer.
Claim 8
Dependent Claim
20 words
The process of claim 4 wherein said calendering is carried out at a temperature of not more than 50° C.
Claim 9
Dependent Claim
28 words
The process of claim 2 or 3 wherein the press-formed article is monoaxially stretched while the organic solvent still remains in the press-formed article of the acetylene polymer.
Claim 10
Dependent Claim
20 words
The process of claim 6 wherein the monoaxial stretching is carried out a temperature of not more than 50° C.
Claim 11
Dependent Claim
28 words
The process of claim 6 wherein the monoaxial stretching is carried out in an inert gas atmosphere or in vacuum at a temperature of 100° to 250° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-12-06 | 1986-06-07 | 1986-12-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-12-06 | 1990-06-07 | 1990-12-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-12-06 | 1994-06-07 | 1994-12-07 | $7700.00 | Window Closed / Lapsed |