US4377544A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Manufacture of a textile-like reticular product from thermoplastic film
Assignee: Individual
•
Filing: 1981-07-20
•
Granted: 1983-03-22
•
Expires: 2001-07-20
Abstract
Abstract A two-dimensional integral net having a nap in form of relatively long fibres which are integral with the net and protrude from the edges which surround the apertures of the net. A method of producing this net from a film is by heating selected areas of the film to a molten state and dragging out this molten material into fibres to leave apertures in the film while controlling the fibre-dragging by cooling with an air jet.
Inventors
- 👤 Ole-Bendt Rasmussen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 23:40
CPC Classifications
D; D04; D04H; D04H11/00; B; B26; B26F; B26F1/00; B26F1/26; B29; B29C; B29C59/00; B29C59/02; B29C59/022; B29C59/025; B29D; B29D28/00; D04H1/00; D04H1/40; D04H1/54; D04H1/559; Y; Y10; Y10S; Y10S264/00; Y10S264/47
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
204 words
A process for the direct conversion of thermoplastic film material into open-work sheet material having fibers on one surface thereof, which comprises the steps of maintaining one surface of a length of such film material into face-to-face contact with a surface capable of adhering to said thermoplastic material when the latter is in molten condition, while said surface is heated in a pattern of heated surface regions separated by unheated surface regions to a temperature above the melting point of the film material; continuing the contact between the film surface and the selectively heated surface for a time sufficient to selectively melt the film areas contacting said heated surface regions, whereby said melted film areas adhere to said surface regions, while the remaining film areas remain in generally unmelted and nonadhering condition; then separating said selectively molten film from contact with said selectively heated surface whereby the molten adhering film areas are drawn out from the remainder of the film as fiber-like projections extending from the surrounding unmelted margins and thereby create apertures in said film generally corresponding to said heated surface regions; and directing a flow of cooling air toward the surfaces undergoing each separation to control the drawing of said fiber-like projections.
Claim 2
Dependent Claim
204 words
A process for the direct conversion of thermoplastic film material into open-work sheet material having fibers on one surface thereof, which comprises the steps of maintaining one surface of a length of such film material into face-to-face contact with a surface capable of adhering to said thermoplastic material when the latter is in molten condition, while said surface is heated in a pattern of heated surface regions separated by unheated surface regions to a temperature above the melting point of the film material; continuing the contact between the film surface and the selectively heated surface for a time sufficient to selectively melt the film areas contacting said heated surface regions, whereby said melted film areas adhere to said surface regions, while the remaining film areas remain in generally unmelted and nonadhering condition; then separating said selectively molten film from contact with said selectively heated surface whereby the molten adhering film areas are drawn out from the remainder of the film as fiber-like projections extending from the surrounding unmelted margins and thereby create apertures in said film generally corresponding to said heated surface regions; and directing a flow of cooling air toward the surfaces undergoing each separation to control the drawing of said fiber-like projections.
Claim 3
Dependent Claim
15 words
A process according to claim 1, in which the heated areas form a dotted pattern.
Claim 4
Dependent Claim
62 words
A process according to claim 1, in which the starting material film incorporates an array of higher melting filaments having a higher melting point than the temperature of said heated surface regions and the heated areas in said pattern are each generally linear in shape and extend in the same direction, which is different from the direction of said higher melting filaments.
Claim 5
Dependent Claim
18 words
A process according to claim 1, in which said molten portions are embossed prior to said drawing away.
Claim 6
Dependent Claim
17 words
A process according to claim 4, in which the bosses are formed in a linear criss-crossing pattern.
Claim 7
Dependent Claim
22 words
A process according to claim 1, in which the film material is strongly oriented prior to contact with the selectively heated surface.
Claim 8
Dependent Claim
67 words
The process as in claim 1 wherein said thermoplastic film material comprises at least two layers, the layer on the surface contacting the selectively heated surface being a polymeric material having a melt temperature lower than the temperature of the heated regions of said surface and the next adjacent layer being a polymeric material having a melt temperature higher than the temperature of the heated surface regions.
Claim 9
Dependent Claim
32 words
The process of claim 1 in which the heated surface regions are formed as bosses separated by recesses and the surface of said bosses carry a pattern of generally fine pyramidal sub-embossments.
Claim 10
Dependent Claim
37 words
The process of claim 1 wherein said selectively molten film material is separated from said selectively heated surface by deflection away from the latter over a fixed edge arranged in closely spaced proximity to said heated surface.
Claim 11
Dependent Claim
16 words
The process of claim 1 wherein said selectively heated advancing surface comprises a rotatably driven cylinder.
Claim 12
Dependent Claim
97 words
A process for the direct conversion of thermoplastic film material into open-work sheet material having fibers on one surface thereof, which comprises the steps of selectively heating said film material in a pattern of heated areas separated by unheated areas until the material in said heated areas is at least substantially molten; and drawing out the thus molten material in said heated areas from one surface of the material into filaments with consequential creation of perforations by the drawing out of said filaments therefrom, said filaments having a length greater than any dimension of the corresponding perforation.
Claim 13
Dependent Claim
97 words
A process for the direct conversion of thermoplastic film material into open-work sheet material having fibers on one surface thereof, which comprises the steps of selectively heating said film material in a pattern of heated areas separated by unheated areas until the material in said heated areas is at least substantially molten; and drawing out the thus molten material in said heated areas from one surface of the material into filaments with consequential creation of perforations by the drawing out of said filaments therefrom, said filaments having a length greater than any dimension of the corresponding perforation.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-03-21 | 1986-09-20 | 1987-03-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-03-21 | 1990-09-20 | 1991-03-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-03-21 | 1994-09-20 | 1995-03-22 | $7700.00 | Window Closed / Lapsed |