Dental material comprising dimethyacrylate adducts of glycidyl methacrylate with diesters of bis(hydroxymethyl) tricyclo[5.2.1.02,6 ]decane and dicarboxylic acids
Assignee: Scientific Pharmaceuticals Inc
•
Filing: 1981-05-27
•
Granted: 1983-04-12
•
Expires: 2001-05-27
Abstract
Abstract Dimethacrylates are provided having the following chemical structure: ##STR1## wherein n represents a number of 2 to 8; R 1 and R 2 are the same or different and are hydrogen or groups of the formula: ##STR2## where R 3 is an aliphatic, aromatic or cycloaliphatic group having 1 to 14 carbon atoms. These compounds are useful in dental material which cures to form polymers having high mechanical strength, low water sorption, resistance to staining, good color stability when exposed to short-wave radiation (e.g., sunlight) and good chemical resistance to the oral environment. Also provided are a method for polymerizing these compounds in situ on teeth and a tooth comprising polymers of these compounds.
Inventors
- 👤 Jan A. Orlowski
- 👤 David V. Butler
- 👤 Patrick D. Kidd
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 04:43
CPC Classifications
C; C08; C08F; C08F20/00; C08F20/02; C08F20/10; C08F20/34; C08F20/36; A; A61; A61K; A61K6/00; A61K6/80; A61K6/884; A61K6/887
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
123 words
A dental material comprising polymerizable unsaturated material comprising at least about 10% by weight of a dimethacrylate monomer having the following chemical structure: ##STR16## where n represents a number of 2 to 8; R 1 and R 2 are the same or different and are hydrogen or one or more groups of the formula: ##STR17## where R 3 is an aliphatic group of 1-14 carbon atoms, aromatic group of 6 to 14 carbon atoms or cycloaliphatic group having 3 to 14 carbon atoms and at least one of R 1 and R 2 is ##STR18## the remainder of said polymerizable material being at least 10% by weight of at least one acrylic or methacrylic monomer acceptable for oral application associated with dental treatment.
Claim 2
Dependent Claim
123 words
A dental material comprising polymerizable unsaturated material comprising at least about 10% by weight of a dimethacrylate monomer having the following chemical structure: ##STR16## where n represents a number of 2 to 8; R 1 and R 2 are the same or different and are hydrogen or one or more groups of the formula: ##STR17## where R 3 is an aliphatic group of 1-14 carbon atoms, aromatic group of 6 to 14 carbon atoms or cycloaliphatic group having 3 to 14 carbon atoms and at least one of R 1 and R 2 is ##STR18## the remainder of said polymerizable material being at least 10% by weight of at least one acrylic or methacrylic monomer acceptable for oral application associated with dental treatment.
Claim 3
Dependent Claim
44 words
A dental material according to claim 1, wherein said polymerizable unsaturated material comprises about 20 to about 90% by weight of said dimantacrylate monomer and about 10 to about 80% by weight of at least one other polymethacrylate suitable for use in dental materials.
Claim 4
Dependent Claim
40 words
A dental material according to claim 2, wherein said other polymethacrylate is selected from the group consisting of diethylene glycol dimethacrylate, triethylene glycol dimethacrylate, tetraethylene glycol dimethacrylate, 1,6-hexanediol dimethacrylate, trimethylolpropane trimethacrylate, 2,2-bis[4'(3"-methacroyl-2"-hydroxypropoxy)phenyl]propane, 2,2-bis[4'(2"-methacroylethoxy)phenyl]propane, 2-methacroylethyl-3-methacroyl-2-hydroxypropyl tetrahydrophthalate, 2-methacroylethyl-3-methacroyl-2-hydroxypropyl hexahydrophthalate and 2,2 bis-(4'-methacroylphenyl)propane.
Claim 5
Dependent Claim
39 words
A dental material according to claim 1 comprising two parts capable of curing upon mixing of these parts, one of said parts comprising a peroxide-type polymerization initiator and the other of said parts comprising a tertiary aromatic amine-type activator.
Claim 6
Dependent Claim
26 words
A dental material according to claim 1 comprising a light activated polymerization initiator capable of curing said dental material upon irradiation with ultraviolet or visible light.
Claim 7
Dependent Claim
130 words
A composite dental restorative material comprising glass or ceramic filler and polymerizable material, said polymerizable material comprising at least one first monomer and at least one second monomer, said first monomer being the dimethacrylate monomer according to claim 1, said second monomer being a diluent selected from the group consisting of di- and trimethacrylates having from 10 to 18 carbon atoms, said diluent further being selected from the group consisting of alkylene glycol dimethacrylates, polyalkylene glycol dimethacrylates and alkanetriol trimethacrylates, said at least one first monomer constituting at least 20% by weight of said polymerizable material, said at least one second monomer constituting at least 10% by weight of said polymerizable material, and the weight ratio of said filler to said polymerizable material being from about 1.5:1 to about 8.5:1.
Claim 8
Dependent Claim
50 words
A composite restorative material according to claim 6, wherein said polymerizable material further comprises at least one third monomer selected from the group consisting of 2,2-bis[4'(3"-methacroyl-2"-hydroxypropoxy)phenyl]propane, 2,2-bis(4'(2"-methacroylethoxy)phenyl]propane, 2-methacroylethyl-3-methacroyl-2-hydroxypropyl tetrahydrophthalate, 2-methacroylethyl-3-methacroyl-2-hydroxypropyl hexahydrophthalate and 2,2-bis(4'-methacroylphenyl)propane, the weight ratio of said first monomer to said third monomer being from about 7:9 to 9:7.
Claim 9
Dependent Claim
107 words
A composite restorative material according to claim 7, wherein: (i) said at least one first monomer and said at least one third monomer each constitute from about 35% to about 45% by weight of said polymerizable material, provided that the total amount of said at least one first monomer plus said at least one third monomer constitutes from about 75% to about 85% by weight of said polymerizable material; (ii) said at least one second monomer constitutes from about 15% to about 25% by weight of said polymerizable material; and (iii) said ratio of said filler to said polymerizable material is from about 4:1 to about 6:1.
Claim 10
Dependent Claim
26 words
A composite restorative material according to claim 6 wherein the weight ratio of said filler to said polymerizable material is from about 1.5:1 to about 6.5:1.
Claim 11
Dependent Claim
49 words
A composite restorative material according to claim 9 wherein polymerizable material further comprises at least one third monomer selected from the group consisting of 2,2-bis(4'(3"-methacroyl-2"-hydroxypropoxy)phenyl]propane, 2,2-bis[4'(2"-methacroylethoxy)phenyl]propane, 2-methacroylethyl-3-methacroyl-2-hydroxypropyl tetrahydrophthalate, 2-methacroylethyl-3-methacroyl-2-hydroxypropyl hexahydrophthalate and 2,2-bis(4'-methacroylphenyl)propane, the weight ratio of said first monomer to said third monomer being from about 7:9 to 9:7.
Claim 12
Dependent Claim
49 words
A method for forming a hardened substance on teeth comprising the steps of: (i) applying to said teeth a dental material comprising a polymerizable material, said polymerizable material comprising at least 10% by weight of the dimethacrylate monomer of claim 7; and (ii) polymerizing said polymerizable material in situ.
Claim 13
Independent Claim
110 words
A method for forming a hardened substance on teeth comprising the steps of: (i) applying to said teeth a dental material comprising a polymerizable material, said polymerizable material comprising at least 10% by weight of the compound of the following chemical structure: ##STR19## where n represents a number of 2 to 8; R 1 and R 2 are the same or different and are hydrogen or one or more groups of the formula: ##STR20## where R 3 is an aliphatic group of 1-14 carbon atoms, aromatic group of 6 to 14 carbon atoms or cycloaliphatic group having 3 to 14 carbon atoms; and (ii) polymerizing said polymerizable material in situ.
Claim 14
Independent Claim
110 words
A method for forming a hardened substance on teeth comprising the steps of: (i) applying to said teeth a dental material comprising a polymerizable material, said polymerizable material comprising at least 10% by weight of the compound of the following chemical structure: ##STR19## where n represents a number of 2 to 8; R 1 and R 2 are the same or different and are hydrogen or one or more groups of the formula: ##STR20## where R 3 is an aliphatic group of 1-14 carbon atoms, aromatic group of 6 to 14 carbon atoms or cycloaliphatic group having 3 to 14 carbon atoms; and (ii) polymerizing said polymerizable material in situ.
Claim 15
Dependent Claim
15 words
A method according to claim 12 where R 1 and R 2 are both hydrogen.
References Cited (Backward Citations)
US4172951A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-04-11 | 1986-10-11 | 1987-04-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-04-11 | 1990-10-11 | 1991-04-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-04-11 | 1994-10-11 | 1995-04-12 | $7700.00 | Window Closed / Lapsed |