Raw polymer powder of a modified tetrafluoroethylene polymer having a high bulk density and a good powder flow index and also a process for the manufacture and use thereof
Assignee: Hoechst AG
•
Filing: 1981-06-04
•
Granted: 1983-04-12
•
Expires: 2001-06-04
Abstract
Abstract Novel granular, free-flowing, non-melt-fabricable raw polymer powders of tetrafluoroethylene polymers consisting of 0.004 to 0.075 mole % of polymerized units of a perfluoroalkyl vinyl ether and of tetrafluoroethylene units, are described. These powders have an average particle diameter of 450 to 1,400 μm, a bulk density of at least 570 g/l, a powder flow index of ≦5 seconds/50 g and a grain stability of ≦5.5 seconds/50 g. They are prepared direct by suspension polymerizing TFE in the presence of the perfluoroalkyl ether, while stirring, the calculated concentration of the ether in the gas phase being kept within the range from 0.1 to 1.0% by volume in the period of time until 1.5% by weight of solid polymer have been formed, and the polymerization being carried out under a total pressure of 5 to 11 bars. A further improvement in bulk density, powder flow and grain stability is achieved if the intensity of stirring is kept at a relatively low level in a critical range, beginning at the formation of 1.5 to 3% by weight of solid polymer and extending to the formation of 8 to 12% by weight of solid polymer. The raw polymer powders which can be obtained in this manner are suitable, as such and without further pretreatment, for the production of ram-extruded articles of all types.
Inventors
- 👤 Reinhard A. Sulzbach
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 08:57
CPC Classifications
C; C08; C08F; C08F214/00; C08F214/18; C08F214/26; C08F214/262
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
125 words
In a granular, free-flowing, non-melt-fabricable, non-presintered raw polymer powder of a tetrafluoroethylene polymer, consisting essentially of from 0.004 to 0.075 mole percent polymerized units of a perfluoroalkyl vinyl ether of the formula CF.sub.2 ═CF--O--R.sub.f wherein R f is C 2 F 5 , n-C 3 F 7 , or n-C 4 F 9 , and of polymerized tetrafluoroethylene units having a specific surface of from 0.5 to 4.5 m 2 /g, the improvement residing in the fact that said powder has an average particle diameter d 50 of from 450 to 1400 μm, a bulk density of at least 570 g/l, a powder flow index not higher than 5 seconds per 50 grams, and a grain stability not higher than 5.5 seconds per 50 grams.
Claim 2
Dependent Claim
125 words
In a granular, free-flowing, non-melt-fabricable, non-presintered raw polymer powder of a tetrafluoroethylene polymer, consisting essentially of from 0.004 to 0.075 mole percent polymerized units of a perfluoroalkyl vinyl ether of the formula CF.sub.2 ═CF--O--R.sub.f wherein R f is C 2 F 5 , n-C 3 F 7 , or n-C 4 F 9 , and of polymerized tetrafluoroethylene units having a specific surface of from 0.5 to 4.5 m 2 /g, the improvement residing in the fact that said powder has an average particle diameter d 50 of from 450 to 1400 μm, a bulk density of at least 570 g/l, a powder flow index not higher than 5 seconds per 50 grams, and a grain stability not higher than 5.5 seconds per 50 grams.
Claim 3
Dependent Claim
23 words
A raw polymer powder of a tetrafluoroethylene polymer as claimed in claim 1 having a bulk density of from 620 to 750 g/l.
Claim 4
Dependent Claim
23 words
A raw polymer powder of a tetrafluoroethylene polymer as claimed in claim 1 having a bulk density of from 670 to 880 g/l.
Claim 5
Dependent Claim
23 words
A raw polymer powder of a tetrafluoroethylene polymer as claimed in claim 1 having a bulk density of from 750 to 880 g/l.
Claim 6
Dependent Claim
40 words
A raw polymer powder of a tetrafluoroethylene polymer as claimed in claim 1 having a powder flow index of from 4.0 to 3.0 seconds per 50 grams and a grain stability of from 4.0 to 3.0 seconds per 50 grams.
Claim 7
Dependent Claim
40 words
A raw polymer powder of a tetrafluoroethylene polymer as claimed in claim 1 having a powder flow index of from 4.0 to 2.5 seconds per 50 grams and a grain stability of from 4.0 to 2.5 seconds per 50 grams.
Claim 8
Dependent Claim
40 words
A raw polymer powder of a tetrafluoroethylene polymer as claimed in claim 1 having a powder flow index of from 3.5 to 2.5 seconds per 50 grams and a grain stability of from 3.5 to 2.5 seconds per 50 grams.
Claim 9
Dependent Claim
24 words
A raw polymer powder of a tetrafluoroethylene polymer as claimed in claim 1 having an average particle diameter of from 660 to 1200 μm.
Claim 10
Dependent Claim
21 words
A raw polymer powder of a tetrafluoroethylene polymer as claimed in claim 1 wherein the perfluoroalkyl vinyl ether is perfluoro-n-propyl ether.
Claim 11
Dependent Claim
102 words
In a granular, free-flowing, non-melt-fabricable, non-presintered raw polymer powder of tetrafluoroethylene polymer consisting essentially of from 0.004 to 0.075 mole percent polymerized units of perfluoro-n-propyl vinyl ether and of polymerized tetrafluoroethylene units having a specific surface of from 0.5 to 4.5 m 2 /g, the improvement which resides in the fact that said powder has an average particle diameter d 50 of from 450 to 1400 μm, a bulk density of from 670 to 880 g/l, a powder flow index of from 4.0 to 2.5 seconds per 50 grams, and a grain stability of from 4.0 to 2.5 seconds per 50 grams.
Claim 12
Dependent Claim
102 words
In a granular, free-flowing, non-melt-fabricable, non-presintered raw polymer powder of tetrafluoroethylene polymer consisting essentially of from 0.004 to 0.075 mole percent polymerized units of perfluoro-n-propyl vinyl ether and of polymerized tetrafluoroethylene units having a specific surface of from 0.5 to 4.5 m 2 /g, the improvement which resides in the fact that said powder has an average particle diameter d 50 of from 450 to 1400 μm, a bulk density of from 670 to 880 g/l, a powder flow index of from 4.0 to 2.5 seconds per 50 grams, and a grain stability of from 4.0 to 2.5 seconds per 50 grams.
Claim 13
Dependent Claim
202 words
A process for preparing a granular, free-flowing, non-melt-fabricable raw polymer powder of a tetrafluoroethylene polymer as claimed in claim 1 by suspension polymerizing in an agitated aqueous medium a monomer mixture consisting of a perfluoroalkyl vinyl ether of the formula CF.sub.2 ═CF--O--R.sub.f wherein R f is C 2 F 5 , n-C 3 F 7 or n-C 4 F 9 , and of tetrafluoroethylene in the presence of free radical forming initiators which comprises (a) adjusting the concentration of the gaseous perfluoroalkyl vinyl ether monomer in the gaseous monomer phase together with tetrafluoroethylene in a period of the polymerization until 1.5 weight percent of solid polymer, calculated on the aqueous medium, has been formed, to an arithmetical value of from 0.1 to 1.0 percent by volume, and then continuing the polymerization by supplying tetrafluoroethylene and the perfluoroalkyl vinyl ether in a proportion capable of forming a polymer having a content of from 0.004 to 0.075 mole percent of polymerized units of said perfluoroalkyl vinyl ether and of polymerized tetrafluoroethylene units, (b) conducting the polymerization under a total pressure of from 5 to 11 bars, and (c) separating oversized particles having a particle diameter of >3000 μm from the raw polymer powder formed.
Claim 14
Dependent Claim
29 words
The process as claimed in claim 11 wherein the arithmetical value of the concentration of the gaseous perfluoroalkyl vinyl ether monomer is from 0.1 to 0.45 percent by volume.
Claim 15
Dependent Claim
86 words
The process as claimed in claim 11 wherein in a period of the polymerization process beginning at the formation of from 1.5 to 3 and extending to the formation of from 8 to 12 weight percent of solid polymer calculated on the aqueous medium, a number of revolutions of the agitator is adjusted which corresponds to a specific power input of the agitator of from 0.5 to 1.5 W/l of aqueous medium, said specific power input being measured in the aqueous medium before starting the polymerization.
Claim 16
Dependent Claim
64 words
The process as claimed in claim 13 wherein in a period of the polymerization process from the beginning up to the formation of 1.5 weight percent of solid polymer calculated on the aqueous medium, a number of revolutions of the agitator is adjusted corresponding to a specific power input of the agitator which is enhanced compared with the level as defined in claim 13.
Claim 17
Dependent Claim
31 words
The process as claimed in claim 11 wherein the suspension polymerization is carried out in an aqueous medium containing up to 40 ppm of a fluorinated emulsifier free of telogenic activity.
Claim 18
Dependent Claim
43 words
In the method of producing shaped articles of tetrafluoroethylene polymers by ram extruding free-flowing tetrafluoroethylene polymer powders, the improvement which comprises obtaining shaped articles of high mechanical strength by ram extruding shaped articles from free-flowing tetrafluoroethylene polymer powders as claimed in claim 1.
Claim 19
Dependent Claim
191 words
A raw, non-presintered polymer powder of a tetrafluoroethylene polymer as claimed in claim 1 which has been obtained by suspension polymerization in an agitated aqueous medium from a monomer mixture consisting essentially of said perfluoroalkyl vinyl ether and tetrafluoroethylene in the presence of free radical-forming initiators wherein, in addition to the control over average particle diameter d 50 obtained by separation of over-sized particles having a particle diameter of >3000 μm, improved control over said d 50 and the bulk density has been obtained by (a) maintaining the arithmetical concentration of said perfluoroalkyl vinyl ether in said monomer mixture within the range of arithmetical values of from 0.1 to 1.0 percent by volume, in a period of the polymerization until 1.5 weight percent of solid polymer, calculated with reference to the aqueous medium, has been formed and then continuing the polymerization by supplying tetrafluoroethylene and the perfluoroalkyl vinyl ether in a proportion capable of forming a polytetrafluoroethylene polymer having a content of from 0.004 to 0.075 mole percent of polymerized units of said perfluoroalkyl vinyl ether, and (b) conducting the polymerization under a total pressure of from 5 to 11 bars.
Claim 20
Dependent Claim
38 words
A raw, non-presintered polymer powder of a tetrafluoroethylene polymer as claimed in claim 17 wherein said powder has a specific surface area within the range of 0.5 to 4.5 m 2 /g, as determined by the BET method.
References Cited (Backward Citations)
US2400091A
Cited
US3152201A
Cited
US3819594A
Cited
US3911072A
Cited
US3855191A
Cited
US4078134A
Cited
US4078135A
Cited
US4216265A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-04-11 | 1986-10-11 | 1987-04-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-04-11 | 1990-10-11 | 1991-04-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-04-11 | 1994-10-11 | 1995-04-12 | $7700.00 | Window Closed / Lapsed |