Silicon purification
Assignee: Atlantic Richfield Co
•
Filing: 1982-01-27
•
Granted: 1983-06-14
•
Expires: 2002-01-27
Abstract
Abstract A method for refining silicon to produce a high purity silicon product for re-use in industries which demand high purity silicon starting material, comprising vacuum refining said silicon to remove gaseous CO and SiO followed by mixing with an effective fluxing material of at least one fluoride of alkali metals and/or alkaline earth metals, heating the mixture at a temperature and time sufficient to produce a molten silicon phase and a slag phase, and separating the slag from the silicon for recovery of the silicon for re-use.
Inventors
- 👤 Vijay K. Kapur
- 👤 Uppala V. Choudary
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 20:49
CPC Classifications
C; C01; C01B; C01B33/00; C01B33/02; C01B33/037
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
100 words
A method for refining silicon particles which are contaminated with carbon and other impurities to produce high purity silicon comprising vacuum refining the silicon particles in an inert atmosphere and at an elevated temperature to form gaseous CO and SiO, thereafter mixing with said silicon an effective fluxing amount of at least one fluoride of a metal selected from the group consisting of alkali metals and alkaline earth metals, heating said mixture at an elevated temperature and for a time sufficient to produce molten silicon and slag as separate phases, separating said slag from said silicon, and recovering said silicon.
Claim 2
Independent Claim
100 words
A method for refining silicon particles which are contaminated with carbon and other impurities to produce high purity silicon comprising vacuum refining the silicon particles in an inert atmosphere and at an elevated temperature to form gaseous CO and SiO, thereafter mixing with said silicon an effective fluxing amount of at least one fluoride of a metal selected from the group consisting of alkali metals and alkaline earth metals, heating said mixture at an elevated temperature and for a time sufficient to produce molten silicon and slag as separate phases, separating said slag from said silicon, and recovering said silicon.
Claim 3
Dependent Claim
29 words
The method according to claim 1 wherein the silicon particles are heated to at least 1500° C. for said vacuum refining and said vacuum is at least 10 torr.
Claim 4
Dependent Claim
38 words
The method according to claim 1 wherein from about 2 to about 5 weight percent of flux material, based on the weight of the silicon to be refined, is mixed with the silicon that is to be refined.
Claim 5
Dependent Claim
14 words
The method according to claim 1 wherein said flux material is essentially sodium fluoride.
Claim 6
Dependent Claim
21 words
The method according to claim 1 wherein said flux material is essentially a mixture of fluorides of calcium, magnesium and barium.
Claim 7
Dependent Claim
31 words
The method according to claim 1 wherein said mixture is heated to at least about 1410° C. for a time sufficient to form a significant amount of said molten silicon phase.
Claim 8
Dependent Claim
27 words
The method according to claim 1 wherein said slag is separated from said molten silicon by skimming said slag off the top of said molten silicon phase.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-06-13 | 1986-12-13 | 1987-06-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-06-13 | 1990-12-13 | 1991-06-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-06-13 | 1994-12-13 | 1995-06-14 | $7700.00 | Window Closed / Lapsed |