Process for preparing rubbery polymer reinforced styrenic resins
Assignee: Labofina SA
•
Filing: 1981-02-26
•
Granted: 1983-07-12
•
Expires: 2001-02-26
Abstract
Abstract A continuous mass polymerization process for preparing rubber reinforced styrenic copolymers comprising forming a solution in an inert solvent of a styrenic polymer matrix and a monomer material capable of polymerizing to form a cross-linked rubbery polmyer, continuously charging the solution into a polymerization reactor and subjecting the solution to mass polymerization conditions whereby there is formed in situ a cross-linked rubbery polymer dispersed in the styrenic polymer matrix, continuously withdrawing the reaction mixture from the polymerization reactor and recovering the resulting rubber reinforced styrenic copolymer.
Inventors
- 👤 William J. I. Bracke
- 👤 Emmanuel Lanza
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 20:25
CPC Classifications
C; C08; C08F; C08F257/00; C08F257/02; C08F265/00; C08F265/08
Claims Analysis
Total Claims: 46
Claim 1
Independent Claim
185 words
A process for continuous preparation of a rubbery polymer material reinforced styrenic resin comprising the steps of: a. adding a monomer material selected from the group consisting of alkyl esters of acrylic acid, alkyl esters of methacrylic acid and mixtures thereof, together with a polyfunctional cross-linking agent to a first solution of a copolymeric matrix of a styrenic compound and an acrylonitrile compound in an inert solvent, whereby there is formed a second solution of monomer material, polyfunctional cross-linking agent and said copolymeric matrix in said inert solvent; b. continuously charging said second solution into a polymerization zone and subjecting said second solution in said polymerization zone to mass polymerization conditions to polymerize said monomer material whereby there is formed in situ a cross-linked rubbery material dispersed in said copolymeric matrix; c. continuously withdrawing the reaction mixture from said polymerization zone and continuously charging the withdrawn mixture into a devolatilization zone to remove the inert solvent and any residual monomer material, and d. recovering a rubbery polymer material reinforced styrenic resin wherein the rubbery material formed in situ is highly dispersed in the copolymer matrix.
Claim 2
Dependent Claim
185 words
A process for continuous preparation of a rubbery polymer material reinforced styrenic resin comprising the steps of: a. adding a monomer material selected from the group consisting of alkyl esters of acrylic acid, alkyl esters of methacrylic acid and mixtures thereof, together with a polyfunctional cross-linking agent to a first solution of a copolymeric matrix of a styrenic compound and an acrylonitrile compound in an inert solvent, whereby there is formed a second solution of monomer material, polyfunctional cross-linking agent and said copolymeric matrix in said inert solvent; b. continuously charging said second solution into a polymerization zone and subjecting said second solution in said polymerization zone to mass polymerization conditions to polymerize said monomer material whereby there is formed in situ a cross-linked rubbery material dispersed in said copolymeric matrix; c. continuously withdrawing the reaction mixture from said polymerization zone and continuously charging the withdrawn mixture into a devolatilization zone to remove the inert solvent and any residual monomer material, and d. recovering a rubbery polymer material reinforced styrenic resin wherein the rubbery material formed in situ is highly dispersed in the copolymer matrix.
Claim 3
Dependent Claim
34 words
A process according to claim 1, wherein the styrenic polymer matrix comprises a copolymer of from about 10 to about 90 weight percent styrenic compound and about 90 to about 10 weight percent acrylonitrile.
Claim 4
Dependent Claim
22 words
A process according to claim 2, wherein the weight ratio of styrenic compound to acrylonitrile comprises between about 4:1 and about 1:1.
Claim 5
Dependent Claim
24 words
A process according to claim 2, wherein the copolymeric matrix comprises a minor amount of a rubbery polymer not exceeding about 8% by weight.
Claim 6
Dependent Claim
28 words
A process according to claim 1, wherein the solution of copolymeric matrix in the inert solvent comprises from about 10 to about 70 weight % of copolymeric matrix.
Claim 7
Dependent Claim
21 words
A process according to claim 5, wherein the solution contains from about 20 to about 50 weight % of copolymeric matrix.
Claim 8
Dependent Claim
26 words
A process according to claim 1, wherein the monomer material is a saturated alkyl ester wherein the alkyl group contains from 1 to 14 carbon atoms.
Claim 9
Dependent Claim
23 words
A process according to claim 7, wherein the monomer material produces a rubbery material having a glass-transition temperature lower than about 0° C.
Claim 10
Dependent Claim
30 words
A process according to claim 7, wherein the amount of monomer material comprises between about 15 and 50%, based on the total weight of the copolymeric matrix and monomer material.
Claim 11
Dependent Claim
35 words
A process according to claim 1, wherein the cross-linking agent is selected from the group consisting of alkenyl esters of lower aliphatic carboxylic acids, acrylates of polyol compounds, methacrylates of polyol compounds and mixtures thereof.
Claim 12
Dependent Claim
27 words
A process according to claim 10, wherein the amount of cross-linking agent comprises between about 0.025% and about 5%, based on the weight of the monomer material.
Claim 13
Dependent Claim
25 words
A process according to claim 1, wherein the inert solvent is a saturated solvent having a boiling point between about 120° and about 175° C.
Claim 14
Dependent Claim
21 words
A process according to claim 12, wherein the saturated solvent has a boiling point between about 130° and about 150° C.
Claim 15
Dependent Claim
12 words
A process according to claim 12, wherein the solvent is an alkylbenzene.
Claim 16
Dependent Claim
11 words
A process according to claim 14, wherein the solvent is ethylbenzene.
Claim 17
Dependent Claim
28 words
A process according to claim 1, wherein the mass polymerization is a thermal polymerization and is carried out at a temperature between about 130° and about 170° C.
Claim 18
Dependent Claim
32 words
A process according to claim 1, wherein the mass polymerization is carried out in the presence of a free radical generating catalyst at a temperature between about 120° and about 140° C.
Claim 19
Dependent Claim
118 words
A continuous mass polymerization process for preparing rubbery polymer reinforced styrenic copolymer resins comprising the steps of: a. forming a solution in an inert solvent comprising a styrenic polymer matrix and a monomer material capable of polymerizing to form a cross-linked rubbery polymer material; b. continuously charging said solution from step a. into a polymerization reactor and subjecting said solution to mass polymerization conditions to mass polymerize said monomer material whereby there is formed in situ a cross-linked rubbery polymer material dispersed in the styrenic polymer matrix; c. continuously withdrawing the reaction mixture from step b. from said polymerization reactor; and d. recovering a rubbery polymer reinforced styrenic copolymer resin from the withdrawn reaction mixture from step c.
Claim 20
Dependent Claim
118 words
A continuous mass polymerization process for preparing rubbery polymer reinforced styrenic copolymer resins comprising the steps of: a. forming a solution in an inert solvent comprising a styrenic polymer matrix and a monomer material capable of polymerizing to form a cross-linked rubbery polymer material; b. continuously charging said solution from step a. into a polymerization reactor and subjecting said solution to mass polymerization conditions to mass polymerize said monomer material whereby there is formed in situ a cross-linked rubbery polymer material dispersed in the styrenic polymer matrix; c. continuously withdrawing the reaction mixture from step b. from said polymerization reactor; and d. recovering a rubbery polymer reinforced styrenic copolymer resin from the withdrawn reaction mixture from step c.
Claim 21
Dependent Claim
43 words
A process according to claim 18 wherein said styrenic polymer matrix is selected from the group consisting of styrene homopolymers, copolymers of styrene and acrylonitrile; copolymers of styrene, acrylonitrile and butadiene; copolymers of styrene and butadiene; and copolymers of styrene and methyl methacrylate.
Claim 22
Dependent Claim
24 words
A process according to claim 18 wherein said styrenic polymer matrix is a copolymer of styrene and at least one other ethylenically unsaturated monomer.
Claim 23
Dependent Claim
13 words
A process according to claim 20 wherein said copolymer is a styrene-acrylonitrile copolymer.
Claim 24
Dependent Claim
26 words
A process according to claim 18 wherein said monomer material comprises at least one monomer selected from the group consisting of acrylate monomers and conjugated diolefins.
Claim 25
Dependent Claim
32 words
A process according to claim 22 wherein said monomer material comprises an alkyl ester of acrylic acid or methacrylic acid and an effective polyfunctional cross-linking amount of at least one cross-linking agent.
Claim 26
Dependent Claim
22 words
A process according to claim 23 wherein said alkyl ester is selected from the group consisting of n-butyl acrylate and 2-ethylhexyl acrylate.
Claim 27
Dependent Claim
14 words
A process according to claim 22 wherein said monomer material comprises a conjugated diolefin.
Claim 28
Dependent Claim
12 words
A process according to claim 25 wherein said conjugated diolefin is 1,3-butadiene.
Claim 29
Dependent Claim
34 words
A process according to claim 18 wherein said recovery step comprises treating the mixture withdrawn from the polymerization reactor to remove the inert solvent and any residual monomer material which may be present therein.
Claim 30
Dependent Claim
25 words
A process according to claim 27 wherein said mixture is devolatilized in a vacuum chamber to remove the inert solvent and any residual monomer material.
Claim 31
Dependent Claim
24 words
A process according to claim 27 wherein a film of said mixture is heated to remove the inert solvent and any residual monomer material.
Claim 32
Dependent Claim
15 words
A process according to claim 18 wherein said inert solvent is a saturated alkylaromatic compound.
Claim 33
Dependent Claim
13 words
A process according to claim 30 wherein said saturated alkylaromatic compound is ethylbenzene.
Claim 34
Dependent Claim
56 words
A process according to claim 18 wherein the initial solution is formed by mass polymerization of a mixture of styrene and acrylonitrile in an inert solvent to produce a styrene-acrylonitrile copolymer matrix in solution in said solvent, said matrix being substantially free of reactive sites; and thereafter adding said monomer material to the copolymer matrix solution.
Claim 35
Dependent Claim
27 words
A process according to claim 18 wherein said mass polymerization is effected at a temperature lying in the range from about 100° C. to about 170° C.
Claim 36
Dependent Claim
31 words
A process according to claim 18 wherein said mass polymerization is effected in the substantial absence of molecular oxygen and in the presence of at least one free radical generating catalyst.
Claim 37
Dependent Claim
27 words
A process according to claim 34 wherein said mass polymerization is effected at a temperature lying in the range between about 100° C. and about 140° C.
Claim 38
Dependent Claim
14 words
A process according to claim 18 wherein said mass polymerization is a thermal polymerization.
Claim 39
Dependent Claim
27 words
A process according to claim 36 wherein said mass polymerization is effected at a temperature lying in the range from about 120° C. to about 170° C.
Claim 40
Dependent Claim
17 words
A process according to claim 18 wherein said rubbery polymer reinforced styrenic copolymer resin is substantially gel-free.
Claim 41
Dependent Claim
39 words
A process according to claim 18 wherein said monomer material is selected from the group consisting of acrylic acid esters, mixtures of acrylic acid esters, and mixtures of a methacrylic acid ester with at least one acrylic acid ester.
Claim 42
Dependent Claim
23 words
A process according to claim 39 wherein said monomer material further comprises an effective cross-linking amount of at least one polyfunctional cross-linking agent.
Claim 43
Dependent Claim
17 words
A process according to claim 18 wherein said styrenic polymer matrix is substantially free of reactive sites.
Claim 44
Dependent Claim
22 words
A process according to claim 18 wherein said monomer material is substantially uniformly dispersed throughout said styrenic polymer matrix in said solution.
Claim 45
Dependent Claim
97 words
A continuous mass process for preparing rubbery polymer reinforced ASA styrenic resins comprising the steps of: a. forming a solution in an inert solvent of a styrene-acrylonitrile copolymer matrix together with an acrylate monomer and a polyfunctional cross-linking agent; b. continuously charging said solution into a polymerization zone and subjecting it to mass polymerization whereby there is formed in situ a cross-linked rubbery material dispersed in the styrene-acrylonitrile matrix, c. continuously withdrawing the reaction mixture from the polymerization zone and charging it into a devolatilization zone; and d. recovering the resulting rubbery polymer reinforced ASA styrenic resin.
Claim 46
Dependent Claim
97 words
A continuous mass process for preparing rubbery polymer reinforced ASA styrenic resins comprising the steps of: a. forming a solution in an inert solvent of a styrene-acrylonitrile copolymer matrix together with an acrylate monomer and a polyfunctional cross-linking agent; b. continuously charging said solution into a polymerization zone and subjecting it to mass polymerization whereby there is formed in situ a cross-linked rubbery material dispersed in the styrene-acrylonitrile matrix, c. continuously withdrawing the reaction mixture from the polymerization zone and charging it into a devolatilization zone; and d. recovering the resulting rubbery polymer reinforced ASA styrenic resin.
References Cited (Backward Citations)
US3047533A
Cited
US2994683A
Cited
US3971835A
Cited
US3793402A
Cited
US3845164A
Cited
US3903200A
Cited
US4277574A
Cited
US4283506A
Cited
US4287318A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-07-11 | 1987-01-10 | 1987-07-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-07-11 | 1991-01-10 | 1991-07-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-07-11 | 1995-01-10 | 1995-07-12 | $7700.00 | Window Closed / Lapsed |