Method for the evaluation of solderability
Assignee: RCA Corp
•
Filing: 1981-12-04
•
Granted: 1983-10-11
•
Expires: 2001-12-04
Abstract
Abstract A test procedure is disclosed for evaluating the solderability properties of molten solder. In the method of this invention, a testpiece is provided which has a transparent support with a film of metal such as copper deposited on one surface of the transparent support. The surface having the metal film is immersed in the molten solder and the time required for alloying to occur and be observed through the transparent support is measured to determine rate of alloying and, thereby, the solderability properties of the molten solder under evaluation.
Inventors
- 👤 Soitiro Tosima
- 👤 Shigeo Harada
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 18:10
CPC Classifications
B; B23; B23K; B23K31/00; B23K31/12; H; H05; H05K; H05K3/00; H05K3/30; H05K3/32; H05K3/34; H05K3/3465; H05K3/3468; G; G01; G01N; G01N13/00; G01N13/02; G01N2013/0225; H05K1/00; H05K1/02; H05K1/0266; H05K1/0269; H05K2201/00; H05K2201/01; H05K2201/0104; H05K2201/0108; H05K2201/10; H05K2201/10007; H05K2201/10204; H05K2203/00; H05K2203/16; H05K2203/161; H05K2203/162
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
188 words
The method for evaluating the solderability properties of a molten solder, said method comprising the steps of (a) providing a test piece having a transparent support with first and second surfaces, and having a metal film of a predetermined thickness formed on the first surface, said metal of the metal film being a metal which will alloy with the molten solder, said second surface be positioned relative to the first surface so that the area of the metal film on the first surface can be observed through the transparent support from the second surface; (b) placing the metal film in contact with the molten solder; (c) maintaining the metal film in contact with the molten solder for a measured length of time, at least sufficiently long enough for noticeable change due to alloying of the molten solder with the metal of the metal film to occur and be observed through the transparent support from second surface; whereby, a rate of alloying of the molten solder with the predetermined thickness of the metal film is obtained which rate is directly related to the solderability properties of the molten solder.
Claim 2
Independent Claim
188 words
The method for evaluating the solderability properties of a molten solder, said method comprising the steps of (a) providing a test piece having a transparent support with first and second surfaces, and having a metal film of a predetermined thickness formed on the first surface, said metal of the metal film being a metal which will alloy with the molten solder, said second surface be positioned relative to the first surface so that the area of the metal film on the first surface can be observed through the transparent support from the second surface; (b) placing the metal film in contact with the molten solder; (c) maintaining the metal film in contact with the molten solder for a measured length of time, at least sufficiently long enough for noticeable change due to alloying of the molten solder with the metal of the metal film to occur and be observed through the transparent support from second surface; whereby, a rate of alloying of the molten solder with the predetermined thickness of the metal film is obtained which rate is directly related to the solderability properties of the molten solder.
Claim 3
Dependent Claim
29 words
The method according to claim 1 wherein the metal film has a first color as formed on the support and a second color when alloyed with the molten solder.
Claim 4
Dependent Claim
11 words
The method according to claim 2 wherein the metal is copper.
Claim 5
Dependent Claim
11 words
The method according to claim 2 wherein the metal is gold.
Claim 6
Dependent Claim
44 words
The method according to claim 2 wherein the time is measured from the time the metal film enters the molten solder until a color change due to alloying is observed at the first surface as viewed through the transparent support from the second surface.
Claim 7
Dependent Claim
39 words
The method according to claim 1 wherein the time is measured from the time the metal film enters the molten solder until the predetermined thickness of metal film on the support alloys with and dissolves into the molten solder.
Claim 8
Dependent Claim
19 words
The method according to claim 1 wherein the transparent support is about 0.20 to about 0.30 mm. in thickness.
Claim 9
Dependent Claim
15 words
The method according to claim 7 wherein the transparent support is made of borosilicate glass.
Claim 10
Dependent Claim
18 words
The method according to claim 1 wherein the film of metal is applied in a uniform thickness layer.
Claim 11
Dependent Claim
14 words
The method according to claim 9 wherein the predetermined thickness is about 5 μm.
Claim 12
Dependent Claim
19 words
The method according to claim 1 wherein the metal film is applied in a film of predetermined increasing thickness.
Claim 13
Dependent Claim
58 words
The method according to claim 11 wherein the testpiece with the film of predetermined increasing thickness is immersed in the molten solder for a fixed period of time and the amount of alloying observable through the transparent support on the second surface relative to the thickness of the metal film is measured to determine the rate of alloying.
Claim 14
Dependent Claim
16 words
The method according to claim 1 wherein the molten solder is circulated past the metal film.
Claim 15
Dependent Claim
24 words
The method according to claim 13 wherein the molten solder is circulated past the film of metal at a rate of about 11 cm./sec.
Claim 16
Dependent Claim
19 words
The method according to claim 1 wherein the molten solder is maintained at a temperature of about 260° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-10-10 | 1987-04-11 | 1987-10-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-10-10 | 1991-04-11 | 1991-10-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-10-10 | 1995-04-11 | 1995-10-11 | $7700.00 | Window Closed / Lapsed |