Process for manufacturing ornamental parts and ion plating apparatus to be used therefor
Assignee: Citizen Watch Co Ltd
•
Filing: 1983-02-28
•
Granted: 1983-11-15
•
Expires: 2003-02-28
Abstract
Abstract Within a vacuum chamber filled with a low-pressure gas atmosphere including nitrogen, titanium is vaporized to coat a titanium nitride film on a surface of an ornamental part such as a watch case by a reactive ion plating method, and a gold film is coated thereon to modulate the color. In this process, the titanium vapor is supplied from an electron beam melting vapor source whereas the gold vapor is supplied from a sputtering vapor source, and the periods both vapors are supplied partly overlap. This process improves the reproducibility of color modulation by coating the gold film and enhances the affinity at the interface between the titanium nitride film and the gold film.
Inventors
- 👤 Yasutomo Sasanuma
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 15:59
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/06; C23C14/0641; C23C14/02; C23C14/024; C23C14/027; C23C14/14; C23C14/16; C23C14/22; G; G04; G04B; G04B37/00; G04B37/22
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
187 words
A process for manufacturing an ornamental part comprising: providing the ornamental part as a work to be treated, an electron beam melting vapor source for evaporating a titanium based metal, and one or more sputtering vapor sources for supplying at least a gold based metal vapor, within a vacuum chamber filled with a low-pressure gas atmosphere including a nitride gas; establishing an electric field between said ornamental part and said electron beam melting vapor source to produce a plasma glow discharge therebetween; evaporating and ionizing said titanium based metal in the plasma glow discharge to coat a film mainly composed of titanium nitride on a surface of said ornamental part; at the final stage of this process, applying a negative voltage to one or more targets of said one or more sputtering vapor sources and at the same time, supplying a gold based metal vapor to form a transition layer including both titanium nitride and gold; and while continuing supplying the gold based metal vapor, stopping gradually the evaporation of said titanium based metal to coat a film of the gold based metal as a topcoat layer.
Claim 2
Dependent Claim
187 words
A process for manufacturing an ornamental part comprising: providing the ornamental part as a work to be treated, an electron beam melting vapor source for evaporating a titanium based metal, and one or more sputtering vapor sources for supplying at least a gold based metal vapor, within a vacuum chamber filled with a low-pressure gas atmosphere including a nitride gas; establishing an electric field between said ornamental part and said electron beam melting vapor source to produce a plasma glow discharge therebetween; evaporating and ionizing said titanium based metal in the plasma glow discharge to coat a film mainly composed of titanium nitride on a surface of said ornamental part; at the final stage of this process, applying a negative voltage to one or more targets of said one or more sputtering vapor sources and at the same time, supplying a gold based metal vapor to form a transition layer including both titanium nitride and gold; and while continuing supplying the gold based metal vapor, stopping gradually the evaporation of said titanium based metal to coat a film of the gold based metal as a topcoat layer.
Claim 3
Dependent Claim
14 words
A manufacturing process of claim 1, wherein said titanium based metal comprises pure titanium.
Claim 4
Dependent Claim
19 words
A manufacturing process of claim 1, wherein said titanium based metal comprises a titanium alloy with zirconium and hafnium.
Claim 5
Dependent Claim
18 words
A manufacturing process of claim 1, wherein said sputtering target comprises a gold alloy with palladium and copper.
Claim 6
Dependent Claim
15 words
A manufacturing process of claim 1, wherein one of said plurality of targets comprises gold.
Claim 7
Dependent Claim
20 words
A manufacturing process of claim 1, wherein said low-pressure gas including a nitride gas is composed of nitride and argon.
Claim 8
Dependent Claim
49 words
A manufacturing process of claim 1, wherein said film mainly composed of titanium nitride is from 1 to 10 microns in thickness, the film containing gold is from 0.1 to 1 micron in thickness, and the transient layer is corresponding to 10 to 90% of the latter in thickness.
Claim 9
Dependent Claim
20 words
A manufacturing process of claim 1, wherein said ornamental part includes a watch case, glass frame, lighter, and pen cap.
Claim 10
Dependent Claim
102 words
An ion plating apparatus comprising: a vacuum chamber having a gas inlet pipe and an evacuation duct; a rotary work holder arranged in said vacuum chamber for supporting a work to be treated; an electron beam melting vapor source for supplying a titanium metal vapor; one or more sputtering vapor sources for supplying at least a gold based metal vapor, said one or more sputtering vapor sources having each a sputtering target. means for establishing an electric field between said work to be treated and said electron beam melting vapor source; and means for applying a negative voltage to said sputtering target.
Claim 11
Dependent Claim
102 words
An ion plating apparatus comprising: a vacuum chamber having a gas inlet pipe and an evacuation duct; a rotary work holder arranged in said vacuum chamber for supporting a work to be treated; an electron beam melting vapor source for supplying a titanium metal vapor; one or more sputtering vapor sources for supplying at least a gold based metal vapor, said one or more sputtering vapor sources having each a sputtering target. means for establishing an electric field between said work to be treated and said electron beam melting vapor source; and means for applying a negative voltage to said sputtering target.
Claim 12
Dependent Claim
17 words
An apparatus of claim 9, wherein said electron beam melting vapor source is of a filament type.
Claim 13
Dependent Claim
18 words
An apparatus of claim 9, wherein said electron beam melting vapor source is of a hollow cathode type.
Claim 14
Dependent Claim
17 words
An apparatus of claim 9, wherein said sputtering vapor source or sources are of a magnetron type.
Claim 15
Dependent Claim
14 words
An apparatus of claim 9, wherein one of said plurality of targets comprises gold.
Claim 16
Dependent Claim
16 words
An apparatus of claim 9, wherein said rotary work holder has a vertically pivoted rotation axis.
Claim 17
Dependent Claim
16 words
An apparatus of claim 9, wherein said rotary work holder has a horizontally pivoted rotation axis.
References Cited (Backward Citations)
US4226082A
Cited
US4254159A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-11-14 | 1987-05-16 | 1987-11-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-11-14 | 1991-05-16 | 1991-11-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-11-14 | 1995-05-16 | 1995-11-15 | $7700.00 | Window Closed / Lapsed |