Nuclear waste encapsulation in borosilicate glass by chemical polymerization
Assignee: Westinghouse Electric Corp
•
Filing: 1980-08-11
•
Granted: 1983-12-27
•
Expires: 2000-08-11
Abstract
Abstract Disclosed is a process for containing a solution of nuclear waste, where the nuclear waste is at least 10% sodium or nitrate. A composition is prepared in an alcohol of about 1 to about 99% of a silicon alkoxide and about 1 to about 99% of a boron alkoxide. The pH of the nuclear waste solution is adjusted to about 4 to about 6 and the pH of the composition is adjusted to match. The composition is dried to about 50 to about 75% of its original volume and is mixed with up to about 30% of the solution of nuclear waste, thereby forming a gel. The mixture is dried and heated at up to about 500 DEG C. Finally, it is consolidated either by warm pressing at about 400 DEG to about 800 DEG C. at about 40,000 to about 100,000 psi, or by melting at about 700 DEG to about 1150 DEG C.
Inventors
- 👤 Ronald W. Chickering
- 👤 Bulent E. Yoldas
- 👤 Bruce H. Neuman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 12:28
CPC Classifications
C; C03; C03C; C03C1/00; C03C1/002; C03C1/006; G; G21; G21F; G21F9/00; G21F9/04; G21F9/06; G21F9/16; G21F9/162; G21F9/28; G21F9/30; G21F9/301; G21F9/302; G21F9/305; Y; Y10; Y10S; Y10S65/00; Y10S65/901
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
221 words
A method of encapsulating an aqueous solution of nuclear waste, comprising: (A) adjusting the pH of said solution of nuclear waste to about 4 to about 6; (B) preparing a composition in an alcohol which consists essentially of: (1) about 1 to about 99% by weight of a silicon compound having the general formula Si(OR) 4 where each R is independently selected from alkyl to C 6 ; and (2) about 1 to about 99% by weight of a boron compound having the general formula B(OR) 3 where each R is independently selected from alkyl to C 6 , said composition being partially hydrolyzed; (C) adjusting the pH of said composition to about the pH of said solution of nuclear waste; (D) drying said composition to about 50 to about 75% of its original volume; (E) mixing together up to about 30% by weight of said solution of nuclear waste with said composition, based on total weight, to form a gel; (F) drying the mixture at a temperature between room temperature and the boiling point of said alcohol; (G) heating said mixture at up to 500° C.; (H) consolidating said mixture by (1) warm pressing at about 400 to about 800° C. at about 40,000 to about 100,000 psi; or (2) melting said mixture at about 700° to about 1150° C.
Claim 2
Independent Claim
221 words
A method of encapsulating an aqueous solution of nuclear waste, comprising: (A) adjusting the pH of said solution of nuclear waste to about 4 to about 6; (B) preparing a composition in an alcohol which consists essentially of: (1) about 1 to about 99% by weight of a silicon compound having the general formula Si(OR) 4 where each R is independently selected from alkyl to C 6 ; and (2) about 1 to about 99% by weight of a boron compound having the general formula B(OR) 3 where each R is independently selected from alkyl to C 6 , said composition being partially hydrolyzed; (C) adjusting the pH of said composition to about the pH of said solution of nuclear waste; (D) drying said composition to about 50 to about 75% of its original volume; (E) mixing together up to about 30% by weight of said solution of nuclear waste with said composition, based on total weight, to form a gel; (F) drying the mixture at a temperature between room temperature and the boiling point of said alcohol; (G) heating said mixture at up to 500° C.; (H) consolidating said mixture by (1) warm pressing at about 400 to about 800° C. at about 40,000 to about 100,000 psi; or (2) melting said mixture at about 700° to about 1150° C.
Claim 3
Dependent Claim
14 words
A method according to claim 1 wherein R is C 2 H 5 .
Claim 4
Dependent Claim
21 words
A method according to claim 1 wherein said composition is aged before said solution of nuclear waste is mixed with it.
Claim 5
Dependent Claim
14 words
A method according to claim 1 wherein said gel is aged prior to drying.
Claim 6
Dependent Claim
38 words
A method according to claim 1 wherein the amount of said silicon compound in said composition is about 65 to about 95% and the amount of said boron compound in said composition is about 5 to about 35%.
Claim 7
Dependent Claim
24 words
A method according to claim 1 wherein said nuclear waste is an aqueous solution having a solids content of about 5 to about 50%.
Claim 8
Dependent Claim
24 words
A method according to claim 1 wherein said composition is partially hydrolyzed after said silicon compound and said boron compound have been mixed together.
Claim 9
Dependent Claim
21 words
A method according to claim 1 wherein the alcohol in said composition is about 30 to about 65% of said composition.
Claim 10
Dependent Claim
20 words
A method according to claim 1 wherein said alcohol in said composition is ROH where R has been defined above.
Claim 11
Dependent Claim
14 words
A method according to claim 1 wherein said pH is adjusted with acetic acid.
Claim 12
Dependent Claim
13 words
A glass containing nuclear waste prepared according to the method of claim 1.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-12-26 | 1987-06-27 | 1987-12-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-12-26 | 1991-06-27 | 1991-12-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-12-26 | 1995-06-27 | 1995-12-27 | $7700.00 | Window Closed / Lapsed |