Method of producing a metallic thin film magnetic disk
Assignee: International Business Machines Corp
•
Filing: 1982-02-26
•
Granted: 1984-01-17
•
Expires: 2002-02-26
Abstract
Abstract For a metallic thin film magnetic disk, a chromium undercoat and a magnetic layer, in particular of an FeCoCr alloy, are obliquely sputtered by means of a sputtering system onto a substrate at an angle of incidence of about 60°. The operating pressure of the argon gas atmosphere is between 5 and 15 μbar and the thickness (t Cr ) of the undercoat, which also influences the coercive field strength, is between about 50 and 180 nm. By means of a sector shutter of suitable shape, the thickness distribution between the inner diameter ID and the outer diameter OD of the storage area of the magnetic disk can be influenced in the desired manner.
Inventors
- 👤 Arwed Brunsch
- 👤 Wolf-Dieter Ruh
- 👤 Gerhard Trippel
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 11:40
CPC Classifications
H; H01; H01F; H01F41/00; H01F41/14; H01F41/18; G; G11; G11B; G11B5/00; G11B5/84; G11B5/851; H01F41/20; Y; Y10; Y10S; Y10S428/00; Y10S428/90
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
106 words
A method of producing a metallic magnetic thin film recording surface on a metallic substrate comprising the steps of sputtering an underlayer of Cr on said substrate as said substrate rotates, sputtering a metallic magnetic layer of Cr, Co and Fe on said Cr underlayer of said rotating substrate, said underlayer and said magnetic layer being sputter deposited at an angle between 50° and 75° obliquely to the substrate normal; and selectively shielding different portions of said rotating substrate from said sputtered material during sputtering of both said Cr underlayer and said Co Cr Fe magnetic layer to produce a magnetic recording surface of uniform thickness.
Claim 2
Independent Claim
106 words
A method of producing a metallic magnetic thin film recording surface on a metallic substrate comprising the steps of sputtering an underlayer of Cr on said substrate as said substrate rotates, sputtering a metallic magnetic layer of Cr, Co and Fe on said Cr underlayer of said rotating substrate, said underlayer and said magnetic layer being sputter deposited at an angle between 50° and 75° obliquely to the substrate normal; and selectively shielding different portions of said rotating substrate from said sputtered material during sputtering of both said Cr underlayer and said Co Cr Fe magnetic layer to produce a magnetic recording surface of uniform thickness.
Claim 3
Dependent Claim
21 words
A method in accordance with claim 1, in which said Cr underlayer has a thickness of between 50 and 180 nm.
Claim 4
Dependent Claim
21 words
A method in accordance with claim 1, in which said Cr underlayer has a thickness of between 80 and 100 nm.
Claim 5
Dependent Claim
20 words
A method in accordance with claim 3, in which said magnetic layer is deposited to a thickness of 48 nm.
References Cited (Backward Citations)
GB1439869A
Cited
US3850690A
Cited
GB1408753A
Cited
US4260466A
Cited
US3996095A
Cited
US4245008A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-01-16 | 1987-07-18 | 1988-01-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-01-16 | 1991-07-18 | 1992-01-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-01-16 | 1995-07-18 | 1996-01-17 | $7700.00 | Window Closed / Lapsed |