Electrical insulating refractory composition
Assignee: Combustion Engineering Inc
•
Filing: 1982-06-07
•
Granted: 1984-03-06
•
Expires: 2002-06-07
Abstract
Abstract Sheathed electrical heating elements containing MgO heat conductive, electrical insulating material having a high degree of calcination together with additives in the form of a clay and fumed silica to increase the electrical resistivity, density and flow properties.
Inventors
- 👤 Walter R. Johnson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 20:37
CPC Classifications
H; H01; H01B; H01B3/00; H01B3/02; H01B3/10; H05; H05B; H05B3/00; H05B3/10; H05B3/40; H05B3/42; H05B3/48
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
118 words
A MgO heat conductive electrical insulating embedding composition for sheathing electrical heating elements and having a density of at least 2.385 g/cm 3 , a static flow at least 45.0 g, and an electrical resistivity of at least 5.85 Megohm-inches measured after two hours at 885° C. consisting essentially of in admixture: a. from 97.0 to 99.97 weight % MgO, said MgO being minus 40 mesh and having been calcined at a temperature in excess of 1200° C.; b. from 0.025 to 2.0 weight % of a clay having a soluble salt content less than 0.5% by weight; and c. from 0.005 to 1.0 weight % fumed silica having a particle size of from 0.2 to 0.7 microns.
Claim 2
Dependent Claim
118 words
A MgO heat conductive electrical insulating embedding composition for sheathing electrical heating elements and having a density of at least 2.385 g/cm 3 , a static flow at least 45.0 g, and an electrical resistivity of at least 5.85 Megohm-inches measured after two hours at 885° C. consisting essentially of in admixture: a. from 97.0 to 99.97 weight % MgO, said MgO being minus 40 mesh and having been calcined at a temperature in excess of 1200° C.; b. from 0.025 to 2.0 weight % of a clay having a soluble salt content less than 0.5% by weight; and c. from 0.005 to 1.0 weight % fumed silica having a particle size of from 0.2 to 0.7 microns.
Claim 3
Dependent Claim
41 words
A sheathed electrical heating element comprising an electrical resistance element, a metal sheath surrounding said electrical resistance element and an improved heat conductive electrical insulating composition embedding said electrical resistance element within said sheath consisting of the composition of claim 1.
Claim 4
Dependent Claim
18 words
A MgO heat conductive electrical insulating embedding composition as recited in claim 1 wherein said clay is kaolin.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-03-06 | 1987-09-05 | 1988-03-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-03-06 | 1991-09-05 | 1992-03-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-03-06 | 1995-09-05 | 1996-03-06 | $7700.00 | Window Closed / Lapsed |