Process for producing aromatic polyimide composite separating membrane
Assignee: Ube Corp
•
Filing: 1982-06-11
•
Granted: 1984-04-03
•
Expires: 2002-06-11
Abstract
Abstract An aromatic polyimide composite membrane having an excellent gas-separating property is produced by a process comprising the steps of: coating at least one surface of a substrate consisting of an aromatic polyimide porous membrane with a solution of 0.05% to 10% by weight of an aromatic polyamic acid in a polar organic solvent, which is not capable of dissolving the polyimide porous membrane, at a temperature not exceeding 140 DEG C.; after a during drying the resultant thin coating layer of the polyamic acid solution, heating the resultant polyamic acid layer at a temperature of 150 DEG C. or more so as to convert the polyamic acid layer to the corresponding polyimide layer.
Inventors
- 👤 Hiroshi Makino
- 👤 Yoshihiro Kusuki
- 👤 Takashi Harada
- 👤 Hiroshi Shimazaki
- 👤 Tosio Isida
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 03:49
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/28; B; B01; B01D; B01D69/00; B01D69/12; B01D71/00; B01D71/06; B01D71/58; B01D71/62; B01D71/64; C08J2379/00; C08J2379/04; C08J2379/08; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31721
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
172 words
A process for producing an aromatic polyimide composite separating membrane, comprising the steps of: coating at least one surface of a porous membrane substrate comprised of an aromatic polyimide which contains at least 80 molar % of at least one recurring unit of the formula (I): ##STR4## wherein R represents an aromatic tetravalent radical and R' represents an aromatic divalent radical, with a homogeneous solution containing 0.05% to 10% by weight of an aromatic polyamic acid dissolved in an organic polar solvent capable of dissolving said polyamic acid therein, but not capable of dissolving said polyimide membrane substrate, at a temperature of 140° C. or less, to form a thin layer of said polyamic acid solution; and after or during drying said thin layer of said polyamic acid solution by evaporating said solvent therefrom, heating the resultant polyamic acid coating layer at a temperature of 150° C. or more, whereby the amideacid structure in said polyamic acid is imide-cyclized to convert said polyamic acid coating layer to the corresponding polyimide coating layer.
Claim 2
Dependent Claim
172 words
A process for producing an aromatic polyimide composite separating membrane, comprising the steps of: coating at least one surface of a porous membrane substrate comprised of an aromatic polyimide which contains at least 80 molar % of at least one recurring unit of the formula (I): ##STR4## wherein R represents an aromatic tetravalent radical and R' represents an aromatic divalent radical, with a homogeneous solution containing 0.05% to 10% by weight of an aromatic polyamic acid dissolved in an organic polar solvent capable of dissolving said polyamic acid therein, but not capable of dissolving said polyimide membrane substrate, at a temperature of 140° C. or less, to form a thin layer of said polyamic acid solution; and after or during drying said thin layer of said polyamic acid solution by evaporating said solvent therefrom, heating the resultant polyamic acid coating layer at a temperature of 150° C. or more, whereby the amideacid structure in said polyamic acid is imide-cyclized to convert said polyamic acid coating layer to the corresponding polyimide coating layer.
Claim 3
Dependent Claim
17 words
An aromatic polyimide composite separating membrane produced in accordance with the process as claimed in claim 1.
Claim 4
Dependent Claim
61 words
The process as claimed in claim 1, wherein said aromatic polyimide porous membrane substrate has a permeability (P H .sbsb.2) of hydrogen gas of 5×10 -5 to 5×10 -1 cm 3 /cm 2 .sec.cmHg and exhibits a ratio of the permeability (P H .sbsb.2) of hydrogen gas to a permeability (P CO ) of carbon monoxide gas of 2.0 to 10.0.
Claim 5
Dependent Claim
37 words
The process as claimed in claim 1, wherein the aromatic tetravalent radical represented by R in the formula (I) is a residue of an aromatic tetracarboxylic acid from which the four carboxylic acid moieties have been excluded.
Claim 6
Dependent Claim
34 words
The process as claimed in claim 1, wherein said aromatic divalent radical represented by R' in the formula is a residue of an aromatic diamine from which the two amino moieties have been excluded.
Claim 7
Dependent Claim
30 words
The process as claimed in claim 1, wherein said polyimide in said porous membrane substrate is a polymerization-imidization product of an aromatic tetracarboxylic acid component and an aromatic diamine component.
Claim 8
Dependent Claim
48 words
The process as claimed in claim 6, wherein the tetracarboxylic acid component comprises at least one member selected from the group consisting of biphenyl tetracarboxylic acids, benzophenone tetracarboxylic acids, 2,2-bis(dicarboxyphenyl)propane, bis(3,4-dicarboxyphenyl)-methane, bis(3,4-dicarboxyphenyl)sulfone, bis(3,4-dicarboxyphenyl)ether, bis(3,4-dicarboxyphenyl)thioether, pyromellitic acid, and acid anhydrides, salts, and lower alcohol esters of the above-mentioned acids.
Claim 9
Dependent Claim
112 words
The process as claimed in claim 6, wherein the diamine component comprises at least one member selected from the group consisting of those of the formulae (II) through (V) ##STR5## wherein R 1 , R 2 and R 3 each represent, independently from each other, a member selected from the group consisting of hydrogen atom, lower alkyl radicals having 1 to 3 carbon atoms, and lower alkoxyl radicals having 1 to 3 carbon atoms: A represents a divalent linking member selected from the class consisting of --O--, --S--, --CO--, --SO 2 --, --SO--, --CH 2 -- and --C(CH 3 ) 2 --; and m represents an integer of from 1 to 4.
Claim 10
Dependent Claim
22 words
The process as claimed in claim 1, wherein said polyimide porous membrane substrate has a thickness of from 2 to 500 microns.
Claim 11
Dependent Claim
40 words
The process as claimed in claim 1, wherein said polyamic acid contains at least 60 molar % of at least one type of recurring unit of the formula (VI): ##STR6## wherein R and R' are the same as defined above.
Claim 12
Dependent Claim
39 words
The process as claimed in claim 1, wherein said polar solvent comprises at least one member selected from the group consisting of acetamide, formamide, N-methyl-2-pyrrolidone, N,N-dimethylacetamide, N,N-diethylacetamide, N,N-dimethylformamide, N,N-diethylformamide, N-methylcaprolactam, dimethylsulfoxide, diethylsulfoxide, tetramethylurea, tetraethylurea, dioxane, trioxane and glycol compounds.
Claim 13
Dependent Claim
38 words
The process as claimed in claim 1, wherein said polyamic acid has a logarithmic viscosity of from 0.1 to 7, determined in a concentration of 0.5 g per 100 ml of N-methyl-2-pyrrolidone at a temperature of 30° C.
Claim 14
Dependent Claim
27 words
The process as claimed in claim 1, wherein said polyamic acid solution has a rotation viscosity of 0.01 to 1000 poise at a temperature of 30° C.
Claim 15
Dependent Claim
22 words
The process as claimed in claim 1, wherein said coating procedure is carried out at a temperature of 120° C. or less.
Claim 16
Dependent Claim
25 words
The process as claimed in claim 1, wherein said thin layer of said polyamic acid solution has a thickness of from 0.1 to 200 microns.
Claim 17
Dependent Claim
52 words
The process as claimed in claim 1, wherein before said coating procedure is carried out, said polyimide porous membrane substrate is impregnated with a liquid consisting of at least one member selected from lower aliphatic alcohols, lower aliphatic ketones, benzene type liquid compounds, lower aliphatic carboxylic esters, aliphatic hydrocarbons, and cycloaliphatic hydrocarbons.
Claim 18
Dependent Claim
31 words
The process as claimed in claim 1, wherein before said heating procedure is carried out, the drying procedure is carried out at a temperature of from 30° C. to 150° C.
Claim 19
Dependent Claim
24 words
The process as claimed in claim 1, wherein said heating procedure is carried out at a temperature of from 160° C. to 300° C.
Claim 20
Dependent Claim
25 words
The process as claimed in claim 1, wherein the resultant polyimide coating layer is a dense layer having a thickness of 5 microns or less.
Claim 21
Dependent Claim
27 words
The process as claimed in claim 1, wherein the polyimide in said coating layer is of the same type as the polyimide in said porous membrane substrate.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-04-03 | 1987-10-03 | 1988-04-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-04-03 | 1991-10-03 | 1992-04-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-04-03 | 1995-10-03 | 1996-04-03 | $7700.00 | Window Closed / Lapsed |