Assignee: Huntington Alloys Corp
•
Filing: 1982-03-04
•
Granted: 1984-04-17
•
Expires: 2002-03-04
Abstract
Abstract An improved process is provided for producing mechanically alloyed powders of simple and complex alloy systems. In the improved process, the mechanically alloyed powder is milled to an acceptable processing level in a gravity-dependent ball mill to obtain a powder characterized by a laminate-type microstructure which is substantially optically homogeneous at a magnification of 100×. Such acceptable processing level is reached without processing the powder to a featureless microstructure or to saturation hardness.
Inventors
- 👤 John H. Weber
- 👤 Paul S. Gilman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 13:05
CPC Classifications
B; B02; B02C; B02C17/00; B02C17/16; B22; B22F; B22F9/00; B22F9/02; B22F9/04; B22F2009/041; B22F2009/043
Claims Analysis
Total Claims: 33
Claim 1
Independent Claim
145 words
A system for controlling the mechanical alloying of at least two solid particulate components, said mechanical alloying being carried out by dry high energy milling of the particles in a gravity-dependent type ball mill to maximize mill throughput and minimize time to processing of the particles to an acceptable processing level, said processing level being suitable for producing a consolidated product with a substantially clean microstructure and having grains which are substantially uniform in size and of a desired shape, comprising milling the particles to produce a powder product characterized in that an optical view at 100× of a representative sample of differentially etched particles milled in said gravity-dependent type ball mill shows the presence of particles having a uniform laminate-type structure, the remaining particles being substantially featureless, the particles with the laminate-type structure having a maximum interlaminar distance no greater than about 50 micrometers.
Claim 2
Independent Claim
145 words
A system for controlling the mechanical alloying of at least two solid particulate components, said mechanical alloying being carried out by dry high energy milling of the particles in a gravity-dependent type ball mill to maximize mill throughput and minimize time to processing of the particles to an acceptable processing level, said processing level being suitable for producing a consolidated product with a substantially clean microstructure and having grains which are substantially uniform in size and of a desired shape, comprising milling the particles to produce a powder product characterized in that an optical view at 100× of a representative sample of differentially etched particles milled in said gravity-dependent type ball mill shows the presence of particles having a uniform laminate-type structure, the remaining particles being substantially featureless, the particles with the laminate-type structure having a maximum interlaminar distance no greater than about 50 micrometers.
Claim 3
Dependent Claim
24 words
A system as defined in claim 1, wherein at least a predominant percentage of the particles of the powder product are of the laminate-type.
Claim 4
Dependent Claim
25 words
A system as defined in claim 1, wherein the interlaminar distances in such particles of the powder product is no greater than about 45 micrometers.
Claim 5
Dependent Claim
34 words
A system as defined in claim 1, wherein the interlaminar distances in such particles of the powder product is no greater than about 25 micrometers and the average intelaminar distance is about 15 micrometers.
Claim 6
Dependent Claim
21 words
A system as defined in claim 1, wherein the gravity-dependent ball mill has a diameter of at least above 1 foot.
Claim 7
Dependent Claim
21 words
A system as defined in claim 1, wherein the gravity-dependent type ball mill a length of at least about 1 foot.
Claim 8
Dependent Claim
21 words
A system as defined in claim 1, wherein length of the gravity-dependent ball mill is less than about 1.5 its diameter.
Claim 9
Dependent Claim
22 words
A system as defined in claim 1, wherein the ball charge to the mill is about 15 up to 45 volume %.
Claim 10
Dependent Claim
27 words
A system as defined in claim 1, wherein the ratio of mill diameter to initial ball diameter of the ball charge is about 24/1 to about 200/1.
Claim 11
Dependent Claim
26 words
A system as defined in claim 1, wherein the initial ball diameter of the ball charge in the mill is about 3/16 to about 3/4 inch.
Claim 12
Dependent Claim
33 words
A system as defined in claim 1, wherein the ratio of the ball charge to the gravity-dependent type ball mill to the particulate feed charge is about 40/1 to about 5/1 by mass.
Claim 13
Dependent Claim
27 words
A system as defined in claim 1, wherein the gravity-dependent type ball mill is operated at about 65% up to about 85% of the critical rotational speed.
Claim 14
Dependent Claim
46 words
A system as defined in claim 1, wherein the particles are processed in the mill to a powder product, said powder product being characterized in that a representative sample of the powder has a microstructure at 100× magnification substantially equivalent to that shown in FIG. 2.
Claim 15
Dependent Claim
138 words
A system as defined in claim 1, wherein the mechanically alloyed powder product has a composition consisting essentially of, by weight, up to about 65% chromium, up to about 10% aluminum, up to about 10% titanium, up to about 40% molybdenum, up to about 40% tungsten, up to about 30% niobium, up to about 30% tantalum, up to about 2% vanadium, up to about 15% manganese, up to about 2% carbon, up to about 3% silicon, up to about 1% boron, up to about 2% zirconium, up to about 0.5% magnesium, and the balance at least one element selected from the group consisting of iron, nickel, cobalt and copper, with the sum of the iron, nickel, cobalt and copper being at least 25%, and said composition containing up to about 10% by volume of a dispersed refractory compound.
Claim 16
Dependent Claim
51 words
A system as defined in claim 14, wherein the mechanically alloyed powder product has a composition based upon a system from the group consisting of nickel-chromium, cobalt-chromium and iron-chromium with at least one alloying additive from the group consisting of molybdenum, tungsten, niobium, tantalum, aluminum, titanium, zirconium, carbon, silcon and boron.
Claim 17
Dependent Claim
24 words
A system as defined in claim 14, wherein the refractory compound is selected from the group consisting of refractory oxides, carbides, nitrides and borides.
Claim 18
Dependent Claim
31 words
A system as defined in claim 14, wherein the mechanically alloyed powder is a nickel-, cobalt- or copper-base alloy and the controlled atmosphere comprising free O 2 in an inert carrier.
Claim 19
Dependent Claim
25 words
A system as defined in claim 14, wherein the mechanically alloyed powder product is an iron-base alloy and the controlled atmosphere comprises an inert gas.
Claim 20
Independent Claim
147 words
A system for controlling the mechanical alloying of nickel-, iron-, cobalt- and copper-base alloy systems carried out by dry high energy milling of particles of the component system in a gravity-dependent type ball mill to maximize mill throughput and minimize time to processing to an acceptable processing level, said processing level being suitable for producing a consolidated product with a substantially clean microstructure and having grains which are substantially uniform in size and of a desired shape, comprising milling the particles to produce a powder product characterized in that an optical view at 100× of a representative sample of differentially etched particles milled in said gravity-dependent type ball mill shows the presence of particles having a uniform laminate-type structure, the remaining particles being substantially featureless, and the interlaminar distance is such particles would be an average of about 15 micrometers and no greater than about 25 micrometers.
Claim 21
Independent Claim
147 words
A system for controlling the mechanical alloying of nickel-, iron-, cobalt- and copper-base alloy systems carried out by dry high energy milling of particles of the component system in a gravity-dependent type ball mill to maximize mill throughput and minimize time to processing to an acceptable processing level, said processing level being suitable for producing a consolidated product with a substantially clean microstructure and having grains which are substantially uniform in size and of a desired shape, comprising milling the particles to produce a powder product characterized in that an optical view at 100× of a representative sample of differentially etched particles milled in said gravity-dependent type ball mill shows the presence of particles having a uniform laminate-type structure, the remaining particles being substantially featureless, and the interlaminar distance is such particles would be an average of about 15 micrometers and no greater than about 25 micrometers.
Claim 22
Independent Claim
137 words
A system for controlling the mechanical alloying of nickel-, cobalt- and iron-base superalloy systems carried out by dry high energy milling of particles of the component system in a gravity-dependent type ball mill to maximize throughput and minimize time to processing to an acceptable processing level, said processing level being suitable for producing a consolidated product with a substantially clean microstructure and having elongated grains, comprising milling the particles to produce a powder product characteized in that an optical view at 100× of a representative sample of differentially etched particles milled in said gravity-dependent type ball mill shows the presence of particles having a uniform laminate-type structure, the remaining particles being substantially featureless, and the interlaminar distance in particles having a laminate-type structure being an average of about 15 micrometers and no greater than about 25 micrometers.
Claim 23
Independent Claim
137 words
A system for controlling the mechanical alloying of nickel-, cobalt- and iron-base superalloy systems carried out by dry high energy milling of particles of the component system in a gravity-dependent type ball mill to maximize throughput and minimize time to processing to an acceptable processing level, said processing level being suitable for producing a consolidated product with a substantially clean microstructure and having elongated grains, comprising milling the particles to produce a powder product characteized in that an optical view at 100× of a representative sample of differentially etched particles milled in said gravity-dependent type ball mill shows the presence of particles having a uniform laminate-type structure, the remaining particles being substantially featureless, and the interlaminar distance in particles having a laminate-type structure being an average of about 15 micrometers and no greater than about 25 micrometers.
Claim 24
Dependent Claim
21 words
A system as defined in claim 1, wherein substantially all of the particles of the powder product are of the laminate-type.
Claim 25
Dependent Claim
24 words
A system as defined in claim 19, wherein at least a predominant percentage of the particles are of the powder product of the laminate-type.
Claim 26
Dependent Claim
21 words
A system as defined in claim 19, wherein substantially all of the particles of the powder product are of the laminate-type.
Claim 27
Dependent Claim
24 words
A system as defined in claim 20, wherein at least a predominant percentage of the particles are of the powder product of the laminate-type.
Claim 28
Dependent Claim
21 words
A system as defined in claim 20, wherein substantially all of the particles of the powder product are of the laminate-type.
Claim 29
Dependent Claim
143 words
A process for preparing a mechanically alloyed product, said product comprising at least two solid components said product being produced by dry high energy milling of particles, comprising milling of the particles in the gravity-dependent ball mill to produce a powder product characterized in that an optical view at 100× of a representative sample of differentially etched particles milled in said gravity-dependent ball mill shows the presence of particles having a uniform laminate-type structure, the remaining particles being substantially featureless, the particles with a laminate-type structure having a maximum interlaminar distance no greater than about 50 micrometers, whereby the mill throughput is maximized and time for processing to an acceptable level is minimized, said acceptable processing level being suitable for producing a consolidated product with a substantially clean microstructure and having grains which are substantially uniform in size and of a desired shape.
Claim 30
Dependent Claim
143 words
A process for preparing a mechanically alloyed product, said product comprising at least two solid components said product being produced by dry high energy milling of particles, comprising milling of the particles in the gravity-dependent ball mill to produce a powder product characterized in that an optical view at 100× of a representative sample of differentially etched particles milled in said gravity-dependent ball mill shows the presence of particles having a uniform laminate-type structure, the remaining particles being substantially featureless, the particles with a laminate-type structure having a maximum interlaminar distance no greater than about 50 micrometers, whereby the mill throughput is maximized and time for processing to an acceptable level is minimized, said acceptable processing level being suitable for producing a consolidated product with a substantially clean microstructure and having grains which are substantially uniform in size and of a desired shape.
Claim 31
Dependent Claim
24 words
A process as defined in claim 26, wherein at least a predominant percentage of the particles of the powder product are of the laminate-type.
Claim 32
Dependent Claim
21 words
A process as defined in claim 26, wherein substantially all of the particles of the powder product are of the laminate-type.
Claim 33
Dependent Claim
24 words
A process as defined in claim 26, wherein the powder product produced in the gravity-dependent type ball mill is subjected to a heat treatment.
References Cited (Backward Citations)
US2853767A
Cited
US2995780A
Cited
US3591362A
Cited
US3723092A
Cited
US3728088A
Cited
US3785801A
Cited
US3749612A
Cited
US3874938A
Cited
US3992161A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-04-17 | 1987-10-17 | 1988-04-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-04-17 | 1991-10-17 | 1992-04-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-04-17 | 1995-10-17 | 1996-04-17 | $7700.00 | Window Closed / Lapsed |