US4444718A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of making a high current density cathode
Assignee: United States Department of the Army
•
Filing: 1982-03-19
•
Granted: 1984-04-24
•
Expires: 2002-03-19
Abstract
Abstract A high current density cathode is made by first forming an active porous h purity tungsten pellet by the steps of: (A) mixing tungsten powder with about 1 to 5 percent by weight of the mixture of an activator powder and compacting the powders at a pressure of about 35 tons per square inch to form a pellet, (B) sintering the pellet in a non-oxidizing atmosphere at about 1800 degrees C. for about 11/2 to 31/2 hours to the desired porosity, (C) filling the porous pellet with a filler material, (D) machining to the desired size and shape, (E) removing the filler material, and then forming the cathode by impregnating the pellet with Ba 5 Sr(WO 6 ) 2 at about 1700 degrees C. in an inert atmosphere and subsequently firing for 2 minutes at 1800 degrees C. in dry hydrogen.
Inventors
- 👤 Bernard Smith
- 👤 Gerard L. Freeman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 21:57
CPC Classifications
B; B22; B22F; B22F3/00; B22F3/24; B22F3/26; H; H01; H01J; H01J9/00; H01J9/02; H01J9/04; H01J9/042; H01J9/047
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
116 words
Method of making an active porous high purity tungsten pellet, said method including the steps of: (A) mixing tungsten powder with about 1 to 5 percent by weight of the mixture of an activator powder selected from the group consisting of zirconium hydride, hafnium hydride, scandium oxide, yttrium oxide and aluminum oxide and compacting the powders at a pressure of about 35 tons per square inch to form a pellet, (B) sintering the pellet in a non-oxidizing atmosphere at about 1800 degrees for about 11/2to 31/2 hours to the desired porosity, (C) filling the porous pellet with a methyl methacrylate filler material, (D) machining to the desired size and shape, and (E) removing the filler material.
Claim 2
Dependent Claim
116 words
Method of making an active porous high purity tungsten pellet, said method including the steps of: (A) mixing tungsten powder with about 1 to 5 percent by weight of the mixture of an activator powder selected from the group consisting of zirconium hydride, hafnium hydride, scandium oxide, yttrium oxide and aluminum oxide and compacting the powders at a pressure of about 35 tons per square inch to form a pellet, (B) sintering the pellet in a non-oxidizing atmosphere at about 1800 degrees for about 11/2to 31/2 hours to the desired porosity, (C) filling the porous pellet with a methyl methacrylate filler material, (D) machining to the desired size and shape, and (E) removing the filler material.
Claim 3
Dependent Claim
12 words
Method according to claim 1 wherein the activator powder is zirconium hydride.
Claim 4
Dependent Claim
19 words
Method according to claim 1 wherein the tungsten powder has a particle size of about 4 to 15 microns.
Claim 5
Dependent Claim
15 words
Method according to claim 1 wherein the non-oxidizing atmosphere in Step (B) is a vacuum.
Claim 6
Dependent Claim
14 words
Method according to claim 1 wherein the non-oxidizing atmosphere in Step (B) is hydrogen.
Claim 7
Dependent Claim
166 words
Method of making a high current density cathode, said method comprising first forming an active porous high purity tungsten pellet by the steps of (A) mixing tungsten powder with about 1 to 5 percent by weight of the mixture of an activator powder selected from the group consisting of zirconium hydride, hafnium hydride, scandium oxide, yttrium oxide and aluminum oxide and compacting the powders at a pressure of about 35 tons per square inch to form a pellet, (B) sintering the pellet in a vacuum at about 1800 degrees C. for about 11/2 to 31/2 hours to a porosity of 70 to 80 percent, (C) filling the porous pellet with a methyl methacrylate filler material, (D) machining to the desired size and shape, (E) removing the filler material, and then forming the cathode by impregnating the pellet with Ba 5 Sr(WO 6 ) 2 at about 1700 degrees C. in an inert atmosphere and subsequently firing for 2 minutes at 1800 degrees C. in dry hydrogen.
Claim 8
Dependent Claim
166 words
Method of making a high current density cathode, said method comprising first forming an active porous high purity tungsten pellet by the steps of (A) mixing tungsten powder with about 1 to 5 percent by weight of the mixture of an activator powder selected from the group consisting of zirconium hydride, hafnium hydride, scandium oxide, yttrium oxide and aluminum oxide and compacting the powders at a pressure of about 35 tons per square inch to form a pellet, (B) sintering the pellet in a vacuum at about 1800 degrees C. for about 11/2 to 31/2 hours to a porosity of 70 to 80 percent, (C) filling the porous pellet with a methyl methacrylate filler material, (D) machining to the desired size and shape, (E) removing the filler material, and then forming the cathode by impregnating the pellet with Ba 5 Sr(WO 6 ) 2 at about 1700 degrees C. in an inert atmosphere and subsequently firing for 2 minutes at 1800 degrees C. in dry hydrogen.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-04-24 | 1987-10-24 | 1988-04-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-04-24 | 1991-10-24 | 1992-04-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-04-24 | 1995-10-24 | 1996-04-24 | $7700.00 | Window Closed / Lapsed |