Method for preparing absorbent fibrous fluff
Assignee: Dow Chemical Co
•
Filing: 1982-01-04
•
Granted: 1984-04-24
•
Expires: 2002-01-04
Abstract
Abstract A method of preparing fibrous hydrophilic fluff having increased absorbency is disclosed. An absorbent polymer solution is coated on base fluffing material, and the coated fluffing material is dried, disintegrated and mechanically worked into a fibrous fluff matrix which contains absorbent polymer platelets distributed throughout said matrix.
Inventors
- 👤 Robert E. Erickson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 10:39
CPC Classifications
B; B32; B32B; B32B27/00; B32B27/12; A; A61; A61L; A61L15/00; A61L15/16; A61L15/22; A61L15/225; A61L15/42; A61L15/60; B32B27/06; B32B27/065; B32B27/10; B32B5/00; B32B5/02; B32B5/022; B32B5/18; D; D21; D21C; D21C9/00; D21C9/001; D21C9/002; D21C9/005; A61F; A61F13/00; A61F13/15; A61F13/20; A61F13/2002; A61F13/202; A61F13/53; A61F13/534; A61F13/537; A61F2013/15008; A61F2013/15048; A61F13/15577; A61F2013/15821; A61F13/51; A61F13/514; A61F13/51401; A61F2013/51409; A61F2013/530131; A61F2013/530481; A61F2013/530802; A61F13/53708; A61F2013/53721; B32B2555/00; B32B2555/02; Y; Y10; Y10S; Y10S428/00; Y10S428/913; Y10T; Y10T428/00; Y10T428/24; Y10T428/24273; Y10T428/24322; Y10T428/24331; Y10T428/29; Y10T428/2982; Y10T442/00; Y10T442/30; Y10T442/3707; Y10T442/3854; Y10T442/3886; Y10T442/60; Y10T442/647; Y10T442/651; Y10T442/659
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
67 words
A method for preparing a fibrous fluff of improved absorbency, said method comprising passing a base fluffing material through a zone wherein an aqueous solution of polymer which has been formulated into an absorbent composition is coated on the base fluffing material, the absorbent coated base fluffing material composite is then dried and finally disintegrated and worked by mechanical means into a plurality of absorbent fluff fibers.
Claim 2
Independent Claim
67 words
A method for preparing a fibrous fluff of improved absorbency, said method comprising passing a base fluffing material through a zone wherein an aqueous solution of polymer which has been formulated into an absorbent composition is coated on the base fluffing material, the absorbent coated base fluffing material composite is then dried and finally disintegrated and worked by mechanical means into a plurality of absorbent fluff fibers.
Claim 3
Dependent Claim
24 words
The method of claim 1 wherein the aqueous solution of absorbent polymer comprises an aqueous solution of a lightly cross-linked alkali metal carboxylic polyelectrolyte.
Claim 4
Dependent Claim
23 words
The method of claim 2 wherein the polyelectrolyte is cross-linked with a polyfunctional or difunctional cross-linking agent that is reactive with carboxylate groups.
Claim 5
Dependent Claim
15 words
The method of claim 3 wherein the polyfunctional cross-linking agent is a polyamide-polyamine epichlorohydrin adduct.
Claim 6
Dependent Claim
14 words
The method of claim 3 wherein the polyfunctional cross-linking agent is a diglycidyl ether.
Claim 7
Dependent Claim
17 words
The method of claim 2 wherein the polyelectrolyte consists of an alkali metal salt of a polyacrylate.
Claim 8
Dependent Claim
27 words
The method of claim 2 wherein the polyelectrolyte consists of a terpolymer of ethyl acrylate, sodium acrylate and sodium methacrylate with 50 mole percent being ethyl acrylate.
Claim 9
Dependent Claim
46 words
A method of claim 7 wherein the polyelectrolyte comprises a 25 percent aqueous solution by volume consisting of 52 mole percent ethyl acrylate, 28 mole percent sodium methacrylate, and 28 mole percent sodium acrylate, and having a pH range of from about 6 to about 8.
Claim 10
Dependent Claim
23 words
The method of claim 1 wherein the absorbent composition comprises a solution consisting of acrylic terpolymer, polyoxyethylene sorbitan monolaurate, polyamide/epichlorohydrin resin and glycerine.
Claim 11
Dependent Claim
54 words
The method of claim 9 wherein the absorbent composition comprises a solution of from about 71.5 to about 94.4 weight percent acrylic polymer, from about 5 to about 1 weight percent polyoxyethylene sorbitan monolaurate, from about 1.0 to about 0.6 weight percent polyamide epichlorohydrin resin, and from 0 to about 27.0 weight percent glycerine.
Claim 12
Dependent Claim
19 words
A method of claim 1 wherein the drying temperature range is from about 150° F. to about 350° F.
Claim 13
Dependent Claim
13 words
A method of claim 4 wherein the drying temperature is about 250° F.
Claim 14
Dependent Claim
11 words
The absorbent fluff prepared according to the method of claim 1.
Claim 15
Dependent Claim
11 words
The absorbent fluff prepared according to the method of claim 2.
Claim 16
Dependent Claim
20 words
An absorbent device which comprises the absorbent fluff of claim 13, a water-impermeable bottom sheet and a water-permeable face sheet.
Claim 17
Dependent Claim
28 words
An absorbent device which comprises the absorbent fluff of claim 13, one or more layers of intermediate wicking sheets, a water-impermeable bottom sheet and a water-permeable face sheet.
Claim 18
Dependent Claim
20 words
An absorbent device which comprises the absorbent fluff of claim 14, a water-impermeable bottom sheet and a water-permeable face sheet.
Claim 19
Dependent Claim
28 words
An absorbent device which comprises the absorbent fluff of claim 14, one or more layers of intermediate wicking sheets, a water-impermeable bottom sheet and a water-permeable face sheet.
Claim 20
Dependent Claim
45 words
The absorbent device of claim 15 wherein said water-impermeable bottom sheet comprises a flexible hydrophilic absorbent laminate having a central, substantially continuous and uniform film consisting of a lightly cross-linked carboxylic polyelectrolyte and a layer of wicking substrates bonded to both sides of said film.
Claim 21
Dependent Claim
45 words
The absorbent device of claim 17 wherein said water-impermeable bottom sheet comprises a flexible hydrophilic absorbent laminate having a central, substantially continuous and uniform film consisting of a lightly cross-linked carboxylic polyelectrolyte and a layer of wicking substrates bonded to both sides of said film.
Claim 22
Dependent Claim
22 words
The absorbent device of claim 19 wherein said water-impermeable bottom sheet is polyethylene and said face sheet is a nonwoven fiber mat.
Claim 23
Dependent Claim
22 words
The absorbent device of claim 20 wherein said water-impermeable bottom sheet is polyethylene and said face sheet is a nonwoven fiber mat.
Claim 24
Dependent Claim
32 words
The absorbent device of claim 19 wherein said intermediate wicking sheets are selected from a group consisting of woven fabrics, paper tissues, nonwoven fiber mats, polymeric foams, and flexible hydrophilic absorbent laminate.
Claim 25
Dependent Claim
32 words
The absorbent device of claim 20 wherein said intermediate wicking sheets are selected from a group consisting of woven fabrics, paper tissues, nonwoven fiber mats, polymeric foams, and flexible hydrophilic absorbent laminates.
References Cited (Backward Citations)
US3658613A
Cited
US3959569A
Cited
US4018951A
Cited
US3888257A
Cited
US3966679A
Cited
US4076928A
Cited
US4079029A
Cited
US4117184A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-04-24 | 1987-10-24 | 1988-04-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-04-24 | 1991-10-24 | 1992-04-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-04-24 | 1995-10-24 | 1996-04-24 | $7700.00 | Window Closed / Lapsed |