US4451517A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Ceramic honeycomb catalyst support coated with activated alumina
Assignee: NIPPON SKEN Inc
•
Filing: 1982-07-15
•
Granted: 1984-05-29
•
Expires: 2002-07-15
Abstract
Abstract A catalyst support provided with an activated alumina layer which is formed on the surface of the ceramic honeycomb structure is disclosed. The catalyst support of the present invention is formed of ceramic such as cordierite, of which coefficient of thermal expansion is lower than alumina and is provided with microcracks which occur when the honeycomb structure is formed. The activated alumina layer is formed on the surface of the catalyst support without filling the microcracks occurred therein. For example, the activated alumina layer is formed by adhering the activated alumina particulates to the surface of the honeycomb structure and firing the structure together with the activated alumina particulates after the microcracks occurred in the honeycomb structure are filled with such a material as to be burnt away at a temperature lower than the sintering temperature of activated alumina.
Inventors
- 👤 Kazuhiro Inoguchi
- 👤 Kunio Okamoto
- 👤 Keiichiro Isomura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 05:49
CPC Classifications
B; B01; B01D; B01D53/00; B01D53/34; B01D53/74; B01D53/86; B01J; B01J21/00; B01J21/02; B01J21/04; B01J37/00; B01J37/02; B01J37/0215; B01J35/00; B01J35/50; B01J35/56; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24149; Y10T428/24744
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
177 words
A ceramic honeycomb catalyst support having a honeycomb structure with an activated alumina coating thereon, adapted for purifying exhaust gases and exhibiting improved resistance to thermal shock, said honeycomb structure formed of a ceramic material having a coefficient of thermal expansion below that of activated alumina, said honeycomb structure having a matrix of thin walls forming a multiplicity of open ended cells or passages defined by the thin walls extending from one end of the honeycomb to the other end, said honeycomb structure having in the surface walls thereof a multiplicity of minute pores and a multiplicity of fine cracks of a width smaller than said minute pores, said fine cracks and minute pores formed during the fabrication of the honeycomb structure, and a layer of activated alumina adhered onto the surfaces of said thin walls, said fine cracks being substantially completely devoid of said activated alumina such that the area within said fine cracks is unfilled and are free to act as buffer zones to absorb deformation of the honeycomb structure as it expands when heated.
Claim 2
Dependent Claim
177 words
A ceramic honeycomb catalyst support having a honeycomb structure with an activated alumina coating thereon, adapted for purifying exhaust gases and exhibiting improved resistance to thermal shock, said honeycomb structure formed of a ceramic material having a coefficient of thermal expansion below that of activated alumina, said honeycomb structure having a matrix of thin walls forming a multiplicity of open ended cells or passages defined by the thin walls extending from one end of the honeycomb to the other end, said honeycomb structure having in the surface walls thereof a multiplicity of minute pores and a multiplicity of fine cracks of a width smaller than said minute pores, said fine cracks and minute pores formed during the fabrication of the honeycomb structure, and a layer of activated alumina adhered onto the surfaces of said thin walls, said fine cracks being substantially completely devoid of said activated alumina such that the area within said fine cracks is unfilled and are free to act as buffer zones to absorb deformation of the honeycomb structure as it expands when heated.
Claim 3
Dependent Claim
61 words
The ceramic honeycomb catalyst support according to claim 1 in which said minute pores only are filled with a ceramic having a coefficient of thermal expansion lower than that of said activated alumina and said activated alumina coating adhered to the thin walls of the structure is also adhered to said ceramic filling exposed at the surface of said minute pores.
Claim 4
Dependent Claim
33 words
The ceramic honeycomb catalyst support according to claim 1 in which said minute pores are greater than about 0.5 microns in diameter and said fine cracks are not greater than about 0.5 microns.
Claim 5
Dependent Claim
21 words
The ceramic honeycomb catalyst support according to claim 1 in which said honeycomb structure is formed of cordierite, mullite or spodumen.
Claim 6
Dependent Claim
25 words
The ceramic honeycomb catalyst support according to claim 2 in which said ceramic filling said minute pores is cordierite, spodumen, eucryptite, aluminum titanate or mullite.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-05-29 | 1987-11-28 | 1988-05-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-05-29 | 1991-11-28 | 1992-05-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-05-29 | 1995-11-28 | 1996-05-29 | $7700.00 | Window Closed / Lapsed |