Surface treatment of inorganic fillers
Assignee: Dow Silicones Corp
•
Filing: 1982-12-02
•
Granted: 1984-06-12
•
Expires: 2002-12-02
Abstract
Abstract This invention relates to a method of surface treating particulate inorganic fillers with a surface-treating agent which is an equilibrated reaction mixture consisting essentially of R 2 SiO 2/2 units, RSiO 3/2 units and CH 3 O 1/2 radicals wherein the mixture contains A moles of R 2 SiO 2/2 units per mole of RSiO 3/2 units and B moles of CH 3 O 1/2 radicals, A having an average value of from 0.5 to 10 and B having an average value of from 3 to 6, the value of B being related to A such that when A=0.5, B=6 and when A=10, B=3, and R being a hydrocarbon radical of from 1 to 10 inclusive carbon atoms or a haloalkyl radical of from 1 to 10 inclusive carbon atoms. Reinforcing silica fillers, surface-treated with such equilibrated reaction mixtures can be compounded with polydiorganosiloxanes curable to elastomers and cured to obtain silicone elastomers possessing high optical clarity and physical properties which make the cured elastomer uniquely suitable for use as prosthetic devices for use on or within the body.
Inventors
- 👤 Kenneth M. Lee
- 👤 Katherine L. Ulman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 22:37
CPC Classifications
C; C09; C09C; C09C3/00; C09C3/12; A; A61; A61L; A61L27/00; A61L27/40; A61L27/44; A61L27/446; C08; C08K; C08K9/00; C08K9/08; C09C1/00; C09C1/28; C09C1/30; C09C1/3081; C01; C01P; C01P2006/00; C01P2006/12; C01P2006/80; C01P2006/90; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31652; Y10T428/31663
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
257 words
A method of surface treating a particulate inorganic filler which comprises the steps of (A) contacting 100 parts by weight of a particulate inorganic filler with a surface treating agent comprising at least one component which is an equilibrated reaction mixture consisting essentially of R 2 SiO 2/2 units, RSiO 3/2 units and CH 3 O 1/2 radicals, there being A moles of R 2 SiO 2/2 units per mole of RSiO 3/2 units present in said mixture and B moles of said CH 3 O 1/2 radicals, said A having an average value of from 0.5 to 10 and B having an average value of from 3 to 6, the value of B being related to A such that when A=0.5, B=6 and when A=10, B=3, and wherein R is selected from the group consisting of hydrocarbon radicals of from 1 to 10 inclusive carbon atoms and haloalkyl radicals of from 1 to 10 inclusive carbon atoms, said reaction mixture (1) having been prepared by equilibration in the presence of a catalyst for the equilibration reaction and (2) having an overall average molecular weight of less than 500, there being at least 5 and up to 50 parts of weight of said equilibrated reaction mixture based on the total weight of R 2 SiO 2/2 and RSiO 3/2 units present in the mixture per 100 parts by weight of said filler, and (B) maintaining said surface-treating agent in contact with said filler for a sufficient amount of time to obtain a hydrophobic, surface-treated particulate inorganic filler.
Claim 2
Independent Claim
257 words
A method of surface treating a particulate inorganic filler which comprises the steps of (A) contacting 100 parts by weight of a particulate inorganic filler with a surface treating agent comprising at least one component which is an equilibrated reaction mixture consisting essentially of R 2 SiO 2/2 units, RSiO 3/2 units and CH 3 O 1/2 radicals, there being A moles of R 2 SiO 2/2 units per mole of RSiO 3/2 units present in said mixture and B moles of said CH 3 O 1/2 radicals, said A having an average value of from 0.5 to 10 and B having an average value of from 3 to 6, the value of B being related to A such that when A=0.5, B=6 and when A=10, B=3, and wherein R is selected from the group consisting of hydrocarbon radicals of from 1 to 10 inclusive carbon atoms and haloalkyl radicals of from 1 to 10 inclusive carbon atoms, said reaction mixture (1) having been prepared by equilibration in the presence of a catalyst for the equilibration reaction and (2) having an overall average molecular weight of less than 500, there being at least 5 and up to 50 parts of weight of said equilibrated reaction mixture based on the total weight of R 2 SiO 2/2 and RSiO 3/2 units present in the mixture per 100 parts by weight of said filler, and (B) maintaining said surface-treating agent in contact with said filler for a sufficient amount of time to obtain a hydrophobic, surface-treated particulate inorganic filler.
Claim 3
Dependent Claim
80 words
The method as claimed in claim 1 wherein said reaction mixture is obtained by equilibrating a mixture of (1) cyclic polydiorganosiloxanes of the average formula (R 2 SIO) x and (2) RSi(OCH 3 ) 3 wherein the amounts of (1) and (2) are selected such that the equilibrated reaction mixture has a molar ratio of R 2 SiO 2/2 :RSiO 3/2 units in the range of 0.5:1 to 10:1, said x having an average value of from 3 to 7.
Claim 4
Dependent Claim
80 words
The method as claimed in claim 2 wherein the inorganic filler is a silica filler having a surface area of at least 50 m 2 /g, the ratio of R 2 SiO 2/2 :RSiO 3/2 is in the range of 0.75:1 to 4:1 and at least 70 weight percent of the cyclic polysiloxanes are cyclic polysiloxanes wherein x=4, and wherein more than 50 mole percent of the total moles of R radicals present in said reaction mixture are methyl radicals.
Claim 5
Dependent Claim
41 words
The method as claimed in claim 3 wherein R is selected from the group consisting of methyl and vinyl radicals, no more than 10 mole percent of the total moles of R radicals present in said reaction mixture being vinyl radicals.
Claim 6
Dependent Claim
25 words
The method as claimed in claim 3 wherein the ratio of R 2 SiO 2/2 :RSiO 3/2 is in the range of 0.9:1 to 1.1:1.
Claim 7
Dependent Claim
41 words
The method as claimed in claim 5 wherein R is selected from the group consisting of methyl and vinyl radicals, no more than 10 mole percent of the total moles of R radicals present in said reaction mixture being vinyl radicals.
Claim 8
Dependent Claim
19 words
A hydrophobic, surface-treated particulate inorganic filler which has been surface treated in accordance with the method of claim 1.
Claim 9
Dependent Claim
19 words
A hydrophobic, surface-treated particulate inorganic filler which has been surface treated in accordance with the method of claim 2.
Claim 10
Dependent Claim
19 words
A hydrophobic, surface-treated particulate silica filler which has been surface treated in accordance with the method of claim 3.
Claim 11
Dependent Claim
19 words
A hydrophobic, surface-treated particulate silica filler which has been surface treated in accordance with the method of claim 4.
Claim 12
Dependent Claim
18 words
A hydrophobic, surface-treated particulate silica filler which has been surface treated in accordance with method of claim 5.
Claim 13
Dependent Claim
20 words
A hydrophobic, surface treated particulate silica filler which has been surface treated in accordance with the method of claim 6.
Claim 14
Dependent Claim
46 words
A composition curable to a silicone elastomer comprising from 50 to 97.5 parts by weight of at least one polydiorganosiloxane and from 2.5 to 50 parts by weight of a particulate inorganic filler which has been surface treated in accordance with the method of claim 1.
Claim 15
Dependent Claim
70 words
The curable composition as claimed in claim 13 wherein said reaction mixture is obtained by equilibrating a mixture of (1) cyclic polydiorganosiloxanes of the average formula (R 2 SiO) x and (2) RSi(OCH 3 ) 3 wherein the amount of (1) and (2) are selected such that the equilibrated reaction mixture has a molar ratio of R 2 SiO 2/2 :RSiO 3/2 units in the range of 0.5:1 to 10:1.
Claim 16
Dependent Claim
59 words
The curable composition as claimed in claim 14 wherein the inorganic filler is a silica filler having a surface area of at least 50 m 2 /g, the ratio of R 2 SiO 2/2 :RSiO 3/2 is in the range of 0.75:1 to 4:1 and at least 70 weight percent of the cyclic polysiloxanes are cyclic polysiloxanes wherein x=4.
Claim 17
Dependent Claim
42 words
The curable composition as claimed in claim 15 wherein R is selected from the group consisting of methyl and vinyl radicals, no more then 10 mole percent of the total moles of R radicals present in said reaction mixture being vinyl radicals.
Claim 18
Dependent Claim
26 words
The curable composition as claimed in claim 16 wherein the ratio of R 2 SiO 2/2 :RSiO 3/2 is in the range of 0.9:1 to 1.1:1.
Claim 19
Dependent Claim
42 words
The curable composition as claimed in claim 17 wherein R is selected from the group consisting of methyl and vinyl radicals, no more than 10 mole percent of the total moles of R radicals present in said reaction mixture being vinyl radicals.
Claim 20
Dependent Claim
14 words
A cured elastomer comprising the product obtained upon curing the composition of claim 13.
Claim 21
Dependent Claim
14 words
A cured elastomer comprising the product obtained upon curing the composition of claim 14.
Claim 22
Dependent Claim
14 words
A cured elastomer comprising the product obtained upon curing the composition of claim 15.
Claim 23
Dependent Claim
14 words
A cured elastomer comprising the product obtained upon curing the composition of claim 17.
Claim 24
Dependent Claim
14 words
A cured elastomer comprising the product obtained upon curing the composition of claim 18.
Claim 25
Dependent Claim
15 words
The cured elastomer of claim 20 which is in the form of a prosthetic device.
Claim 26
Dependent Claim
15 words
The cured elastomer of claim 21 which is in the form of a prosthetic device.
Claim 27
Dependent Claim
15 words
The cured elastomer of claim 22 which is in the form of a prosthetic device.
Claim 28
Dependent Claim
15 words
The cured elastomer of claim 23 which is in the form of a prosthetic device.
References Cited (Backward Citations)
US2927909A
Cited
US2706724A
Cited
US2909549A
Cited
US2954357A
Cited
US3024126A
Cited
US3341489A
Cited
US3305524A
Cited
GB1364248A
Cited
US3979546A
Cited
US3876605A
Cited
US4228054A
Cited
US4344800A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-06-12 | 1987-12-12 | 1988-06-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-06-12 | 1991-12-12 | 1992-06-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-06-12 | 1995-12-12 | 1996-06-12 | $7700.00 | Window Closed / Lapsed |