US4457955A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for producing magnetizable particles
Assignee: Daikin Industries Ltd
•
Filing: 1982-12-29
•
Granted: 1984-07-03
•
Expires: 2002-12-29
Abstract
Abstract A process for producing cobalt-modified iron oxide particles, which comprises the steps of: (1) adding to magnetic iron oxide particles (a) a cobalt compound, (b) an iron component which is either (b1) a ferric compound at an atomic ratio to the cobalt compound in the range of 0.68 to 2 or (b2) a combination of a ferrous compound and a ferric compound, and (c) an alkali at a concentration enough to cause the cobalt and iron to precipitate as hydroxides; and (2) heating the mixture at a temperature of at least 50 DEG C. and not higher than the reflux temperature thereof in a non-oxidizing atmosphere.
Inventors
- 👤 Kazuo Okamura
- 👤 Kohji Tamura
- 👤 Shigeo Daimon
- 👤 Yoshiyuki Shibuya
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 23:23
CPC Classifications
C; C01; C01G; C01G51/00; C01G51/40; C01G49/00; C01G49/02; C01G49/06; G; G11; G11B; G11B5/00; G11B5/62; G11B5/68; G11B5/70; G11B5/706; G11B5/70626; G11B5/70642; G11B5/70652; G11B5/70668; G11B5/70673; C01P; C01P2002/00; C01P2002/50; C01P2002/52; C01P2002/54; C01P2006/00; C01P2006/42
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
116 words
A process for producing cobalt-modified iron oxide particles, which comprises the steps of: (1) forming a slurry by adding to magnetic iron oxide particles dispersed in an aqueous solution (a) a cobalt compound, (b) an iron component which is a combination of a ferrous compound and a ferric compound, at a Fe/Co atomic ratio in the range of 1.3 to 2.5 for the ferrous compound and 0.5 to 1.3 for the ferric compound, and (c) an alkali at a concentration enough to cause the cobalt and iron to precipitate as hydroxides; and (2) heating the slurry at a temperature of at least 50° C. and not higher than the reflux temperature thereof in a non-oxidizing atmosphere.
Claim 2
Dependent Claim
116 words
A process for producing cobalt-modified iron oxide particles, which comprises the steps of: (1) forming a slurry by adding to magnetic iron oxide particles dispersed in an aqueous solution (a) a cobalt compound, (b) an iron component which is a combination of a ferrous compound and a ferric compound, at a Fe/Co atomic ratio in the range of 1.3 to 2.5 for the ferrous compound and 0.5 to 1.3 for the ferric compound, and (c) an alkali at a concentration enough to cause the cobalt and iron to precipitate as hydroxides; and (2) heating the slurry at a temperature of at least 50° C. and not higher than the reflux temperature thereof in a non-oxidizing atmosphere.
Claim 3
Dependent Claim
37 words
A process as defined in claim 1 wherein the cobalt compound is added in an amount of 0.3 to 10 parts by weight as Co atom per 100 parts by weight of the magnetic iron oxide particles.
Claim 4
Dependent Claim
35 words
A process as defined in claim 2 wherein the amount of the cobalt compound is 0.5 to 5 parts by weight as Co atom per 100 parts by weight of the magnetic iron oxide particles.
Claim 5
Dependent Claim
46 words
A process as defined in claim 1 wherein the magnetic iron oxide is γ-Fe 2 O 3 , Fe 3 O 4 or a Berthollide iron oxide having a degree of oxidation intermediate between those of γ-Fe 2 O 3 and Fe 3 O 4 .
Claim 6
Dependent Claim
19 words
A process as defined in claim 1 wherein the cobalt compound is sulfate, nitrate, chloride or hydroxide of Co(II).
Claim 7
Dependent Claim
19 words
A process as defined in claim 1 wherein the ferrous compound is sulfate, nitrate, chloride or hydroxide of Fe(II).
Claim 8
Dependent Claim
19 words
A process as defined in claim 1 wherein the ferric compound is sulfate, nitrate, chloride or hydroxide of Fe(III).
Claim 9
Dependent Claim
28 words
A process as defined in claim 1 wherein the alkali is added at a concentration enough to adjust the pH of the reaction system to 9.5 or greater.
Claim 10
Dependent Claim
28 words
A process as defined in claim 8 wherein the alkali is added at a concentration enough to adjust the pH of the reaction system to 12 or greater.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-07-03 | 1988-01-02 | 1988-07-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-07-03 | 1992-01-02 | 1992-07-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-07-03 | 1996-01-02 | 1996-07-03 | $7700.00 | Window Closed / Lapsed |