Polyvinyl-alcohol-based thermoplastic composition
Assignee: Individual
•
Filing: 1982-11-01
•
Granted: 1984-09-04
•
Expires: 2002-11-01
Abstract
Abstract This invention relates to a thermoplastic composition based on polyvinyl alcohol, which is adapted to be subjected, as such, to the common methods of shaping in the hot condition used for thermoplastic materials, such as molding and extrusion, for the product of articles, characterized in that it is composed of a substantially dry mixture of said polyvinyl alcohol with at least one or more solid polyhydroxylated monomeric alcohols, which, as such or in admixture with each other, exhibit their main peak melting point, as determined by Differential Thermal Analysis, between 160° C., and 230° C.
Inventors
- 👤 Pietro Cattaneo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 15:39
CPC Classifications
C; C08; C08K; C08K5/00; C08K5/04; C08K5/05; C08K5/053
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
86 words
A thermostatic composition based on polyvinyl alcohol and adapted to be subjected as such to the conventional hot shaping procedure for thermoplastic materials, such as molding and extrusion for the production of articles, characterized in that it is composed of a dry mixture of said polyvinyl alcohol containing originally absorbed moisture and one or more solid monomeric polyhydroxylated alcohols which, as such or in mutual admixture, exhibit the main melting point peak as determined by differential thermal analysis (DTA) comprised between 160° C. and 230° C.
Claim 2
Dependent Claim
86 words
A thermostatic composition based on polyvinyl alcohol and adapted to be subjected as such to the conventional hot shaping procedure for thermoplastic materials, such as molding and extrusion for the production of articles, characterized in that it is composed of a dry mixture of said polyvinyl alcohol containing originally absorbed moisture and one or more solid monomeric polyhydroxylated alcohols which, as such or in mutual admixture, exhibit the main melting point peak as determined by differential thermal analysis (DTA) comprised between 160° C. and 230° C.
Claim 3
Dependent Claim
34 words
Composition according to claim 1, characterized in that at least one of said monomeric polyhydroxylated alcohols is a member selected from among the alcohols having at least three primary alcoholic functional groups per mol.
Claim 4
Dependent Claim
34 words
Composition according to claim 2, characterized in that said monomeric polyhydroxylated alcohol is a member preferably selected from the group consisting of pure or technical grade pentaerythritol, bipentaerythritol, pure or technical grade, and trimethylolethane.
Claim 5
Dependent Claim
36 words
Composition according to claim 1, characterized in that at least one of said monomeric polyhydroxylated alcohols is a member selected from the group consisting of those having two primary alcoholic groups per mol, such as mannitol.
Claim 6
Dependent Claim
34 words
Composition according to claim 1, characterized in that said polyvinyl alcohol has a degree of hydrolysis greater than 70%, expressed as a molar fraction, and a degree of polymerization comprised between 500 and 2500.
Claim 7
Dependent Claim
26 words
Composition according to claim 1, characterized in that it comprises between 10 and 50 parts of said monomeric polyhydroxylated alcohols per 100 parts of polyvinyl alcohols.
Claim 8
Dependent Claim
44 words
Composition according to claim 1, including a component selected from the group consisting of glycol monoethers, glycol monoesters, polycondensed glycols metallic oxides, carbonates, silicates, mineral salts and mixtures thereof having a melting point higher than 160° C., both in their hydrous and anhydrous forms.
Claim 9
Dependent Claim
22 words
Composition according to claim 1, characterized in that it contains mixture up to a maximum of 7% by weight on the total.
Claim 10
Dependent Claim
13 words
Composition according to claim 1, characterized in that it is in granular form.
References Cited (Backward Citations)
US4323492A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-09-04 | 1988-03-05 | 1988-09-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-09-04 | 1992-03-05 | 1992-09-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-09-04 | 1996-03-05 | 1996-09-04 | $7700.00 | Window Closed / Lapsed |