Abstract
Abstract A method of manufacturing capacitance video discs comprising thermoplastic resins and conductive carbon black, wherein said conductive carbon black having an average primary particle size of 25 millimicrons or less is washed by water or an inorganic acid, heated at temperatures of 400 DEG to 1,200 DEG C. in a non-oxidizing atmosphere and wherein the coarse particles having a grain size of 0.05 mm or more are substantially eliminated. This method can provide video discs having reduced surface defects and stability after a moisture-proof test.
Inventors
- 👤 Yoshio Enoki
- 👤 Kazuhisa Morimoto
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 16:55
CPC Classifications
G; G11; G11B; G11B9/00; G11B9/06; G11B9/061; G11B9/063; G11B9/068
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
112 words
A method of producing video discs having reduced surface defects and improved moisture-proofness by molding a conductive material comprising a blend of thermoplastic resins and conductive carbon blacks and forming information signals on said video discs in the form of a change in the geometric variation, wherein said conductive blacks have an average primary particle size of 25 millimicrons or less measured by an electron microscope and an oil absorption of 200 cm 3 /100 g or more measured by ASTM D 2414-79, and wherein said conductive carbon blacks are preliminarily washed with water or an aqueous solution of an inorganic acid to remove ash before blending and molding the conductive material.
Claim 2
Independent Claim
112 words
A method of producing video discs having reduced surface defects and improved moisture-proofness by molding a conductive material comprising a blend of thermoplastic resins and conductive carbon blacks and forming information signals on said video discs in the form of a change in the geometric variation, wherein said conductive blacks have an average primary particle size of 25 millimicrons or less measured by an electron microscope and an oil absorption of 200 cm 3 /100 g or more measured by ASTM D 2414-79, and wherein said conductive carbon blacks are preliminarily washed with water or an aqueous solution of an inorganic acid to remove ash before blending and molding the conductive material.
Claim 3
Dependent Claim
31 words
A method of producing video discs as claimed in claim 1, wherein said inorganic acids contain at least one acid selected from the group consisting of sulfuric acid and hydrochloric acid.
Claim 4
Dependent Claim
32 words
A method of producing video discs as claimed in claim 1, wherein said conductive carbon blacks, from which ash was removed, are dried by heating in vacuum or an inert gas atmosphere.
Claim 5
Dependent Claim
46 words
A method of producing video discs as claimed in claim 1, wherein said conductive carbon blacks, from which ash was removed, are impregnated with an alkaline aqueous solution selected from the group consisting of ammonia, alkali metal hydroxides and alkali metal salts solutions, and then dried.
Claim 6
Dependent Claim
29 words
A method of producing video discs as claimed in claim 1, wherein the ash removed blacks are heated in a nonoxidizing atmosphere at temperature of 400° to 900° C.
Claim 7
Dependent Claim
50 words
A method of producing video discs as claimed in claim 1, wherein the ash removed carbon blacks are heated in a nonoxidizing atmosphere at a temperature of 400° to 1,200° C. and the coarse particles having grain size of 0.05 mm or more are removed substantially by a dry classification.
Claim 8
Dependent Claim
33 words
A method according to claim 1 wherein the conductive material comprises 10 to 40 parts by weight of the preliminarily washed carbon blacks blended with 100 parts by weight of the thermoplastic resin.
Claim 9
Dependent Claim
17 words
A method according to claim 7 wherein the thermoplastic resin is a vinyl chloride type thermoplastic resin.
Claim 10
Dependent Claim
20 words
A method according to claim 7 wherein the conductive material also contains an effective amount of plasticizers, stabilizers and lubricants.
Claim 11
Dependent Claim
22 words
A method according to claim 1 wherein the conductive carbon blacks have an average primary particle size of 20 millimicrons or less.
References Cited (Backward Citations)
US3842194A
Cited
US4151132A
Cited
US4228050A
Cited
US4280941A
Cited
US4351747A
Cited
US4275100A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-09-18 | 1988-03-19 | 1988-09-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-09-18 | 1992-03-19 | 1992-09-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-09-18 | 1996-03-19 | 1996-09-18 | $7700.00 | Window Closed / Lapsed |