US4472873A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for forming submicron bipolar transistors without epitaxial growth and the resulting structure
Assignee: National Semiconductor Corp
•
Filing: 1981-10-22
•
Granted: 1984-09-25
•
Expires: 2001-10-22
Abstract
Abstract A vertical bipolar transistor is fabricated in a semiconductor substrate without an epitaxial layer using oxide isolation and ion implantation techniques. Ion implantation energies in the KEV ranges are used to implant selected ions into the substrate to form a collector region and buried collector layer less than 1 micron from the surface of the device, and then to form a base region of opposite conductivity type in the collector layer and an emitter region of the first conductivity type in the base region. Even though ion implantation techniques are used to form all regions, the base and the emitter regions can, if desired, be formed to abut the field oxide used to laterally define the islands of semiconductor material. The field oxide is formed to a thickness of less than 1 micron and typically to a thickness of approximately 0.4 microns, thereby substantially reducing the lateral oxidation of the semiconductor silicon islands and making possible devices of extremely small size, typically around 16-18 square microns. During the implantation of channel stop regions between the islands of semiconductor material a thin oxide layer is used to screen the underlying silicon from forming oxidation-induced stacking faults by the subsequent high dose field implantation and oxidation. A nitrogen anneal following this implantation and prior to forming the field oxide further reduces the frequency of stacking faults.
Inventors
- 👤 Wen-Chuang Ko
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 09:11
CPC Classifications
H; H10; H10D; H10D10/00; H10D10/40; H10D10/441; H10W; H10W10/00; H10W10/01; H10W10/011; H10W10/012; H10W10/0121; H10W10/0124; H10W10/0125; H10W10/0126; H10W10/10; H10W10/13
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
133 words
The process of forming a semiconductor structure having a substrate of a first conductivity type comprising: forming a first region of opposite conductivity type in said substrate by ion implanting a selected impurity at a selected dosage into said substrate where the energy used for said ion implanting is selected so that the peak concentration of said impurity in said first region occurs less than 1 micron beneath the surface of said substrate; then, annealing said structure for a selected period of time sufficient to produce a tail portion of said first region extending to the surface of the substrate, said dosage being selected so that the concentration of said impurity in said tail portion at the surface of said substrate after said annealing is sufficient to prevent surface inversion in said structure.
Claim 2
Dependent Claim
133 words
The process of forming a semiconductor structure having a substrate of a first conductivity type comprising: forming a first region of opposite conductivity type in said substrate by ion implanting a selected impurity at a selected dosage into said substrate where the energy used for said ion implanting is selected so that the peak concentration of said impurity in said first region occurs less than 1 micron beneath the surface of said substrate; then, annealing said structure for a selected period of time sufficient to produce a tail portion of said first region extending to the surface of the substrate, said dosage being selected so that the concentration of said impurity in said tail portion at the surface of said substrate after said annealing is sufficient to prevent surface inversion in said structure.
Claim 3
Dependent Claim
10 words
The method of claim 1 wherein said substrate comprises silicon.
Claim 4
Dependent Claim
54 words
The method of claim 2 wherein said selected impurity is phosphorous, said selected dosage is about 1×10 14 ions/cm 2 to 3×10 14 ions/cm 2 and said energy level is approximately 200 KEV, so that the peak concentration of said impurity in said first region is at least about 2×10 18 atoms/cm 3 .
Claim 5
Dependent Claim
33 words
The method of claim 3 wherein the period of time for annealing said structure is selected so that the concentration of said impurity at said surface is approximately 1×10 16 atoms/cm 3 .
Claim 6
Dependent Claim
312 words
The method of claim 1 further comprising: forming grooves of a selected depth in said substrate to leave islands of substrate in which active regions of said structure are to be formed, separated by said grooves; forming a protective layer of material of a selected thickness over the bottom portion of said grooves; implanting ions of said first conductivity type through said protective layer at a dosage of at least 1×10 15 ions/cm 2 , thereby to form second regions of said first conductivity type in said substrate to electrically isolate said first regions of opposite conductivity type in each of said islands from the portions of said first region in the other islands; then, annealing said structure before performing the following oxidizing step; then oxidizing said structure to form an oxide layer over said grooves to a thickness no greater than approximately 1 micron, thereby to minimize the lateral encroachment of said oxide material, where the thickness of said protective layer is selected so that said implanting ions of said first conductivity type, annealing, and then oxidizing said structure does not cause stacking faults in said second regions beneath said grooves; forming a base region of said first conductivity type in said first region by implanting ions of said first conductivity type in said first region; forming an emitter region in said base region by ion implanting an impurity of said second conductivity type into said base region, said emitter region extending into said base region a selected distance less than the depth of base region extending into said first region; forming a collector contact to that portion of said first region in which the base region is not formed; forming insulation over the top surface of each of said islands of semiconductor material and forming contacts to selected portions of said emitter region, said base region and said first region.
Claim 7
Dependent Claim
37 words
The method of claim 5 wherein the base region is formed in said first region such that the base-collector junction of the to-be-formed device in said island is approximately 0.4 microns beneath the surface of said island.
Claim 8
Dependent Claim
30 words
The method of claim 6 wherein the emitter region is formed in said base region such that the emitter-base junction is approximately 0.2 microns beneath the surface of said island.
Claim 9
Dependent Claim
25 words
The method of claim 5 wherein the implantation of ions of said first conductivity type is accomplished using energy of approximately 10 to 50 KEV.
Claim 10
Dependent Claim
14 words
The method of claim 5 wherein said protective layer comprises an oxide of silicon.
Claim 11
Dependent Claim
23 words
The Method of claim 9 wherein said oxide of silicon comprises silicon dioxide formed by thermally oxidizing the surface of said silicon material.
Claim 12
Dependent Claim
16 words
The Method of claim 9 wherein said silicon dioxide layer has a thickness of 200-300 Å.
Claim 13
Dependent Claim
16 words
The Method of claim 11 wherein said silicon dioxide layer has a thickness of 270 Å.
Claim 14
Independent Claim
130 words
The method of forming a channel stopper in a semiconductor structure containing a substrate which comprises: forming a protective layer of material of a selected thickness over a portion of said substrate; implanting ions through said protective layer using a dosage of at least 1×10 15 ions/cm 2 to form a channel stop region in said substrate beneath said protective layer; then annealing said structure before the following oxidizing step; then, oxidizing said structure to form an oxide layer over said portion of said substrate to a thickness no greater than approximately 1 micron, thereby to minimize the lateral encroachment of said oxide material, where the thickness of said protective layer is selected so that said implanting, annealing, and oxidizing does not cause stacking faults in said channel stop region.
Claim 15
Independent Claim
130 words
The method of forming a channel stopper in a semiconductor structure containing a substrate which comprises: forming a protective layer of material of a selected thickness over a portion of said substrate; implanting ions through said protective layer using a dosage of at least 1×10 15 ions/cm 2 to form a channel stop region in said substrate beneath said protective layer; then annealing said structure before the following oxidizing step; then, oxidizing said structure to form an oxide layer over said portion of said substrate to a thickness no greater than approximately 1 micron, thereby to minimize the lateral encroachment of said oxide material, where the thickness of said protective layer is selected so that said implanting, annealing, and oxidizing does not cause stacking faults in said channel stop region.
Claim 16
Dependent Claim
17 words
The Method of claim 13 wherein said portion of said substrate is a groove in said substrate.
Claim 17
Dependent Claim
19 words
The Method of claim 14 wherein said substrate comprises silicon, and said protective layer comprises an oxide of silicon.
Claim 18
Dependent Claim
13 words
The Method of claim 15 wherein said annealing is carried out in nitrogen.
Claim 19
Dependent Claim
19 words
The Method of claim 15 wherein said oxide of silicon has a thickness of 200 Å to 300 Å.
Claim 20
Dependent Claim
17 words
The Method of claim 15 wherein said oxide of silicon comprises a thermally grown oxide of silicon.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-09-25 | 1988-03-26 | 1988-09-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-09-25 | 1992-03-26 | 1992-09-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-09-25 | 1996-03-26 | 1996-09-25 | $7700.00 | Window Closed / Lapsed |