Multilayer glass structure
Assignee: Mizusawa Industrial Chemicals Ltd
•
Filing: 1982-06-22
•
Granted: 1984-10-09
•
Expires: 2002-06-22
Abstract
Abstract A multilayer glass structure constructed by joining the edge portions of a plurality of glass sheets by a sealant through spacers having an adsorbent filled therein. According to this invention, the adsorbent comprises a combination of a granular zeolite composed of a core of a synthetic zeolite/clay binder mixture containing the synthetic zeolite in an amount larger than its average content in the granular zeolite and a shell of a synthetic zeolite/clay binder mixture containing the clay in an amount larger than its average content in the granular zeolite, with granular activated carbon having on its surface 1 to 20% by weight, based on the activated carbon, of a coating of a synthetic resin latex. The adsorbent can effectively adsorb water vapor and the vapor of an organic solvent evaporated from the sealant, and prevent dew deposition on the glass surface. Moreover, it does not yield dust even when the glass structure is handled under severe conditions.
Inventors
- 👤 Hiroshi Nishino
- 👤 Fumiichi Ogino
- 👤 Tetsuo Masuko
- 👤 Kunio Goto
- 👤 Masao Takahashi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 20:04
CPC Classifications
B; B01; B01J; B01J20/00; B01J20/28; B01J20/28014; B01J20/28016; B01J20/28019; E; E06; E06B; E06B3/00; E06B3/04; E06B3/06; E06B3/24; B01J20/02; B01J20/10; B01J20/12; B01J20/16; B01J20/18; B01J20/20; B01J20/28002; B01J20/28004; B01J20/2803; B01J20/28054; B01J20/28057; B01J20/30; B01J20/3042; B01J20/32; B01J20/3202; B01J20/3204; B01J20/3231; B01J20/3234; B01J20/3238; B01J20/3242; B01J20/3268; B01J20/327; B01J20/3276; B01J20/3291; B01J20/3293; E06B3/66; E06B3/677; B01J2220/00; B01J2220/40; B01J2220/42; B01J2220/46; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2982; Y10T428/2991; Y10T428/2993; Y10T428/2998
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
243 words
A multilayer glass structure consisting of a plurality of glass sheets joined at their edge portions through spacers and sealed by a sealant between their edge portions and the outer surfaces of the spacers, that spacer which is located in at least one side of the glass sheets having an adsorbent filled therein; characterized in that said adsorbent comprises a combination of (1) a granular zeolite composed of a core of a synthetic zeolite/clay binder mixture containing the synthetic zeolite in an amount larger than its average content in the granular zeolite and a shell of a synthetic zeolite/clay binder mixture containing the clay binder in an amount larger than its average content in the granular zeolite, the core and the shell in said granular zeolite existing in a weight ratio of from 99:1 to 80:20, the core of said granular zeolite containing said synthetic zeolite and said clay binder in a weight ratio of from 90:10 to 60:40, the shell of said granular zeolite containing said clay binder and said synthetic zeolite in a weight ratio of from 95:5 to 30:70, said shell containing the clay binder in an amount at least 10% larger than the amount of the clay binder in said core, said core and shell being calcined to harden the clay binder, with (2) granular activated carbon having on its surface 1 to 20% by weight, based on the activated carbon, of a coating of a synthetic resin latex.
Claim 2
Dependent Claim
243 words
A multilayer glass structure consisting of a plurality of glass sheets joined at their edge portions through spacers and sealed by a sealant between their edge portions and the outer surfaces of the spacers, that spacer which is located in at least one side of the glass sheets having an adsorbent filled therein; characterized in that said adsorbent comprises a combination of (1) a granular zeolite composed of a core of a synthetic zeolite/clay binder mixture containing the synthetic zeolite in an amount larger than its average content in the granular zeolite and a shell of a synthetic zeolite/clay binder mixture containing the clay binder in an amount larger than its average content in the granular zeolite, the core and the shell in said granular zeolite existing in a weight ratio of from 99:1 to 80:20, the core of said granular zeolite containing said synthetic zeolite and said clay binder in a weight ratio of from 90:10 to 60:40, the shell of said granular zeolite containing said clay binder and said synthetic zeolite in a weight ratio of from 95:5 to 30:70, said shell containing the clay binder in an amount at least 10% larger than the amount of the clay binder in said core, said core and shell being calcined to harden the clay binder, with (2) granular activated carbon having on its surface 1 to 20% by weight, based on the activated carbon, of a coating of a synthetic resin latex.
Claim 3
Dependent Claim
26 words
The structure of claim 1 wherein said granular synthetic zeolite and said granular activated carbon are present in a weight ratio of from 95:5 to 30:70.
Claim 4
Dependent Claim
35 words
The structure of claim 2 or 1 wherein said adsorbent further comprises not more than 70% by weight, based on the total weight of said granular zeolite and granular activated carbon, of granular alumina-silica gel.
Claim 5
Dependent Claim
27 words
The structure of claim 1 wherein the amount of said adsorbent is 20 to 300 g per square meter of the area of the multilayer glass structure.
Claim 6
Dependent Claim
23 words
The structure of claim 1, wherein the synthetic zeolite in said granular zeolite is A-type zeolite, X-type zeolite, Y-type zeolite or synthetic mordenite.
Claim 7
Dependent Claim
28 words
The structure of claim 1 wherein the clay binder in said granular zeolite is a kaolinite-group clay mineral, a palygorskite-group clay mineral, a smectite-group clay mineral, or allophane.
Claim 8
Dependent Claim
28 words
The structure of claim 1 wherein the activated carbon itself in the granular activated carbon has a BET specific surface area of 500 to 2,000 m 2 /g.
Claim 9
Dependent Claim
22 words
The structure of claim 1 wherein the coating of the granular activated carbon is applied in the form of an aqueous emulsion.
Claim 10
Dependent Claim
205 words
An adsorbent for multilayer glass structures said adsorbent comprising a combination of (a) a granular zeolite composed of a core of a synthetic zeolite/clay binder mixture containing the synthetic zeolite in an amount larger than its average content in the granular zeolite and a shell of a synthetic zeolite/clay binder mixture containing the clay binder in an amount larger than its average content in the granular zeolite, the core and the shell in said granular zeolite existing in a weight ratio of from 99:1 to 80:20, the core of said granular zeolite containing said synthetic zeolite and said clay binder in a weight ratio of from 90:10 to 60:40, the shell of said granular zeolite containing said clay binder and said synthetic zeolite in a weight ratio of from 95:5 to 30:70, said shell containing the clay binder in an amount at least 10% larger than the amount of the clay binder in said core, said core and shell being calcined to harden the clay binder, and (b) granular activated carbon having at its surface 1 to 20% by weight, based on the activated carbon, of a coating of a synthetic resin latex, the weight ratio of (a) to (b) being from 80:20 to 50:50.
Claim 11
Dependent Claim
205 words
An adsorbent for multilayer glass structures said adsorbent comprising a combination of (a) a granular zeolite composed of a core of a synthetic zeolite/clay binder mixture containing the synthetic zeolite in an amount larger than its average content in the granular zeolite and a shell of a synthetic zeolite/clay binder mixture containing the clay binder in an amount larger than its average content in the granular zeolite, the core and the shell in said granular zeolite existing in a weight ratio of from 99:1 to 80:20, the core of said granular zeolite containing said synthetic zeolite and said clay binder in a weight ratio of from 90:10 to 60:40, the shell of said granular zeolite containing said clay binder and said synthetic zeolite in a weight ratio of from 95:5 to 30:70, said shell containing the clay binder in an amount at least 10% larger than the amount of the clay binder in said core, said core and shell being calcined to harden the clay binder, and (b) granular activated carbon having at its surface 1 to 20% by weight, based on the activated carbon, of a coating of a synthetic resin latex, the weight ratio of (a) to (b) being from 80:20 to 50:50.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-10-09 | 1988-04-09 | 1988-10-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-10-09 | 1992-04-09 | 1992-10-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-10-09 | 1996-04-09 | 1996-10-09 | $7700.00 | Window Closed / Lapsed |