US4482444A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for electrochemically modifying electrochemically roughened aluminum support materials and the use of these materials in the manufacture of offset printing plates
Assignee: Hoechst AG
•
Filing: 1983-06-16
•
Granted: 1984-11-13
•
Expires: 2003-06-16
Abstract
Abstract This invention pertains to a process for electrochemically modifying electrochemically roughened aluminum or aluminum alloy-based support materials for printing plates. An aluminum or aluminum alloy-based support material is electrochemically roughened using alternating current in an electrolyte containing at least one from the group consisting of hydrochloric acid and nitric acid. Subsequently, at least one surface of the material is treated in an aqueous electrolyte, with the roughened material being made the cathode. The cathodic treatment results in removal of material from the surface in the order of from 0.1 to 10 g/m 2 , and is carried out in an aqueous electrolyte which has a pH value in the range from 3 to 11 and includes at least one water-soluble salt in a concentration ranging from 5 g/l up to the saturation limit thereof. The cathodic treatment is appropriately conducted using direct current at a current density from 3 to 100 A/dm 2 , at a temperature from 15° to 90° C., and for a duration from 5 to 90 seconds. The removal of material is optionally followed by an anodic oxidation of the support material and a hydrophilizing post-treatment of the oxide layer. Support materials which have been prepared in this manner are used in the manufacture of offset printing plates carrying a radiation-sensitive coating.
Inventors
- 👤 Werner Frass
- 👤 Dieter Mohr
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 07:47
CPC Classifications
C; C25; C25F; C25F3/00; C25F3/02; C25F3/04; B; B41; B41N; B41N3/00; B41N3/03; B41N3/034; Y; Y10; Y10S; Y10S204/00; Y10S204/08
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
187 words
A process for electrochemically modifying at least one surface of electrochemically roughened aluminum or aluminum alloy-based support materials for printing plates in an aqueous electrolyte, comprising the steps of: (a) using alternating current to electrochemically roughen an aluminum or aluminum alloy-based support in an aqueous electrolyte containing at least one from the group consisting of hydrochloric acid and nitric acid, and (b) after step (a), subjecting said support as a cathode to direct current in an aqueous electrolyte which has a pH value in the range of 3 to 11 and which consists essentially of at least one water-soluble salt selected from the group consisting of an alkali metal salt and an alkaline earth metal salt of: (i) a hydrohalogenic acid, (ii) an oxo-acid or halogen, carbon, boron, nitrogen or sulfur, or (iii) a fluorine-containing acid of boron, silicon or sulfur, said water-soluble salt being present in a concentration ranging from about 5 g/l up to the saturation limit of said salt, so as to electrochemically remove from the surface of said support an amount of material ranging between about 0.1 and about 10 g/m 2 .
Claim 2
Dependent Claim
187 words
A process for electrochemically modifying at least one surface of electrochemically roughened aluminum or aluminum alloy-based support materials for printing plates in an aqueous electrolyte, comprising the steps of: (a) using alternating current to electrochemically roughen an aluminum or aluminum alloy-based support in an aqueous electrolyte containing at least one from the group consisting of hydrochloric acid and nitric acid, and (b) after step (a), subjecting said support as a cathode to direct current in an aqueous electrolyte which has a pH value in the range of 3 to 11 and which consists essentially of at least one water-soluble salt selected from the group consisting of an alkali metal salt and an alkaline earth metal salt of: (i) a hydrohalogenic acid, (ii) an oxo-acid or halogen, carbon, boron, nitrogen or sulfur, or (iii) a fluorine-containing acid of boron, silicon or sulfur, said water-soluble salt being present in a concentration ranging from about 5 g/l up to the saturation limit of said salt, so as to electrochemically remove from the surface of said support an amount of material ranging between about 0.1 and about 10 g/m 2 .
Claim 3
Dependent Claim
25 words
A process as claimed in claim 1, wherein said aqueous electrolyte in step (b) has a pH value in the range of 5 to 9.
Claim 4
Dependent Claim
30 words
A process as claimed in claim 1, wherein said amount of material electrochemically removed from the surface of said support ranges from about 0.5 to about 5 g/m 2 .
Claim 5
Dependent Claim
26 words
A process as claimed in claim 1, wherein said aqueous electrolyte in step (b) conains between about 10 and about 250 g/l of said water-soluble salt.
Claim 6
Dependent Claim
44 words
A process as claimed in claim 1, wherein step (b) is carried out using direct current at a current density from 3 to 100 A/dm 2 , at a temperature from 15° to 90° C., and for a duration of 5 to 90 seconds.
Claim 7
Dependent Claim
47 words
A process as claimed in claim 1, wherein step (b) is carried out at a current density ranging between about 10 and about 80 A/dm 2 , at a temperature of about 20° to 40° C., and for a duration of about 10 to about 60 seconds.
Claim 8
Dependent Claim
29 words
A process as claimed in claim 1, wherein the support is anodically oxidized, in an aqueous electrolyte containing sulfuric acid and/or phosphoric acid, using direct current, after step (b).
Claim 9
Dependent Claim
22 words
A process as claimed in claim 7, wherein the anodically oxidized support materials for printing plates are subjected to a hydrophilizing post-treatment.
Claim 10
Dependent Claim
33 words
A process as claimed in claim 1, wherein the mean peak-to-valley roughness of said support after electrochemical roughening during step (a) is in the range of from about 1 to about 15 μm.
Claim 11
Dependent Claim
175 words
An offset printing plate comprising: (a) a support material produced by: (i) electrochemically roughening an aluminum or aluminum alloy-based support using alternating current in an aqueous electrolyte containing at least one from the group consisting of hydrochloric acid and nitric acid; and, thereafter, (i) subjecting said support as a cathode to direct current in an aqueous electrolyte which has a pH value in the range of 3 to 11 and which consists essentially of at least one water-soluble salt selected from the group consisting of an alkali metal salt and an alkaline earth metal salt of (i) a hydrohalogenic acid, (ii) an oxo-acid of halogen, carbon, boron, nitrogen or sulfur, or (iii) a fluorine-containing acid of boron, silicon or sulfur, said water-soluble salt being present in a concentration ranging from about 5 g/l up to the saturation limit of said salt, so as to electrochemically remove from the surface of said support an amount of material ranging between about 0.1 and about 10 g/m 2 ; and (b) a radiation-sensitive coating on said support material.
Claim 12
Dependent Claim
175 words
An offset printing plate comprising: (a) a support material produced by: (i) electrochemically roughening an aluminum or aluminum alloy-based support using alternating current in an aqueous electrolyte containing at least one from the group consisting of hydrochloric acid and nitric acid; and, thereafter, (i) subjecting said support as a cathode to direct current in an aqueous electrolyte which has a pH value in the range of 3 to 11 and which consists essentially of at least one water-soluble salt selected from the group consisting of an alkali metal salt and an alkaline earth metal salt of (i) a hydrohalogenic acid, (ii) an oxo-acid of halogen, carbon, boron, nitrogen or sulfur, or (iii) a fluorine-containing acid of boron, silicon or sulfur, said water-soluble salt being present in a concentration ranging from about 5 g/l up to the saturation limit of said salt, so as to electrochemically remove from the surface of said support an amount of material ranging between about 0.1 and about 10 g/m 2 ; and (b) a radiation-sensitive coating on said support material.
References Cited (Backward Citations)
US3160506A
Cited
DE2250275A1
Cited
DE2420704A1
Cited
US3929591A
Cited
US3935080A
Cited
DE2557222A1
Cited
DE2537725A1
Cited
DE2537724A1
Cited
JPS5615396A
Cited
US4242417A
Cited
US4324841A
Cited
DE3036174A1
Cited
DE3009103A1
Cited
DE3127329A1
Cited
US4437955A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-11-13 | 1988-05-14 | 1988-11-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-11-13 | 1992-05-14 | 1992-11-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-11-13 | 1996-05-14 | 1996-11-13 | $7700.00 | Window Closed / Lapsed |