Ion implant mask and cap for gallium arsenide structures
Assignee: Westinghouse Electric Corp
•
Filing: 1983-06-15
•
Granted: 1985-01-22
•
Expires: 2003-06-15
Abstract
Abstract A mask and encapsulating layer suitable for use on gallium arsenide substrates is described incorporating a layer of germanium selenide which is photosensitive and may be exposed and developed to form a mask suitable for ion implantation and which may also remain as a capping layer during an anneal process of ion implanted regions in a controlled atmosphere and temperature furnace wherein the layer of germanium selenide is converted to germanium which may subsequently be removed from the gallium arsenide substrate after the step of annealing.
Inventors
- 👤 Zachary J. Lemnios
- 👤 He B. Kim
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 04:43
CPC Classifications
H; H10; H10P; H10P30/00; H10P30/20; H10P30/22; H10P14/00; H10P14/60; H10P30/202; H10P30/206; H10P30/208; H10P30/21; H10P30/212; H10P30/214; H10P30/28; H10P95/00; H10P95/90; H10P95/904
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
108 words
A method for fabricating doped regions in a gallium arsenide substrate comprising the steps of depositing a layer of germanium selenide over a substrate of gallium arsenide, exposing the layer of germanium selenide to a predetermined pattern, developing the exposed layer of germanium selenide to provide openings in the layer of germanium selenide, ion implanting impurities through said openings to form first ion implanted regions, ion implanting impurities of a second concentration through the layer of germanium selenide to form second ion implanted regions, annealing first and second ion implanted regions, converting the layer of germanium selenide to a layer of germanium, and removing the layer of germanium.
Claim 2
Independent Claim
108 words
A method for fabricating doped regions in a gallium arsenide substrate comprising the steps of depositing a layer of germanium selenide over a substrate of gallium arsenide, exposing the layer of germanium selenide to a predetermined pattern, developing the exposed layer of germanium selenide to provide openings in the layer of germanium selenide, ion implanting impurities through said openings to form first ion implanted regions, ion implanting impurities of a second concentration through the layer of germanium selenide to form second ion implanted regions, annealing first and second ion implanted regions, converting the layer of germanium selenide to a layer of germanium, and removing the layer of germanium.
Claim 3
Dependent Claim
28 words
The method of claim 1 wherein the step of annealing further includes raising the temperature of said gallium arsenide substrate and said germanium selenide layer to 850° C.
Claim 4
Dependent Claim
26 words
The method of claim 1 wherein said step of annealing further includes annealing in a controlled atmosphere wherein said atmosphere includes a predetermined arsenic vapor pressure.
Claim 5
Dependent Claim
39 words
The method of claim 1 wherein said step of converting said layer of germanium selenide to germanium includes heating said layer of germanium selenide to a temperature to permit substantial evaporation of selenium from the layer of germanium selenide.
Claim 6
Dependent Claim
18 words
The method of claim 1 further including the step of forming ohmic contacts to selected ion implanted regions.
References Cited (Backward Citations)
US4267014A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-01-22 | 1988-07-23 | 1989-01-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-01-22 | 1992-07-23 | 1993-01-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-01-22 | 1996-07-23 | 1997-01-22 | $7700.00 | Window Closed / Lapsed |