Casting plastic lenses from thermohardening monomer with compensation for polymer expansion and shrinkage

Claim 2

A process of continuous compensation casting a lens of a resinous thermohardening plastics material, said process comprising the steps of:

Claim 3

(1) forming a tubular sleeve of a substantially nondeformable plastic material which is chemically compatible with the thermohardening plastics resin and which sleeve is thermally stable at polymerization temperatures; (2) positioning two mold halves within said sleeve at a predetermined distance apart from each other defining, together with the adjacent internal lateral wall of the sleeve between the two mold halves, a cavity with a diameter the same as each of the mold halves, each mold half retained in position within the sleeve by friction between the mold half rim and the adjacent sleeve wall with which it is in contact; (3) providing a compensation reservoir external of the cavity and in fluid communication therewith through at least one preformed passageway therebetween; (4) introducing a flowable, catalyst-containing thermohardening, homogeneously-polymerizing monomer into the cavity via the preformed passageway and completely filling the cavity, the compensation reservoir and the preformed passageway therebetween; (5) heating the thus formed and filled mold assembly for a period of time to initiate polymerization of the thermohardening monomer, wherein initially the monomer so heated expands and flows from the cavity to the compensation reservoir, then later during the polymerization the polymerizing monomer contracts and flows from the compensation reservoir into the cavity as required to compensate for monomer shrinkage within the mold, until the gel stage is reached, the heating being continued until the gel stage of polymerization is reached and flow between the compensation reservoir and the cavity stops; (6) continuing the heating of the mold assembly until the monomer is completely polymerized, while concurrently moving the mold halves towards each other as required to compensate for the continuing shrinkage of the polymerizing monomer, the shrinkage of the monomer under polymerization from the gel stage to final polymerization being solely compensated by moving the mold halves towards each other; and thereafter (7) removing the two mold halves from the so produced lens when polymerization of the monomer is completed.

Claim 4

(1) forming a tubular sleeve of a substantially nondeformable plastic material which is chemically compatible with the thermohardening plastics resin and which sleeve is thermally stable at polymerization temperatures; (2) positioning two mold halves within said sleeve at a predetermined distance apart from each other defining, together with the adjacent internal lateral wall of the sleeve between the two mold halves, a cavity with a diameter the same as each of the mold halves, each mold half retained in position within the sleeve by friction between the mold half rim and the adjacent sleeve wall with which it is in contact; (3) providing a compensation reservoir external of the cavity and in fluid communication therewith through at least one preformed passageway therebetween; (4) introducing a flowable, catalyst-containing thermohardening, homogeneously-polymerizing monomer into the cavity via the preformed passageway and completely filling the cavity, the compensation reservoir and the preformed passageway therebetween; (5) heating the thus formed and filled mold assembly for a period of time to initiate polymerization of the thermohardening monomer, wherein initially the monomer so heated expands and flows from the cavity to the compensation reservoir, then later during the polymerization the polymerizing monomer contracts and flows from the compensation reservoir into the cavity as required to compensate for monomer shrinkage within the mold, until the gel stage is reached, the heating being continued until the gel stage of polymerization is reached and flow between the compensation reservoir and the cavity stops; (6) continuing the heating of the mold assembly until the monomer is completely polymerized, while concurrently moving the mold halves towards each other as required to compensate for the continuing shrinkage of the polymerizing monomer, the shrinkage of the monomer under polymerization from the gel stage to final polymerization being solely compensated by moving the mold halves towards each other; and thereafter (7) removing the two mold halves from the so produced lens when polymerization of the monomer is completed.

Claim 5

The process in accordance with claim 1 wherein said monomer is diethyleneglycol-bis-allyl-carbonate.

Claim 6

The process in accordance with claim 1 wherein said monomer is diethyleneglycol-bis-allyl-carbonate and copolymers thereof.

Claim 7

The process in accordance with claim 1, 2 or 3 wherein the monomer is diethylene-glycol-bis-allyl-carbonate catalyzed with isopropyl dicarbonate-peroxide.

Claim 8

The process in accordance with claim 1, 2 or 3 wherein said monomer is catalyzed with isopropyl dicarbonateperoxide and also contains 2-(2-hydroxy-5-methyl-phenyl)benzotriazole as an U.V. absorber.

Claim 9

The process in accordance with claim 1 wherein the catalyzed monomer is heated during the total of steps (5) and (6) for a period of 15 hours during which time the temperature gradually increases from about +40° C. to about 110° C.

Claim 10

The process in accordance with claim 1 wherein the compensation reservoir is integral with a portion of the tubular sleeve.

Claim 11

The process in accordance with claim 1 wherein the compensation reservoir is placed adjacent to the exterior of the tubular sleeve in a position corresponding to the cavity as defined by the two mold halves.

Claim 12

The process in accordance with claim 1 wherein the compensation reservoir is contained within the tubular sleeve above the upper mold half.

Claim 13

The process in accordance with claim 1 wherein after the gel stage of the monomer has been reached in step (5), compression springs are applied to the two mold halves prior to step (6) and remain in place during the heating of step (6).

Claim 14

The process in accordance with claim 1 or 10, wherein the compression springs applied to the mold include at least one meniscus-shaped contact saucer around an articulation pin.

Claim 15

The process in accordance with claim 1 wherein the lens is removed from the mold halves in step (7) by immersing in a warm water bath and subjecting the assembly to ultrasonic frequencies between 20 and 70 KHz.

Claim 16

The process in accordance with claim 12, wherein the water bath is an aqueous solution of a surfactant.