Porous aromatic imide polymer membrane and a process for its manufacture
Assignee: Ube Corp
•
Filing: 1982-04-13
•
Granted: 1985-04-23
•
Expires: 2002-04-13
Abstract
Abstract A porous aromatic imide polymer membrane usable as a gas or liquid separator or concentrator is prepared by a process comprising the steps of: (1) dissolving 3 to 30% by weight of an aromatic imide polymer which comprises at least 80 molar % of a recurring unit selected from those of the formulae (I) and (II): <IMAGE> (I) and <IMAGE> (II) wherein R represents a divalent aromatic or heterocyclic radical in 70 to 97% by weight of a solvent consisting essentially of a homogeneous mixture of: (A) 100 parts by weight of a base solvent which consists essentially of at least one polar organic compound and is capable of dissolving therein said aromatic imide polymer in a concentration of 5% by weight or more therein and of evaporating at a temperature of from 50 DEG to 400 DEG C., and (B) 5 to 150 parts by weight of an additional liquid which consists essentially of at least one polar organic compound, is incapable of dissolving therein 3% by weight or more of said aromatic imide polymer and is capable of evaporating at a smaller evaporating rate than that of said base solvent at the above-mentioned evaporating temperature so as to provide a dope solution: (2) forming a thin layer of the dope solution; and (3) heating the thin layer of the dope solution at a temperature of from 50 DEG to 400 DEG C., whereby said mixed solvent is gradually evaporated from the thin layer of the dope solution.
Inventors
- 👤 Hiroshi Makino
- 👤 Yoshihiro Kusuki
- 👤 Takashi Harada
- 👤 Hiroshi Shimazaki
- 👤 Tosio Isida
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 14:43
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/28; B; B01; B01D; B01D71/00; B01D71/06; B01D71/58; B01D71/62; B01D71/64; C08G; C08G73/00; C08G73/06; C08G73/10; C08G73/14; C08J2379/00; C08J2379/04; C08J2379/08; Y; Y10; Y10S; Y10S55/00; Y10S55/05
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
259 words
A process for producing a porous aromatic imide polymer membrane, comprising the steps of: (1) dissolving 3 to 30% by weight of an aromatic imide copolymer which has a degree of imidization of at least 90% and comprises at least 80 molar % of at least one type of recurring unit selected from the group consisting of those of the formulae (I) and (II): ##STR9## wherein R represents a member selected from divalent aromatic radicals, in 70 to 97% by weight of a solvent consisting essentially of a homogeneous mixture of: (A) 100 parts by weight of a base solvent consisting essentially of at least one polar organic compound, which base solvent is capable of dissolving therein said aromatic imide polymer in a concentration of 5% by weight of more therein and of evaporating at a temperature of from 50° to 400° C., and (B) 5 to 150 parts by weight of an additional liquid consisting essentially of at least one polar organic compound, which additional liquid is incapable of dissolving therein 3% by weight or more of said aromatic imide polymer and is capable of evaporating at a smaller evaporating rate than that of said base solvent at the above-mentioned evaporating temperature so as to provide a dope solution; (2) forming a thin layer of said dope solution; and (3) gradually and completely removing said solvent from said thin layer of said dope solution by means of a dry-evaporating method at a temperature of from 50° C. to 400° C., to form a porous aromatic imide polymer membrane.
Claim 2
Dependent Claim
259 words
A process for producing a porous aromatic imide polymer membrane, comprising the steps of: (1) dissolving 3 to 30% by weight of an aromatic imide copolymer which has a degree of imidization of at least 90% and comprises at least 80 molar % of at least one type of recurring unit selected from the group consisting of those of the formulae (I) and (II): ##STR9## wherein R represents a member selected from divalent aromatic radicals, in 70 to 97% by weight of a solvent consisting essentially of a homogeneous mixture of: (A) 100 parts by weight of a base solvent consisting essentially of at least one polar organic compound, which base solvent is capable of dissolving therein said aromatic imide polymer in a concentration of 5% by weight of more therein and of evaporating at a temperature of from 50° to 400° C., and (B) 5 to 150 parts by weight of an additional liquid consisting essentially of at least one polar organic compound, which additional liquid is incapable of dissolving therein 3% by weight or more of said aromatic imide polymer and is capable of evaporating at a smaller evaporating rate than that of said base solvent at the above-mentioned evaporating temperature so as to provide a dope solution; (2) forming a thin layer of said dope solution; and (3) gradually and completely removing said solvent from said thin layer of said dope solution by means of a dry-evaporating method at a temperature of from 50° C. to 400° C., to form a porous aromatic imide polymer membrane.
Claim 3
Dependent Claim
58 words
The process as claimed in claim 1, wherein said aromatic imide polymer exhibits a logarithmic viscosity of from 0.3 to 7.0 determined at a concentration of 0.5 g per 100 ml of a solvent consisting of a mixture of four parts by volume of p-chlorophenol and one part by volume of o-chlorophenol at a temperature of 30° C.
Claim 4
Dependent Claim
39 words
The process as claimed in claim 1, wherein said aromatic imide polymer comprises at least 90 molar % of at least one type of recurring unit selected from the group consisting of those of the formulae (I) and (II).
Claim 5
Dependent Claim
115 words
The process as claimed in claim 1, wherein in said formulae (I) and (II), R represents a member selected from the group consisting of divalent radicals of the formulae ##STR10## wherein R 1 , R 2 , and R 3 , respectively, represent, independently from each other, a member selected from the group consisting of a hydrogen atom, lower alkyl radicals having 1 to 3 carbon atoms, and lower alkoxyl radicals having 1 to 3 carbon atoms; A represents a divalent linking member selected from the class consisting of --O--, --S--, --CO--, --SO 2 --, --SO--, --CH 2 --, and --C(CH 3 ) 2 --; and m represents an integer of from 1 to 4.
Claim 6
Dependent Claim
42 words
The process as claimed in claim 1, wherein said base solvent consists essentially of at least one phenolic compound having a melting point of approximately 100° C. or less and a boiling point of approximately 300° C. or less under atmospheric pressure.
Claim 7
Dependent Claim
28 words
The process as claimed in claim 5, wherein said phenolic compound is selected from the group consisting of phenol, alkyl-substituted monohydric phenol compounds, and halogenated monohydric phenol compounds.
Claim 8
Dependent Claim
28 words
The process as claimed in claim 6, wherein said alkyl-substituted monohydric phenol compound is selected from the group consisting of o-, m-, and p-cresols, 3,5-xylenol, carvacrol, and thymol.
Claim 9
Dependent Claim
55 words
The process as claimed in claim 6, wherein said halogenated monohydric phenol compound is selected from the group consisting of those of the formula ##STR11## wherein R 4 represents a member selected from the group consisting of a hydrogen atom and alkyl radicals having 1 to 3 carbon atoms and X represents a halogen atom.
Claim 10
Dependent Claim
72 words
The process as claimed in claim 1, wherein said porous aromatic imide polymer membrane exhibits a hydrogen gas-permeating rate (P H2 ) of 1.0 to 10 -2 to 1.6×10 -4 cm 3 /cm 2 .sec.cmHg and a ratio (P H2 /P CO ) of the hydrogen gas-permeating rate (P H2 ) to carbon monoxide gas-permeating rate (P CO ) of from 2.6 to 3.5 under a pressure of 3.0 kg/cm 2 G.
Claim 11
Dependent Claim
38 words
The process as claimed in claim 1, wherein said additional liquid consists of at least one member selected from the group consisting essentially of phenanthrene, o-terphenyl, p-terphenyl, α-chloronaphthalene, triphenylphosphine, triphenylamine, aniline, naphthalene, 1-methylnaphthalene, 2-methylnaphthalene, dimethylnaphthalene, anthracene, and 1,2-benzanthracene.
Claim 12
Dependent Claim
26 words
The process as claimed in claim 1, wherein said thin layer-forming procedure is carried out at a temperature of from approximately 50° C. to 180° C.
Claim 13
Dependent Claim
53 words
The process as claimed in claim 11, wherein said heating procedure is carried out firstly at a temperature of from 50° to 150° C., secondly at a temperature of from 30° to 80° C. above the first temperature, and finally at a temperature of from 30° to 80° C. above the second temperature.
Claim 14
Dependent Claim
25 words
The process as claimed in claim 1, wherein said dope solution exhibits a rotation viscosity of at least 500 centi-poises at the thin layer-forming temperature.
Claim 15
Dependent Claim
15 words
A porous aromatic imide polymer membrane prepared by the process as claimed in claim 1.
References Cited (Backward Citations)
US3692740A
Cited
US3862897A
Cited
US3708458A
Cited
US3985934A
Cited
US4214071A
Cited
US4290936A
Cited
US4284594A
Cited
US4385084A
Cited
US4307135A
Cited
US4370290A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-04-22 | 1988-10-22 | 1989-04-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-04-22 | 1992-10-22 | 1993-04-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-04-22 | 1996-10-22 | 1997-04-23 | $7700.00 | Window Closed / Lapsed |