Low density nonwoven sheets
Assignee: EIDP Inc
•
Filing: 1982-08-09
•
Granted: 1985-05-07
•
Expires: 2002-08-09
Abstract
Abstract Coherent expanded nonwoven sheets having a density of less than 0.16 g/mL are comprised of fibrids of a wholly synthetic polymer, preferably not melting below 130° C., and optionally containing up to 80% by weight floc. The sheet is comprised of a plurality of paper-like membranous layers which join and separate at random throughout the thickness of the sheet to form expanded cells. The expanded nonwoven sheets are prepared by rapid vaporization of water in a wet, never-dried sheet of fibrids containing at least 60% by weight water. Rapid vaporization of the water preferably is induced by dielectric heating. Embossing may be used before or during expansion to produce a sheet which is expanded only in selected areas.
Inventors
- 👤 Wesley Memeger, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 04:44
CPC Classifications
D; D21; D21F; D21F11/00; D21F11/006; D21H; D21H13/00; D21H5/00; D21H5/12; Y; Y10; Y10T; Y10T428/00; Y10T428/23; Y10T428/234; Y10T428/24; Y10T428/24058; Y10T428/24074; Y10T428/24091; Y10T428/24479; Y10T428/24612; Y10T428/24628; Y10T428/24661; Y10T442/00; Y10T442/60
Claims Analysis
Total Claims: 37
Claim 1
Independent Claim
178 words
Process for preparing a coherent expanded adhesive-free wet laid nonwoven sheet comprised of fibrids of a wholly synthetic polymer and optionally up to 80% by weight floc, the sheet having an apparent density of less than 0.16 g/mL and being comprised of a plurality of paper-like layers of membranous elements which join and separate at random throughout the thickness of the sheet to form expanded macroscopic cells, the expanded sheet further comprising up to 50%, based on the total area of the sheet, of discrete areas which are not expanded, the process comprising preparing a wet mixture of fibrids of a wholly synthetic polymer, and optionally up to 80% by weight floc, forming a wet-laid nonwoven sheet of the fibrids on paper-forming equipment, maintaining water in the sheet, adding additional water if needed to increase the water content of the sheet to at least 60% by weight, and heating the wet sheet under such pressure and for such time to vaporize the water rapidly and, simultaneously, to expand the wet-laid nonwoven sheet to provide the aforesaid expanded sheet.
Claim 2
Dependent Claim
178 words
Process for preparing a coherent expanded adhesive-free wet laid nonwoven sheet comprised of fibrids of a wholly synthetic polymer and optionally up to 80% by weight floc, the sheet having an apparent density of less than 0.16 g/mL and being comprised of a plurality of paper-like layers of membranous elements which join and separate at random throughout the thickness of the sheet to form expanded macroscopic cells, the expanded sheet further comprising up to 50%, based on the total area of the sheet, of discrete areas which are not expanded, the process comprising preparing a wet mixture of fibrids of a wholly synthetic polymer, and optionally up to 80% by weight floc, forming a wet-laid nonwoven sheet of the fibrids on paper-forming equipment, maintaining water in the sheet, adding additional water if needed to increase the water content of the sheet to at least 60% by weight, and heating the wet sheet under such pressure and for such time to vaporize the water rapidly and, simultaneously, to expand the wet-laid nonwoven sheet to provide the aforesaid expanded sheet.
Claim 3
Dependent Claim
16 words
Process of claim 1 wherein the water content is maintained at at least 40% by weight.
Claim 4
Dependent Claim
30 words
Process of claim 2 wherein up to 50% of the total area of the sheet is embossed before expansion to provide a sheet which is expanded only in unembossed areas.
Claim 5
Dependent Claim
24 words
Process of claim 2 wherein the wet nonwoven sheet contains 20-80% by weight fibrids and complementally 20-80% by weight floc on a dry basis.
Claim 6
Dependent Claim
23 words
Process of claim 2 wherein the wet nonwoven sheet contains 50-80% by weight fibrids and 20-50% by weight floc on a dry basis.
Claim 7
Dependent Claim
15 words
Process of claim 2 or 3 wherein the fibrids are comprised of an aromatic polyamide.
Claim 8
Dependent Claim
10 words
Process of claim 6 wherein the fibrids are poly(m-phenylene isophthalamide).
Claim 9
Dependent Claim
10 words
Process of claim 2 wherein aromatic polyamide floc is used.
Claim 10
Dependent Claim
10 words
Process of claim 8 wherein poly(m-phenylene isophthalamide) floc is used.
Claim 11
Dependent Claim
10 words
Process of claim 8 wherein poly(p-phenylene terephthalamide) floc is used.
Claim 12
Dependent Claim
11 words
Process of claim 10 wherein the poly(p-phenylene terephthalamide) floc is pulped.
Claim 13
Dependent Claim
18 words
Process of claim 1, 2 or 3 wherein the rapid vaporization of water is induced by dielectric heating.
Claim 14
Dependent Claim
20 words
Process of claim 1 wherein the sheet after expansion is heated at about the glass transition temperature of the fibrids.
Claim 15
Dependent Claim
24 words
Process of claim 2 wherein the sheet is embossed and expanded simultaneously in a single operation to expand only predetermined areas of the sheet.
Claim 16
Dependent Claim
25 words
Process of claim 1, 2 or 3 wherein the wet mixture contains floc and the fibrids comprise more than 30% by weight of the two.
Claim 17
Dependent Claim
93 words
A coherent expanded adhesive-free wet laid nonwoven sheet comprised of fibrids of a wholly synthetic polymer which fibrids form a multiplicity of layered membranous elements which join with and separate from one another at random to form a three-dimensional, highly irregular network of numerous interleaved macroscopic cells with tapered edges positioned substantially throughout the thickness of the expanded sheet, said sheet having an apparent density of less than 0.16 g/mL, the expanded sheet further comprising up to 50%, based on the total area of the sheet, of discrete areas which are not expanded.
Claim 18
Dependent Claim
93 words
A coherent expanded adhesive-free wet laid nonwoven sheet comprised of fibrids of a wholly synthetic polymer which fibrids form a multiplicity of layered membranous elements which join with and separate from one another at random to form a three-dimensional, highly irregular network of numerous interleaved macroscopic cells with tapered edges positioned substantially throughout the thickness of the expanded sheet, said sheet having an apparent density of less than 0.16 g/mL, the expanded sheet further comprising up to 50%, based on the total area of the sheet, of discrete areas which are not expanded.
Claim 19
Dependent Claim
24 words
An expanded wet laid nonwoven sheet of claim 16 comprised of 50-80% by weight fibrids and 20-50% by weight floc based on dry weight.
Claim 20
Dependent Claim
22 words
An expanded wet laid nonwoven sheet of claim 17 wherein both the fibrids and the floc are comprised of an aromatic polyamide.
Claim 21
Dependent Claim
27 words
An expanded wet laid nonwoven sheet of claim 18 wherein the thickness of expanded areas is at least 10 times greater than that of the unexpanded areas.
Claim 22
Dependent Claim
18 words
An expanded wet laid nonwoven sheet of claim 18 having an apparent density of less than 0.10 g/mL.
Claim 23
Dependent Claim
25 words
An expanded nonwoven sheet of claim 16 containing floc mixed with the fibrids and the fibrids comprise more than 30% by weight of the two.
Claim 24
Dependent Claim
17 words
An expanded wet laid nonwoven sheet of claim 16 wherein the fibrids are comprised of polyvinylidene fluoride.
Claim 25
Dependent Claim
14 words
An expanded wet laid nonwoven sheet of claim 22 comprised of floc of poly(tetrafluoroethylene).
Claim 26
Dependent Claim
18 words
An expanded nonwoven sheet of claim 16 or 8 comprising a reinforcing scrim as an integral part thereof.
Claim 27
Dependent Claim
26 words
An expanded wet laid nonwoven sheet of claim 16 containing 20-80% by weight fibrids and complementally 20-80% by weight floc, each not melting below 130° C.
Claim 28
Dependent Claim
18 words
An expanded wet laid nonwoven sheet of claim 16 wherein the fibrids are comprised of an aromatic polyamide.
Claim 29
Dependent Claim
16 words
An expanded wet laid nonwoven sheet of claim 26 wherein the fibrids are of poly(m-phenylene isophthalamide).
Claim 30
Dependent Claim
19 words
An expanded wet laid nonwoven sheet of claim 25 wherein at least some of the floc has been pulped.
Claim 31
Dependent Claim
16 words
An expanded nonwoven sheet of claim 26 containing floc which is comprised of an aromatic polyamide.
Claim 32
Dependent Claim
16 words
An expanded wet laid nonwoven sheet of claim 29 wherein the floc is of poly(m-phenylene isophthalamide).
Claim 33
Dependent Claim
18 words
An expanded wet laid nonwoven sheet of claim 29 wherein the floc is of a crystalline aromatic polyamide.
Claim 34
Dependent Claim
18 words
An expanded wet laid nonwoven sheet of claim 31 wherein the floc is of a crystalline poly(m-phenylene isophthalamide).
Claim 35
Dependent Claim
16 words
An expanded wet laid nonwoven sheet of claim 31 wherein the floc is of poly(p-phenylene terephthalamide).
Claim 36
Dependent Claim
12 words
An expanded nonwoven sheet of claim 27 containing floc of glass fibers.
Claim 37
Dependent Claim
19 words
An expanded wet laid nonwoven sheet of claim 17 which has an apparent density of less than 0.10 g/mL.
References Cited (Backward Citations)
US2999788A
Cited
US3101294A
Cited
US3375156A
Cited
US3759775A
Cited
US3756908A
Cited
US3880705A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-05-06 | 1988-11-05 | 1989-05-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-05-06 | 1992-11-05 | 1993-05-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-05-06 | 1996-11-05 | 1997-05-07 | $7700.00 | Window Closed / Lapsed |