US4523975A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Integrated circuit planarizing process
Assignee: Microsemi Semiconductor ULC
•
Filing: 1982-04-28
•
Granted: 1985-06-18
•
Expires: 2002-04-28
Abstract
Abstract A planarizing process for producing a passivation or insulating layer immediately underlying an upper metallized layer on the surface of an integrated circuit having very large radius of curvature steps, thus providing a reliable base for the metallized layer. The process is comprised of the steps of depositing and defining first metal conductors on the surface of an integrated circuit, depositing a first dielectric layer over the surface of the integrated circuit including the conductors, the dielectric layer being comprised of material selected from the group comprised of silicon dioxide and silicon nitride, depositing and polymerizing a layer of negative isoprene resist over the surface of the dielectric layer, plasma etching the surface of the isoprene and dielectric layers to a predetermined thickness over the metal conductors in an atmosphere of CF 4 gas containing 32 to 50% oxygen, cleaning the etched surface, and depositing a second dielectric layer over the surface selected from a group comprised of silicon dioxide and silicon nitride, whereby a surface having very large radius of curvature steps over the metal conductors is produced.
Inventors
- 👤 Christopher K. Groves
- 👤 Kevin Duncan
- 👤 Edward C. D. Darwall
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 04:41
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/69; H10P14/692; H10P14/6921; H10P14/69215; H10P14/63; H10P14/6326; H10P14/6328; H10P14/6334; H10P14/6336; H10P14/6342; H10P14/66; H10P14/662; H10P14/68; H10P14/683; H10P14/694; H10P14/6943; H10P14/69433; H10P50/00; H10P50/20; H10P50/28; H10P50/282; H10P50/283; H10P95/00; H10P95/06; H10P95/062; H10P95/064; H10W; H10W20/00; H10W20/01; H10W20/071; H10W20/092
Claims Analysis
Total Claims: 46
Claim 1
Independent Claim
164 words
A process for planarizing an integrated circuit comprising: (a) depositing and defining first metal conductors on the surface of an integrated circuit, (b) depositing a first dielectric layer over the surface of the integrated circuit including said conductors, the dielectric layer being comprised of a material selected from the group consisting of silicon dioxide and silicon nitride, (c) depositing and polymerizing a layer of negative isoprene resist over the surface of the dielectric layer, (d) etching the surface of the isoprene and dielectric layers, with an etchant to which the first metal conductors are substantially immune, to a predetermined thickness over the metal conductors, in an atmosphere containing 32 to 50% oxygen in a CF 4 gas in a plasma etcher, (e) cleaning the etched surface, and (f) depositing a second dielectric layer over the surface selected fron the group consisting of silicon dioxide and silicon nitride, whereby a planarized surface having very large radius of curvature steps over the metal conductors is produced.
Claim 2
Dependent Claim
164 words
A process for planarizing an integrated circuit comprising: (a) depositing and defining first metal conductors on the surface of an integrated circuit, (b) depositing a first dielectric layer over the surface of the integrated circuit including said conductors, the dielectric layer being comprised of a material selected from the group consisting of silicon dioxide and silicon nitride, (c) depositing and polymerizing a layer of negative isoprene resist over the surface of the dielectric layer, (d) etching the surface of the isoprene and dielectric layers, with an etchant to which the first metal conductors are substantially immune, to a predetermined thickness over the metal conductors, in an atmosphere containing 32 to 50% oxygen in a CF 4 gas in a plasma etcher, (e) cleaning the etched surface, and (f) depositing a second dielectric layer over the surface selected fron the group consisting of silicon dioxide and silicon nitride, whereby a planarized surface having very large radius of curvature steps over the metal conductors is produced.
Claim 3
Dependent Claim
26 words
A process as defined in claim 1, including the further step of depositing and defining second metal conductors on the surface of the second dielectric layer.
Claim 4
Dependent Claim
21 words
A process as defined in claim 1 in which at least the second dielectric layer is composed of undoped silicon dioxide.
Claim 5
Dependent Claim
21 words
A process as defined in claim 1, in which the metal conductors are comprised of an alloy of aluminum and silicon.
Claim 6
Dependent Claim
20 words
A process as defined in claim 1, 2 or 3 in which the negative isoprene resist is a cis polyisoprene.
Claim 7
Dependent Claim
21 words
A process as defined in claim 1, 2 or 3 in which the negative isoprene resist is a negative type photoresist.
Claim 8
Dependent Claim
20 words
A process as defined in claim 1, 2 or 3 in which the first metal conductors are comprised of aluminum.
Claim 9
Dependent Claim
33 words
A process as defined in claim 1, 2 or 3 in which the first metal conductors are composed of aluminum or an alloy of aluminum which is compatible with said first dielectric layer.
Claim 10
Dependent Claim
60 words
A process as defined in claim 1 wherein the first metal conductors are first aluminum conductors and the first dielectric layer is a first silicon dioxide layer, and in which the surface of the photoresist and first silicon dioxide layer are etched in the etching step until the vicinity of the upper surface of the first aluminum conductors is reached.
Claim 11
Dependent Claim
57 words
A process as defined in claim 1 wherein the first metal conductors are first aluminum conductors and the first dielectric layer is a first silicon dioxide layer, and in which the surface of the photoresist and first silicon dioxide layer are etched in the etching step until the upper surface of the first aluminum conductors is exposed.
Claim 12
Dependent Claim
22 words
A process as defined in claim 1, wherein the layer of negative isoprene resin has a thickness of at least 0.5 micron.
Claim 13
Dependent Claim
166 words
A process for planarizing an integrated circuit comprising: (a) depositing and defining first aluminum conductors having a thickness of between approximately 0.7 and 1.3 microns on the passivated surface of an integrated circuit, (b) depositing between about 0.8 and 1.4 microns of a first silicon dioxide layer over the surface of the integrated circuit including the conductors, (c) depositing by spinning a negative photoresist layer of about 0.9 microns over the surface of the silicon dioxide layer, (d) baking the photoresist layer at 160° C. for about 20 minutes, (e) plasma etching the photoresist layer and first silicon dioxide layer in a CF 4 atmosphere including about 32% to 50% oxygen in a plasma etcher, to the upper surface of the first conductors, (f) cleaning the etched surface, (g) depositing between about 0.4 and 1.0 micron of a second silicon dioxide layer over the etched surface, whereby a planarized surface devoid of sharply angled steps in the regions around and over the aluminum conductors is produced.
Claim 14
Dependent Claim
166 words
A process for planarizing an integrated circuit comprising: (a) depositing and defining first aluminum conductors having a thickness of between approximately 0.7 and 1.3 microns on the passivated surface of an integrated circuit, (b) depositing between about 0.8 and 1.4 microns of a first silicon dioxide layer over the surface of the integrated circuit including the conductors, (c) depositing by spinning a negative photoresist layer of about 0.9 microns over the surface of the silicon dioxide layer, (d) baking the photoresist layer at 160° C. for about 20 minutes, (e) plasma etching the photoresist layer and first silicon dioxide layer in a CF 4 atmosphere including about 32% to 50% oxygen in a plasma etcher, to the upper surface of the first conductors, (f) cleaning the etched surface, (g) depositing between about 0.4 and 1.0 micron of a second silicon dioxide layer over the etched surface, whereby a planarized surface devoid of sharply angled steps in the regions around and over the aluminum conductors is produced.
Claim 15
Dependent Claim
19 words
A process as defined in claim 12, including depositing the silicon dioxide layers using a CVD or LPCVD process.
Claim 16
Dependent Claim
19 words
A process as defined in claim 12 including depositing the silicon dioxide layer using a plasma enhanced deposition process.
Claim 17
Dependent Claim
25 words
A process as defined in claim 12, in which the second, or the first and second, silicon dioxide layers are composed of undoped silicon dioxide.
Claim 18
Dependent Claim
27 words
A process as defined in claim 12, 13 or 15, including the further step of depositing and defining second aluminum conductors on the second silicon dioxide layer.
Claim 19
Dependent Claim
175 words
A process for planarizing an integrated circuit comprising: (a) depositing and defining first aluminum conductors having a thickness of between approximately 0.7 and 1.3 microns on the passivated surface of an integrated circuit, (b) depositing between about 0.8 and 1.4 microns of a first silicon dioxide layer over the surface of the integrated circuit including the conductors, (c) depositing by spinning a negative photoresist layer of about 0.9 microns over the surface of the silicon dioxide layer, (d) baking the photoresist layer at 160° C. for about 20 minutes, (e) plasma etching the photoresist layer and first silicon dioxide layer in a CF 4 atmosphere including about 32% to 50% oxygen in a plasma etcher, to the upper surface of the first conductors, at a pressure of about 0.9 to 1.6 torr, (f) cleaning the etched surface, (g) depositing between about 0.4 and 1.0 micron of a second silicon dioxide layer over the etched surface, whereby a planarized surface devoid of sharply angled steps in the regions around and over the aluminum conductors is produced.
Claim 20
Dependent Claim
175 words
A process for planarizing an integrated circuit comprising: (a) depositing and defining first aluminum conductors having a thickness of between approximately 0.7 and 1.3 microns on the passivated surface of an integrated circuit, (b) depositing between about 0.8 and 1.4 microns of a first silicon dioxide layer over the surface of the integrated circuit including the conductors, (c) depositing by spinning a negative photoresist layer of about 0.9 microns over the surface of the silicon dioxide layer, (d) baking the photoresist layer at 160° C. for about 20 minutes, (e) plasma etching the photoresist layer and first silicon dioxide layer in a CF 4 atmosphere including about 32% to 50% oxygen in a plasma etcher, to the upper surface of the first conductors, at a pressure of about 0.9 to 1.6 torr, (f) cleaning the etched surface, (g) depositing between about 0.4 and 1.0 micron of a second silicon dioxide layer over the etched surface, whereby a planarized surface devoid of sharply angled steps in the regions around and over the aluminum conductors is produced.
Claim 21
Dependent Claim
182 words
A process for planarizing an integrated circuit comprising: (a) depositing and defining first aluminum conductors having a thickness of between approximately 0.7 and 1.3 microns on the passivated surface of an integrated circuit, (b) depositing between about 0.8 and 1.4 microns of a first silicon dioxide layer over the surface of the integrated circuit including the conductors, (c) depositing by spinning a negative photoresist layer of about 0.9 microns over the surface of the silicon dioxide layer, (d) baking the photoresist layer at 160° C. for about 20 minutes, (e) plasma etching the photoresist layer and first silicon dioxide layer in a CF 4 atmosphere including about 32% to 50% oxygen in a plasma etcher, to the upper surface of the first conductors, at a pressure of about 0.9 to 1.6 torr, and a temperature of about 70° C., (f) cleaning the etched surface, (g) depositing between about 0.4 and 1.0 micron of a second silicon dioxide layer over the etched surface, whereby a planarized surface devoid of sharply angled steps in the regions around and over the aluminum conductors is produced.
Claim 22
Dependent Claim
182 words
A process for planarizing an integrated circuit comprising: (a) depositing and defining first aluminum conductors having a thickness of between approximately 0.7 and 1.3 microns on the passivated surface of an integrated circuit, (b) depositing between about 0.8 and 1.4 microns of a first silicon dioxide layer over the surface of the integrated circuit including the conductors, (c) depositing by spinning a negative photoresist layer of about 0.9 microns over the surface of the silicon dioxide layer, (d) baking the photoresist layer at 160° C. for about 20 minutes, (e) plasma etching the photoresist layer and first silicon dioxide layer in a CF 4 atmosphere including about 32% to 50% oxygen in a plasma etcher, to the upper surface of the first conductors, at a pressure of about 0.9 to 1.6 torr, and a temperature of about 70° C., (f) cleaning the etched surface, (g) depositing between about 0.4 and 1.0 micron of a second silicon dioxide layer over the etched surface, whereby a planarized surface devoid of sharply angled steps in the regions around and over the aluminum conductors is produced.
Claim 23
Dependent Claim
158 words
A process for planarizing an integrated circuit comprising: (a) vapor depositing a first layer of silicon dioxide on the surface of an integrated circuit having metal or metal alloy conductors resistant to etching in an atmosphere of CF 4 +O 2 (32-50%) on said surface, the thickness of said layer being about the same as the thickness of the conductors, (b) depositing and polymerizing a layer of negative type photoresist on the surface of the silicon dioxide layer, the thickness of the deposit being about the same or less than that of the silicon dioxide layer, (c) plasma etching the photoresist and layer of silicon dioxide in an atmosphere of CF 4 with about 32% to 50% oxygen, (d) cleaning the etched surface, (e) vapor depositing a second layer of silicon dioxide or silicon nitride of about the same thickness as the conductors over the etched surface, whereby a planarized surface devoid of sharp angled corners is produced.
Claim 24
Dependent Claim
158 words
A process for planarizing an integrated circuit comprising: (a) vapor depositing a first layer of silicon dioxide on the surface of an integrated circuit having metal or metal alloy conductors resistant to etching in an atmosphere of CF 4 +O 2 (32-50%) on said surface, the thickness of said layer being about the same as the thickness of the conductors, (b) depositing and polymerizing a layer of negative type photoresist on the surface of the silicon dioxide layer, the thickness of the deposit being about the same or less than that of the silicon dioxide layer, (c) plasma etching the photoresist and layer of silicon dioxide in an atmosphere of CF 4 with about 32% to 50% oxygen, (d) cleaning the etched surface, (e) vapor depositing a second layer of silicon dioxide or silicon nitride of about the same thickness as the conductors over the etched surface, whereby a planarized surface devoid of sharp angled corners is produced.
Claim 25
Dependent Claim
21 words
A process as defined in claim 19, in which the second or the first and second silicon dioxide layers are undoped.
Claim 26
Dependent Claim
30 words
A process as defined in claim 19 or 20 including the further step of depositing and defining a metal or metal alloy conductor on the surface of said second layer.
Claim 27
Dependent Claim
23 words
A process as defined in claim 19 or 20 in which the etch time proceeds to the point of exposure of the conductors.
Claim 28
Dependent Claim
55 words
A process as defined in claim 19 or 20 in which the etch time proceeds to the point of exposure of the conductors, and including the further step following the deposition of the second layer of silicon dioxide of depositing and defining a metal or metal alloy conductor on the surface of said second layer.
Claim 29
Dependent Claim
167 words
A process for planarizing an integrated circuit comprising: (a) vapor depositing a first layer of silicon dioxide on the surface of an integrated circuit having metal or metal alloy conductors resistant to etching in an atmosphere of CF 4 +O 2 (32-50%) on said surface, the thickness of said layer being about the same as the thickness of the conductors, (b) depositing and polymerizing a layer of negative type photoresist on the surface of the silicon dioxide layer, the thickness of the deposit being about the same or less than that of the silicon dioxide layer, (c) plasma etching the photoresist and layer of silicon dioxide in an atmosphere of CF 4 with about 32% to 50% oxygen, at a pressure of about 0.9 to 1.6 torr, (d) cleaning the etched surface, (e) vapor depositing a second layer of silicon dioxide or silicon nitride of about the same thickness as the conductors over the etched planarized surface, whereby a surface devoid of sharp angled corners is produced.
Claim 30
Dependent Claim
167 words
A process for planarizing an integrated circuit comprising: (a) vapor depositing a first layer of silicon dioxide on the surface of an integrated circuit having metal or metal alloy conductors resistant to etching in an atmosphere of CF 4 +O 2 (32-50%) on said surface, the thickness of said layer being about the same as the thickness of the conductors, (b) depositing and polymerizing a layer of negative type photoresist on the surface of the silicon dioxide layer, the thickness of the deposit being about the same or less than that of the silicon dioxide layer, (c) plasma etching the photoresist and layer of silicon dioxide in an atmosphere of CF 4 with about 32% to 50% oxygen, at a pressure of about 0.9 to 1.6 torr, (d) cleaning the etched surface, (e) vapor depositing a second layer of silicon dioxide or silicon nitride of about the same thickness as the conductors over the etched planarized surface, whereby a surface devoid of sharp angled corners is produced.
Claim 31
Dependent Claim
174 words
A process for planarizing an integrated circuit comprising: (a) vapor depositing a first layer of silicon dioxide on the surface of an integrated circuit having metal or metal alloy conductors resistant to etching in an atmosphere of CF 4 +O 2 (32-50%) on said surface, the thickness of said layer being about the same as the thickness of the conductors, (b) depositing and polymerizing a layer of negative type photoresist on the surface of the silicon dioxide layer, the thickness of the deposit being about the same or less than that of the silicon dioxide layer, (c) plasma etching the photoresist and layer of silicon dioxide in an atmosphere of CF 4 with about 32% to 50% oxygen, at a pressure of about 0.9 to 1.6 torr, and a temperature of about 70° C., (d) cleaning the etched surface, (e) vapor depositing a second layer of silicon dioxide or silicon nitride of about the same thickness as the conductors over the etched surface, whereby a planarized surface devoid of sharp angled corners is produced.
Claim 32
Dependent Claim
174 words
A process for planarizing an integrated circuit comprising: (a) vapor depositing a first layer of silicon dioxide on the surface of an integrated circuit having metal or metal alloy conductors resistant to etching in an atmosphere of CF 4 +O 2 (32-50%) on said surface, the thickness of said layer being about the same as the thickness of the conductors, (b) depositing and polymerizing a layer of negative type photoresist on the surface of the silicon dioxide layer, the thickness of the deposit being about the same or less than that of the silicon dioxide layer, (c) plasma etching the photoresist and layer of silicon dioxide in an atmosphere of CF 4 with about 32% to 50% oxygen, at a pressure of about 0.9 to 1.6 torr, and a temperature of about 70° C., (d) cleaning the etched surface, (e) vapor depositing a second layer of silicon dioxide or silicon nitride of about the same thickness as the conductors over the etched surface, whereby a planarized surface devoid of sharp angled corners is produced.
Claim 33
Dependent Claim
161 words
A process for planarizing an integrated circuit comprising: (a) depositing and defining first aluminum conductors on the surface of an integrated circuit, (b) depositing a first silicon dioxide layer over the surface of the integrated circuit including the conductors, (c) depositing and polymerizing a layer of negative photoresist carrier comprised of cis polyisoprene over the surface of the first silicon dioxide layer, (d) plasma etching the surface of the photoresist and first silicon dioxide layer to a predetermined thickness over the metal conductors in an atmosphere containing about 32 to 50 percent oxygen in a CF 4 gas in a plasma etcher, (e) cleaning the etched surface, removing any remaining photoresist, (f) depositing a second layer of silicon dioxide of predetermined thickness over the cleaned surface, whereby a planarized surface having very large radius of curvature steps over the metal conductors is produced, and (g) depositing and defining second aluminum conductors on the surface of the second layer of silicon dioxide.
Claim 34
Dependent Claim
161 words
A process for planarizing an integrated circuit comprising: (a) depositing and defining first aluminum conductors on the surface of an integrated circuit, (b) depositing a first silicon dioxide layer over the surface of the integrated circuit including the conductors, (c) depositing and polymerizing a layer of negative photoresist carrier comprised of cis polyisoprene over the surface of the first silicon dioxide layer, (d) plasma etching the surface of the photoresist and first silicon dioxide layer to a predetermined thickness over the metal conductors in an atmosphere containing about 32 to 50 percent oxygen in a CF 4 gas in a plasma etcher, (e) cleaning the etched surface, removing any remaining photoresist, (f) depositing a second layer of silicon dioxide of predetermined thickness over the cleaned surface, whereby a planarized surface having very large radius of curvature steps over the metal conductors is produced, and (g) depositing and defining second aluminum conductors on the surface of the second layer of silicon dioxide.
Claim 35
Dependent Claim
166 words
A process for planarizing an integrated circuit comprising: (a) depositing and defining first aluminum conductors on the surface of an integrated circuit, (b) depositing a first silicon dioxide layer over the surface of the integrated circuit including the conductors, (c) depositing and polymerizing a layer of negative photoresist carrier comprised of cis polyisoprene over the surface of the first silicon dioxide layer, (d) plasma etching the surface of the photoresist and first silicon dioxide layer in an atmosphere containing about 32 to 50% oxygen in a CF 4 gas in a plasma etcher until the vicinity of the upper surface of the first aluminum conductors is reached, (e) cleaning the etched surface, removing any remaining photoresist, (f) depositing a second layer of silicon dioxide of predetermined thickness over the cleaned surface, whereby a planarized surface having very large radius of curvature steps over the metal conductors is produced, and (g) depositing and defining second aluminum conductors on the surface of the second layer of silicon dioxide.
Claim 36
Dependent Claim
166 words
A process for planarizing an integrated circuit comprising: (a) depositing and defining first aluminum conductors on the surface of an integrated circuit, (b) depositing a first silicon dioxide layer over the surface of the integrated circuit including the conductors, (c) depositing and polymerizing a layer of negative photoresist carrier comprised of cis polyisoprene over the surface of the first silicon dioxide layer, (d) plasma etching the surface of the photoresist and first silicon dioxide layer in an atmosphere containing about 32 to 50% oxygen in a CF 4 gas in a plasma etcher until the vicinity of the upper surface of the first aluminum conductors is reached, (e) cleaning the etched surface, removing any remaining photoresist, (f) depositing a second layer of silicon dioxide of predetermined thickness over the cleaned surface, whereby a planarized surface having very large radius of curvature steps over the metal conductors is produced, and (g) depositing and defining second aluminum conductors on the surface of the second layer of silicon dioxide.
Claim 37
Dependent Claim
163 words
A process for planarizing an integrated circuit comprising: (a) depositing and defining first aluminum conductors on the surface of an integrated circuit, (b) depositing a first silicon dioxide layer over the surface of the integrated circuit including the conductors, (c) depositing and polymerizing a layer of negative photoresist carrier comprised of cis polyisoprene over the surface of the first silicon dioxide layer, (d) plasma etching the surface of the photoresist and first silicon dioxide layer in an atmosphere containing about 32 to 50% oxygen in a CF 4 gas in a plasma etcher until the upper surface of the first aluminum conductor is exposed, (e) cleaning the etched surface, removing any remaining photoresist, (f) depositing a second layer of silicon dioxide of predetermined thickness over the cleaned surface, whereby a planarized surface having very large radius of curvature steps over the metal conductors is produced, and (g) depositing and defining second aluminum conductors on the surface of the second layer of silicon dioxide.
Claim 38
Dependent Claim
163 words
A process for planarizing an integrated circuit comprising: (a) depositing and defining first aluminum conductors on the surface of an integrated circuit, (b) depositing a first silicon dioxide layer over the surface of the integrated circuit including the conductors, (c) depositing and polymerizing a layer of negative photoresist carrier comprised of cis polyisoprene over the surface of the first silicon dioxide layer, (d) plasma etching the surface of the photoresist and first silicon dioxide layer in an atmosphere containing about 32 to 50% oxygen in a CF 4 gas in a plasma etcher until the upper surface of the first aluminum conductor is exposed, (e) cleaning the etched surface, removing any remaining photoresist, (f) depositing a second layer of silicon dioxide of predetermined thickness over the cleaned surface, whereby a planarized surface having very large radius of curvature steps over the metal conductors is produced, and (g) depositing and defining second aluminum conductors on the surface of the second layer of silicon dioxide.
Claim 39
Dependent Claim
25 words
A process as defined in claim 26, 27 or 28, wherein the layer of negative photoresist carrier has a thickness of at least 0.5 microns.
Claim 40
Dependent Claim
161 words
A process for planarizing an integrated circuit comprising: (a) depositing and defining first aluminum conductors on the surface of an integrated circuit, (b) depositing a first silicon dioxide layer over the surface of the integrated circuit including the conductors, (c) depositing and polymerizing a layer of negative photoresist carrier comprised of cis polyisoprene over the surface of the first silicon dioxide layer, (d) plasma etching the surface of the photoresist and first silicon dioxide layer in an atmosphere containing about 32 to 50% oxygen in a CF 4 gas in a plasma etcher, at a pressure of about 0.9 to 1.6 torr, (e) cleaning the etched surface, removing any remaining photoresist, (f) depositing a second layer of silicon dioxide of predetermined thickness over the cleaned surface, whereby a planarized surface having very large radius of curvature steps over the metal conductors is produced, and (g) depositing and defining second aluminum conductors on the surface of the second layer of silicon dioxide.
Claim 41
Dependent Claim
161 words
A process for planarizing an integrated circuit comprising: (a) depositing and defining first aluminum conductors on the surface of an integrated circuit, (b) depositing a first silicon dioxide layer over the surface of the integrated circuit including the conductors, (c) depositing and polymerizing a layer of negative photoresist carrier comprised of cis polyisoprene over the surface of the first silicon dioxide layer, (d) plasma etching the surface of the photoresist and first silicon dioxide layer in an atmosphere containing about 32 to 50% oxygen in a CF 4 gas in a plasma etcher, at a pressure of about 0.9 to 1.6 torr, (e) cleaning the etched surface, removing any remaining photoresist, (f) depositing a second layer of silicon dioxide of predetermined thickness over the cleaned surface, whereby a planarized surface having very large radius of curvature steps over the metal conductors is produced, and (g) depositing and defining second aluminum conductors on the surface of the second layer of silicon dioxide.
Claim 42
Dependent Claim
169 words
A process for planarizing an integrated circuit comprising: (a) depositing and defining first aluminum conductors on the surface of an integrated circuit, (b) depositing a first silicon dioxide layer over the surface of the integrated circuit including the conductors, (c) depositing and polymerizing a layer of negative photoresist carrier comprised of cis polyisoprene over the surface of the first silicon dioxide layer, (d) plasma etching the surface of the photoresist and first silicon dioxide layer in an atmosphere containing about 32 to 50% oxygen in a CF 4 gas in a plasma etcher, at a pressure of about 0.9 to 1.6 torr, and at a temperature of about 70° C., (e) cleaning the etched surface, removing any remaining photoresist, (f) depositing a second layer of silicon dioxide of predetermined thickness over the cleaned surface, whereby a planarized surface having very large radius of curvature steps over the metal conductors is produced, and (g) depositing and defining second aluminum conductors on the surface of the second layer of silicon dioxide.
Claim 43
Dependent Claim
169 words
A process for planarizing an integrated circuit comprising: (a) depositing and defining first aluminum conductors on the surface of an integrated circuit, (b) depositing a first silicon dioxide layer over the surface of the integrated circuit including the conductors, (c) depositing and polymerizing a layer of negative photoresist carrier comprised of cis polyisoprene over the surface of the first silicon dioxide layer, (d) plasma etching the surface of the photoresist and first silicon dioxide layer in an atmosphere containing about 32 to 50% oxygen in a CF 4 gas in a plasma etcher, at a pressure of about 0.9 to 1.6 torr, and at a temperature of about 70° C., (e) cleaning the etched surface, removing any remaining photoresist, (f) depositing a second layer of silicon dioxide of predetermined thickness over the cleaned surface, whereby a planarized surface having very large radius of curvature steps over the metal conductors is produced, and (g) depositing and defining second aluminum conductors on the surface of the second layer of silicon dioxide.
Claim 44
Dependent Claim
41 words
A process as defined in claim 30 or 31, in which the surface of the photoresist and first silicon dioxide layer are etched in the etching step until the vicinity of the upper surface of the first aluminum conductors is reached.
Claim 45
Dependent Claim
38 words
A process as defined in claim 30 or 31, in which the surface of the photoresist and first silicon dioxide layer are etched in the etching step until the upper surface of the first aluminum conductor is exposed.
Claim 46
Dependent Claim
24 words
A process as defined in claim 30 or 31, wherein the layer of negative photoresist carrier has a thickness of at least 0.5 micron.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-06-17 | 1988-12-17 | 1989-06-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-06-17 | 1992-12-17 | 1993-06-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-06-17 | 1996-12-17 | 1997-06-18 | $7700.00 | Window Closed / Lapsed |