Metal borides, carbides, nitrides, silicides, oxide materials and their method of preparation
Assignee: Moltech Invent SA
•
Filing: 1984-06-28
•
Granted: 1985-07-09
•
Expires: 2004-06-28
Abstract
Abstract Precursors, particularly of non-oxide ceramics, are prepared by special seeding, under carefully controlled conditions. Such procedures can lead to the preparation of unique powders, which may be useful, for example as abrasives, or further processed in special manner to prepare a variety of metal substances. Such procedures can permit final firing to sintered product.
Inventors
- 👤 Albert L. Barnes
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 05:16
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/58; C01; C01B; C01B21/00; C01B21/06; C01B32/00; C01B32/90; C01B33/00; C01B33/06; C01B35/00; C01B35/02; C01B35/04; C04B35/56; C04B35/5805; C04B35/58064; C04B35/58071; C04B35/622; C04B35/626; C04B35/63; C04B35/632; C01B21/0615; C01B21/0617; C01B21/062; C01B21/076; C01P; C01P2006/00; C01P2006/20
Claims Analysis
Total Claims: 38
Claim 1
Independent Claim
155 words
The method of making a composition adapted for preparing refractory hard metal boride in a process first combining metal oxide with reducing agent, which method comprises: establishing a solution of a non-oxide substance of said metal in liquid medium; seeding said solution with solid and insoluble, ultrafine carbon particulates which maintain solid integrity in the resulting dispersion; agitating the seeded dispersion; gradually adjusting the pH of liquid medium, while agitation continues, by bringing said liquid medium in contact with organic, carbon-containing substance yielding hydroxyl ions in aqueous medium at elevated temperature; establishing said liquid medium at sufficiently elevated temperature to yield said hydroxyl ions; forming hydrous metal oxide crystals with said ultrafine particulate carbon seeds in said dispersion; separating the resulting seeded crystals from said dispersion medium; admixing the resulting separated seeded crystals with boron-containing substance; and calcining the resulting admixture, thereby producing a calcined mixture for preparing hard metal boride by elevated temperature reaction.
Claim 2
Independent Claim
155 words
The method of making a composition adapted for preparing refractory hard metal boride in a process first combining metal oxide with reducing agent, which method comprises: establishing a solution of a non-oxide substance of said metal in liquid medium; seeding said solution with solid and insoluble, ultrafine carbon particulates which maintain solid integrity in the resulting dispersion; agitating the seeded dispersion; gradually adjusting the pH of liquid medium, while agitation continues, by bringing said liquid medium in contact with organic, carbon-containing substance yielding hydroxyl ions in aqueous medium at elevated temperature; establishing said liquid medium at sufficiently elevated temperature to yield said hydroxyl ions; forming hydrous metal oxide crystals with said ultrafine particulate carbon seeds in said dispersion; separating the resulting seeded crystals from said dispersion medium; admixing the resulting separated seeded crystals with boron-containing substance; and calcining the resulting admixture, thereby producing a calcined mixture for preparing hard metal boride by elevated temperature reaction.
Claim 3
Dependent Claim
23 words
The method of claim 1, wherein said calcined mixture is reacted and sintered at elevated temperature thereby preparing sintered refractory metal boride product.
Claim 4
Dependent Claim
34 words
The method of claim 1, wherein said solution is seeded with said carbon particulates of high purity and having average particle size within the range of from about 0.01 micron to about 0.1 micron.
Claim 5
Dependent Claim
20 words
The method of claim 1, wherein there is seeded a solution of a halide salt of said refractory hard metal.
Claim 6
Dependent Claim
26 words
The method of claim 1, wherein pH is adjusted by addition of organic, carbon-containing substance yielding ammonia plus hydroxyl ions in aqueous medium at elevated temperature.
Claim 7
Dependent Claim
25 words
The method of claim 1, wherein said liquid medium is heated during crystal formation to establish same at sufficiently elevated temperature to yield hydroxyl ions.
Claim 8
Dependent Claim
30 words
The method of claim 1, wherein bringing said liquid medium in contact with said organic substance comprises bringing organic liquid medium in contact with aqueous medium containing said organic substance.
Claim 9
Dependent Claim
28 words
The method of claim 1, wherein formation of said hydrous metal oxide crystals with said ultrafine particulate carbon seeds precipitates said oxide crystals and seeds from said dispersion.
Claim 10
Dependent Claim
68 words
A dry, solid, free-flowing particulate derived from material containing carbon-nucleated hydrous metal oxide, said composition comprising crystals of dehydroxylized metal oxide nucleated with a reducing agent of solid, ultrafine carbon particulate seeds, the seeded crystals being in intimate mixture in the particulate with a reactant for the metal of said metal oxide, which reactant is capable of reacting with said metal when the metal is reduced by carbon.
Claim 11
Dependent Claim
68 words
A dry, solid, free-flowing particulate derived from material containing carbon-nucleated hydrous metal oxide, said composition comprising crystals of dehydroxylized metal oxide nucleated with a reducing agent of solid, ultrafine carbon particulate seeds, the seeded crystals being in intimate mixture in the particulate with a reactant for the metal of said metal oxide, which reactant is capable of reacting with said metal when the metal is reduced by carbon.
Claim 12
Dependent Claim
20 words
The particulate of claim 9, wherein said crystals are of dehydroxylized titaniun oxide and said reactant is a boron-containing reactant.
Claim 13
Dependent Claim
18 words
The particulate of claim 9, wherein said seeded crystals are in intimate mixture with reactant plus pulverulent metal.
Claim 14
Dependent Claim
85 words
A dry, solid and free-flowing, electrically and thermally conductive particulate derived from material containing nucleated hydrous metal oxide, said composition comprising crystals of dehydroxylized metal oxide nucleated with seeds of finely divided metal plus seeds of a metal oxide reducing agent of solid, ultrafine carbon particulates, the seeded crystals being in intimate mixture in the particulate with a reactant for the metal of said metal oxide, which reactant is capable of reacting with said metal of the oxide when the metal is reduced by carbon.
Claim 15
Dependent Claim
85 words
A dry, solid and free-flowing, electrically and thermally conductive particulate derived from material containing nucleated hydrous metal oxide, said composition comprising crystals of dehydroxylized metal oxide nucleated with seeds of finely divided metal plus seeds of a metal oxide reducing agent of solid, ultrafine carbon particulates, the seeded crystals being in intimate mixture in the particulate with a reactant for the metal of said metal oxide, which reactant is capable of reacting with said metal of the oxide when the metal is reduced by carbon.
Claim 16
Dependent Claim
27 words
The particulate of claim 12, wherein said crystals are of dehydroxylized titanium oxide, said reactant is a boron-containing reactant and said finely divided metal includes pulverulent aluminum.
Claim 17
Dependent Claim
126 words
In the method for producing a metal oxide in combination with reducing agent for same wherein a solution of a soluble, non-oxide substance of the metal is prepared in liquid medium, and thereafter pH adjustment is used to precipitate metal oxide, the improvement which comprises: seeding said solution with solid and insoluble, ultrafine carbon particulates which maintain solid integrity in the resulting dispersion; agitating the seeded dispersion; gradually adjusting the pH of liquid medium, while agitation continues, by bringing said liquid medium in contact with organic, carbon-containing substance yielding hydroxyl ions in aqueous medium at elevated temperature; and establishing said liquid medium at sufficiently elevated temperature to yield said hydroxyl ions; thereby forming hydrous metal oxide crystals with said ultrafine particulate carbon seeds in said dispersion.
Claim 18
Dependent Claim
126 words
In the method for producing a metal oxide in combination with reducing agent for same wherein a solution of a soluble, non-oxide substance of the metal is prepared in liquid medium, and thereafter pH adjustment is used to precipitate metal oxide, the improvement which comprises: seeding said solution with solid and insoluble, ultrafine carbon particulates which maintain solid integrity in the resulting dispersion; agitating the seeded dispersion; gradually adjusting the pH of liquid medium, while agitation continues, by bringing said liquid medium in contact with organic, carbon-containing substance yielding hydroxyl ions in aqueous medium at elevated temperature; and establishing said liquid medium at sufficiently elevated temperature to yield said hydroxyl ions; thereby forming hydrous metal oxide crystals with said ultrafine particulate carbon seeds in said dispersion.
Claim 19
Dependent Claim
34 words
The method of claim 14, wherein said solution is seeded with ultrafine carbon particulates of high purity and having average particle size within the range of from about 0.01 micron to about 0.1 micron.
Claim 20
Dependent Claim
20 words
The method of claim 14, wherein there is seeded a solution of a halide salt of said refractory hard metal.
Claim 21
Dependent Claim
26 words
The method of claim 14, wherein pH is adjusted by addition of organic, carbon-containing substance yielding ammonia plus hydroxyl ions in aqueous medium at elevated temperature.
Claim 22
Dependent Claim
24 words
The method of claim 14, wherein said liquid medium is heated during crystal formation to establish same at sufficient temperature to yield hydroxyl ions.
Claim 23
Dependent Claim
30 words
The method of claim 14, wherein bringing said liquid medium in contact with said organic substance comprises bringing organic liquid medium in contact with aqueous medium containing said organic substance.
Claim 24
Dependent Claim
27 words
The method of claim 14, wherein formation of said hydrous metal oxide crystals with said ultrafine particulate carbon seeds precipitates said crystals and seeds from said dispersion.
Claim 25
Dependent Claim
17 words
The method of claim 14, wherein said solution is seeded with said carbon particulates plus particulate metal.
Claim 26
Dependent Claim
29 words
The method of claim 21, wherein formation of said hydrous metal oxide crystals with said carbon seeds plus particulate metal seeds precipitates said crystals and seeds from said dispersion.
Claim 27
Dependent Claim
13 words
The method of claim 21, wherein said precipitate is separated from supernatant liquid.
Claim 28
Dependent Claim
20 words
The method of claim 23, wherein said precipitate is separated by filtration and further said precipitate is cooled and dried.
Claim 29
Dependent Claim
37 words
A dry, solid and free-flowing, electrically and thermally conductive gray particulate comprising crystals of hydrous metal oxide nucleated with seeds of finely divided metal plus seeds of a metal oxide reducing agent of solid, ultrafine carbon particles.
Claim 30
Dependent Claim
37 words
A dry, solid and free-flowing, electrically and thermally conductive gray particulate comprising crystals of hydrous metal oxide nucleated with seeds of finely divided metal plus seeds of a metal oxide reducing agent of solid, ultrafine carbon particles.
Claim 31
Independent Claim
167 words
The method for preparing a metal oxide in combination with reducing agent for same, the combination being adapted for reduction of said metal oxide, which method comprises: establishing a solution of a soluble, non-oxide of the metal in liquid medium; seeding said solution with solid and insoluble, ultrafine carbon paticulates, which maintain solid integrity in the resulting dispersion, in an amount substantially less than stoichiometric for reduction of said metal oxide; gradually adjusting the pH of liquid medium, while agitation continues, by bringing said liquid medium in contact with substance yielding hydroxyl ions in aqueous medium at elevated temperature; establishing said liquid medium at sufficiently elevated temperature to yield said hydroxyl ions; forming hydrous metal oxide crystals with said ultrafine particulate carbons seeds in said dispersion; separating the resulting seeded crystals from said dispersion medium; and admixing the resulting separated seeded crystals with additional ultrafine carbon particulates in an amount sufficient to provide a total of said particulates greater than stoichiometric for reduction of said metal oxide.
Claim 32
Independent Claim
167 words
The method for preparing a metal oxide in combination with reducing agent for same, the combination being adapted for reduction of said metal oxide, which method comprises: establishing a solution of a soluble, non-oxide of the metal in liquid medium; seeding said solution with solid and insoluble, ultrafine carbon paticulates, which maintain solid integrity in the resulting dispersion, in an amount substantially less than stoichiometric for reduction of said metal oxide; gradually adjusting the pH of liquid medium, while agitation continues, by bringing said liquid medium in contact with substance yielding hydroxyl ions in aqueous medium at elevated temperature; establishing said liquid medium at sufficiently elevated temperature to yield said hydroxyl ions; forming hydrous metal oxide crystals with said ultrafine particulate carbons seeds in said dispersion; separating the resulting seeded crystals from said dispersion medium; and admixing the resulting separated seeded crystals with additional ultrafine carbon particulates in an amount sufficient to provide a total of said particulates greater than stoichiometric for reduction of said metal oxide.
Claim 33
Dependent Claim
19 words
The method of claim 26, wherein reactant is admixed to the seeded crystals along with said additional carbon particulates.
Claim 34
Independent Claim
162 words
The method of making a composition adapted for preparing a metal silicide in a process combining silicon oxide with reducing agent, which method comprises; establishing a solution of a non-oxide of silicon in liquid medium; seeding said solution with solid and insoluble, ultrafine carbon particulates which maintain solid integrity in the resulting dispersion; agitating the seeded dispersion; gradually adjusting the pH of liquid medium, while agitation continues, by bringing said liquid medium in contact with organic, carbon-containing substance yielding hydroxyl ions in aqueous medium at elevated temperature; establishing said liquid medium at sufficiently elevated temperature to yield said hydroxyl ions; forming hydrous silicon oxide crystals with said ultrafine particulate carbon seeds in said dispersion; separating the resulting seeded crystals from said dispersion medium; admixing the resulting separated seeded crystals with metallic oxide; and calcining the resulting admixture to prepare an intimate mixture of metallic oxide with seeded silicon oxide crystals, which mixture is adapted for preparing metal silicide by elevated temperature reaction.
Claim 35
Independent Claim
162 words
The method of making a composition adapted for preparing a metal silicide in a process combining silicon oxide with reducing agent, which method comprises; establishing a solution of a non-oxide of silicon in liquid medium; seeding said solution with solid and insoluble, ultrafine carbon particulates which maintain solid integrity in the resulting dispersion; agitating the seeded dispersion; gradually adjusting the pH of liquid medium, while agitation continues, by bringing said liquid medium in contact with organic, carbon-containing substance yielding hydroxyl ions in aqueous medium at elevated temperature; establishing said liquid medium at sufficiently elevated temperature to yield said hydroxyl ions; forming hydrous silicon oxide crystals with said ultrafine particulate carbon seeds in said dispersion; separating the resulting seeded crystals from said dispersion medium; admixing the resulting separated seeded crystals with metallic oxide; and calcining the resulting admixture to prepare an intimate mixture of metallic oxide with seeded silicon oxide crystals, which mixture is adapted for preparing metal silicide by elevated temperature reaction.
Claim 36
Dependent Claim
18 words
The method of claim 28, wherein said calcined mixture is reacted at elevated temperature thereby preparing metal silicide.
Claim 37
Dependent Claim
138 words
In the method of making a metal boride, carbide or nitride by first preparing metal oxide in combination with reducing agent, wherein a solution of a soluble, non-oxide of the metal is prepared in liquid medium and thereafter pH adjustment is used to precipitate metal oxide, the improvement comprising: seeding said solution with solid and insoluble, ultrafine carbon particulates which maintain solid integrity in the resulting dispersion; agitating the seeded dispersion; gradually adjusting the pH of liquid medium, while agitation continues, by bringing said liquid medium in contact with organic, carbon-containing substance yielding hydroxyl ions in aqueous medium at elevated temperature; establishing said liquid medium at sufficiently elevated temperature to yield said hydroxyl ions; forming hydrous metal oxide crystals with said ultrafine particulate carbon seeds in said dispersion; and separating the resulting seeded crystals from said dispersion medium.
Claim 38
Dependent Claim
138 words
In the method of making a metal boride, carbide or nitride by first preparing metal oxide in combination with reducing agent, wherein a solution of a soluble, non-oxide of the metal is prepared in liquid medium and thereafter pH adjustment is used to precipitate metal oxide, the improvement comprising: seeding said solution with solid and insoluble, ultrafine carbon particulates which maintain solid integrity in the resulting dispersion; agitating the seeded dispersion; gradually adjusting the pH of liquid medium, while agitation continues, by bringing said liquid medium in contact with organic, carbon-containing substance yielding hydroxyl ions in aqueous medium at elevated temperature; establishing said liquid medium at sufficiently elevated temperature to yield said hydroxyl ions; forming hydrous metal oxide crystals with said ultrafine particulate carbon seeds in said dispersion; and separating the resulting seeded crystals from said dispersion medium.
References Cited (Backward Citations)
GB1004585A
Cited
US3649314A
Cited
US3723601A
Cited
GB1367763A
Cited
US3791808A
Cited
US4010242A
Cited
US4292619A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-07-08 | 1989-01-07 | 1989-07-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-07-08 | 1993-01-07 | 1993-07-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-07-08 | 1997-01-07 | 1997-07-09 | $7700.00 | Window Closed / Lapsed |