Method for surface treatment of ferromagnetic fine powder and forming a magnetic recording device
Assignee: Fujifilm Holdings Corp
•
Filing: 1984-05-24
•
Granted: 1985-08-06
•
Expires: 2004-05-24
Abstract
Abstract A method for the surface treatment of a ferromagnetic fine powder is disclosed. The method increases the dispersibility of the powder in a magnetic coating composition. The method comprises subjecting a magnetic composition to a dispersing processing, with the magnetic composition containing (1) a ferromagnetic fine powder, (2) at least one polar compound selected from a group consisting of such compounds as to have one or more of --COOH, --CONH 2 , --CONH 2 , --PO 3 H, --SO 3 H, --OH or --NH 2 in a molecule and quaternary ammonium salts, and (3) an organic solvent capable of dissolving the polar compound, and evaporating the organic solvent from the magnetic composition.
Inventors
- 👤 Tsutomu Okita
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 08:44
CPC Classifications
G; G11; G11B; G11B5/00; G11B5/62; G11B5/68; G11B5/70; G11B5/712
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
125 words
A method for producing a magnetic recording medium which comprises the steps of (1) preparing ferromagnetic fine powder by the process comprising: (A) subjecting a composition to dispersion processing, wherein the composition comprises: (i) a ferromagnetic powder; (ii) a polar compound selected from the group consisting of acrylic acid, crotonic acid and bis(β-acryloyloxyethyl)phosphate; and (iii) an organic solvent capable of dissolving the polar compound; and (B) evaporating the organic solvent from the resulting composition, (2) dispersing said ferromagnetic fine powder of (1) in a binder comprising a compound polymerizable by irradiation with electron beams and has (meth)acryloyl groups at both ends of the molecule, (3) forming, on a support, a magnetic layer from the resulting composition and (4) irradiating the magnetic layer with electron beams.
Claim 2
Independent Claim
125 words
A method for producing a magnetic recording medium which comprises the steps of (1) preparing ferromagnetic fine powder by the process comprising: (A) subjecting a composition to dispersion processing, wherein the composition comprises: (i) a ferromagnetic powder; (ii) a polar compound selected from the group consisting of acrylic acid, crotonic acid and bis(β-acryloyloxyethyl)phosphate; and (iii) an organic solvent capable of dissolving the polar compound; and (B) evaporating the organic solvent from the resulting composition, (2) dispersing said ferromagnetic fine powder of (1) in a binder comprising a compound polymerizable by irradiation with electron beams and has (meth)acryloyl groups at both ends of the molecule, (3) forming, on a support, a magnetic layer from the resulting composition and (4) irradiating the magnetic layer with electron beams.
Claim 3
Dependent Claim
33 words
A method as claimed in claim 1, wherein the polar compound is present in the composition in a portion of 0.5 to 2.0 wt% based on the weight of the ferromagnetic fine powder.
Claim 4
Dependent Claim
33 words
A method as claimed in claim 1, wherein the ferromagnetic fine powder is selected from the group of powders consisting of ferromagnetic iron oxide powder, ferromagnetic chromium dioxide powder and ferromagnetic alloy powder.
Claim 5
Dependent Claim
46 words
A method as claimed in claim 3, wherein the ferromagnetic fine powder comprising ferromagnetic iron oxide or ferromagnetic chromium dioxide particles having an axial ratio ranging from about 2:1 to about 20:1 and an average length in the range of about 0.2 to about 2.0 μm.
Claim 6
Dependent Claim
25 words
A method as claimed in claim 3, wherein the ferromagnetic fine powder comprises ferromagnetic alloy particles having a length of about 1.0 μm or shorter.
Claim 7
Dependent Claim
33 words
A method as claimed in claim 1, wherein the evaporating of the organic solvent is carried out by heating to a temperature within the range of about 80° C. to about 100° C.
Claim 8
Dependent Claim
42 words
A method as claimed in claim 6, wherein the evaporation of the organic solvent is carried out until the remaining unevaporated organic solvent is present in an amount of 5 wt% or less based on the weight of the ferromagnetic fine powder.
References Cited (Backward Citations)
US3790407A
Cited
US4335183A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-08-05 | 1989-02-04 | 1989-08-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-08-05 | 1993-02-04 | 1993-08-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-08-05 | 1997-02-04 | 1997-08-06 | $7700.00 | Window Closed / Lapsed |