Electrodeposition composition, process for providing a Zn/Si/P coating on metal substrates and articles so coated
Assignee: AMP-AKZO Corp A CORP OF
•
Filing: 1984-08-16
•
Granted: 1985-08-06
•
Expires: 2004-08-16
Abstract
Abstract The present invention provides an aqueous composition and process for the electrodeposition of a layer of zinc containing silicon and phosphorus on a metal substrate. The electrodeposition composition is prepared by reacting metallic silicon and zinc with phosphoric acid and an alkali metal hydroxide in the ratio of between 0.4 and 1.3 moles of alkali metal hydroxide per mole of phosphoric acid, and adjusting the solution to a pH of 2 or higher after completion of the reaction. The coating is deposited on the metal substrate by electrodeposition and comprises about 70% to about 99.5% by weight of zinc, and about 0.10% to about 10% by weight of silicon, and about 0.5% to about 20% by weight of phosphorus. The resultant zinc/silicon/phosphorus coating improves the resistance of the metal substrate to corrosion, wear, galling and stress corrosion cracking. While essentially all metals of industrial importance may be coated, this process is especially important for ferrous metals, steels, stainless steels, copper, aluminum and titanium. The coated metal substrates are useful in various industries, including appliance, automobile, oil field equipment, nuclear reactor equipment, aerospace equipment, etc.
Inventors
- 👤 Yu-Ling Teng
- 👤 Charles McCoy
- 👤 Francis DeFalco
- 👤 Richard Mayernick
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 21:03
CPC Classifications
C; C25; C25D; C25D3/00; C25D3/02; C25D3/56; C25D3/565; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12771; Y10T428/12785; Y10T428/12792; Y10T428/12799
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
105 words
A method to provide a solution suitable for electrodepositing a coating comprising at least about 70% by weight of zinc, at least about 0.1% by weight of silicon, and at least about 0.5% by weight of phosphorus on a metallic substrate, the method comprising: (a) contacting metallic zinc and silicon with phosphoric acid and an alkali metal hydroxide until between 0.4 and 1.3 moles of alkali metal hydroxide per mole of phosphoric acid has been added; (b) allowing the reaction to proceed until gas evolution ceases; (c) removing residual metallic zinc and silicon from the solution; and (d) adjusting the pH to 2.5 or greater.
Claim 2
Independent Claim
105 words
A method to provide a solution suitable for electrodepositing a coating comprising at least about 70% by weight of zinc, at least about 0.1% by weight of silicon, and at least about 0.5% by weight of phosphorus on a metallic substrate, the method comprising: (a) contacting metallic zinc and silicon with phosphoric acid and an alkali metal hydroxide until between 0.4 and 1.3 moles of alkali metal hydroxide per mole of phosphoric acid has been added; (b) allowing the reaction to proceed until gas evolution ceases; (c) removing residual metallic zinc and silicon from the solution; and (d) adjusting the pH to 2.5 or greater.
Claim 3
Dependent Claim
33 words
The method according to claim 1 wherein the reaction temperature is less than 75° C., and wherein between 0.6 and 0.9 moles of alkali metal hydroxide per mole of phosphoric acid are added.
Claim 4
Dependent Claim
19 words
The method according to claim 2 wherein the alkali metal hydroxide is added in the form of a solid.
Claim 5
Dependent Claim
16 words
A method of claim 3 wherein the pH is adjusted to a pH of about 2.
Claim 6
Independent Claim
131 words
A method to provide a solution suitable for electrodepositing a coating comprising at least about 70% by weight of zinc, at least about 0.1% by weight of silicon, and at least about 0.5% by weight of phosphorus on a metallic substrate, the method comprising: (a) contacting metallic zinc and silicon with phosphoric acid; (b) adding an alkali metal hydroxide in increments to the zinc and silicon mixture such that the temperature of the reaction does not exceed the boiling point of the solution, and until between 0.4 and 1.2 moles of alkali metal hydroxide per mole of phosphoric acid has been added; (c) Allowing the reaction to proceed until gas evolution ceases; (d) removing residual metallic zinc and silicon from the solution; and (e) adjusting the pH to 2.5 or greater.
Claim 7
Independent Claim
131 words
A method to provide a solution suitable for electrodepositing a coating comprising at least about 70% by weight of zinc, at least about 0.1% by weight of silicon, and at least about 0.5% by weight of phosphorus on a metallic substrate, the method comprising: (a) contacting metallic zinc and silicon with phosphoric acid; (b) adding an alkali metal hydroxide in increments to the zinc and silicon mixture such that the temperature of the reaction does not exceed the boiling point of the solution, and until between 0.4 and 1.2 moles of alkali metal hydroxide per mole of phosphoric acid has been added; (c) Allowing the reaction to proceed until gas evolution ceases; (d) removing residual metallic zinc and silicon from the solution; and (e) adjusting the pH to 2.5 or greater.
Claim 8
Dependent Claim
33 words
The method according to claim 5 wherein the reaction temperature is less than 75° C., and wherein between 0.6 and 0.9 moles of alkali metal hydroxide per mole of phosphoric acid are added.
Claim 9
Independent Claim
192 words
A method of producing a solution suitable for electrodeposition to provide a coating containing at least about 70% by weight of zinc, at least about 0.1% by weight of silicon, and at least about 0.5% by weight of phosphorus on a metallic substrate, the method comprising: (a) contacting metallic zinc with phosphoric acid and an alkali metal hydroxide until between 0.4 and 1.3 moles of alkali metal hydroxide per mole of phosphoric acid has been added; (b) allowing the reaction to proceed until the pH is in the range of about 1.5 to 4; and, (c) removing the residual metallic zinc from the solution; (d) contacting metallic silicon with phosphoric acid and an alkali metal hydroxide until between 0.2 and 0.4 moles of phosphoric acid per mole of alkali metal hydroxide has been added; (e) allowing the reaction to proceed until the pH reaches between 10 and 12; and, (f) removing residual metallic silicon from the solution; (g) adding the silicon-containing solution to the zinc-containing solution such that the ratio of zinc to silicon is in the range of 8:1 to 30:1; and (h) adjusting the solution pH to 2.5 or greater.
Claim 10
Independent Claim
192 words
A method of producing a solution suitable for electrodeposition to provide a coating containing at least about 70% by weight of zinc, at least about 0.1% by weight of silicon, and at least about 0.5% by weight of phosphorus on a metallic substrate, the method comprising: (a) contacting metallic zinc with phosphoric acid and an alkali metal hydroxide until between 0.4 and 1.3 moles of alkali metal hydroxide per mole of phosphoric acid has been added; (b) allowing the reaction to proceed until the pH is in the range of about 1.5 to 4; and, (c) removing the residual metallic zinc from the solution; (d) contacting metallic silicon with phosphoric acid and an alkali metal hydroxide until between 0.2 and 0.4 moles of phosphoric acid per mole of alkali metal hydroxide has been added; (e) allowing the reaction to proceed until the pH reaches between 10 and 12; and, (f) removing residual metallic silicon from the solution; (g) adding the silicon-containing solution to the zinc-containing solution such that the ratio of zinc to silicon is in the range of 8:1 to 30:1; and (h) adjusting the solution pH to 2.5 or greater.
Claim 11
Dependent Claim
17 words
The method of claim 7 wherein the alkali metal hydroxide is in the form of a solid.
Claim 12
Dependent Claim
14 words
The method of claim 7 wherein the solution pH is adjusted to about 3.
Claim 13
Independent Claim
247 words
A method of producing a solution suitable for electrodeposition to provide a coating containing at least about 70% by weight of zinc, at least about 0.1% by weight of silicon, at least about 0.5% by weight of phosphorus on the metallic substrate, the method comprising: (a) contacting metallic zinc with phosphoric acid; (b) adding an alkali metal hydroxide in increments to react with the zinc such that the temperature of the reaction mixture does not exceed the boiling point of the solution, and until between 0.4 and 1.3 moles of alkali metal hydroxide per mole of phosphoric acid has been added; (c) allowing the reaction to proceed until the pH is in the range of about 1.5-4; and, (d) removing the residual metallic zinc from the solution; (e) contacting metallic silicon with an alkali metal hydroxide solution in a separate container; (f) adding phosphoric acid in increments to react with the silicon alkali metal hydroxide mixture such that the temperature of the reaction mixture does not exceed the boiling point of the solution and until between 0.2 and 0.4 moles of phosphoric acid per mole of alkali metal hydroxide has been added; (g) allowing the reaction to proceed until the pH reaches 10-12; and, (h) removing residual silicon metal from the solution; (i) adding the silicon-containing solution to the zinc-containing solution such that the ratio of zinc to silicon is in the range of 8:1 to 30:1; and (j) adjusting the solution pH to 2.5 or greater.
Claim 14
Independent Claim
247 words
A method of producing a solution suitable for electrodeposition to provide a coating containing at least about 70% by weight of zinc, at least about 0.1% by weight of silicon, at least about 0.5% by weight of phosphorus on the metallic substrate, the method comprising: (a) contacting metallic zinc with phosphoric acid; (b) adding an alkali metal hydroxide in increments to react with the zinc such that the temperature of the reaction mixture does not exceed the boiling point of the solution, and until between 0.4 and 1.3 moles of alkali metal hydroxide per mole of phosphoric acid has been added; (c) allowing the reaction to proceed until the pH is in the range of about 1.5-4; and, (d) removing the residual metallic zinc from the solution; (e) contacting metallic silicon with an alkali metal hydroxide solution in a separate container; (f) adding phosphoric acid in increments to react with the silicon alkali metal hydroxide mixture such that the temperature of the reaction mixture does not exceed the boiling point of the solution and until between 0.2 and 0.4 moles of phosphoric acid per mole of alkali metal hydroxide has been added; (g) allowing the reaction to proceed until the pH reaches 10-12; and, (h) removing residual silicon metal from the solution; (i) adding the silicon-containing solution to the zinc-containing solution such that the ratio of zinc to silicon is in the range of 8:1 to 30:1; and (j) adjusting the solution pH to 2.5 or greater.
Claim 15
Independent Claim
106 words
A method of electrodepositing a coating comprising at least about 70% by weight of zinc, at least about 0.1% by weight of silicon, and at least about 0.5% by weight of phosphorus on a metallic substrate, the method comprising: (a) providing an aqueous solution for electrodeposition prepared according to claims 1, 5, 2, 6, 3, 4, 7, 10, 8, or 9; (b) cleaning the metallic substrate sufficiently to achieve an adherent electrodeposit on the substrate; (c) immersing the cleaned substrate in the electroplating solution; and (d) electrodepositing the coating with the substrate as a cathode at a current density of at least 0.5 A/dm 2 .
Claim 16
Dependent Claim
31 words
The method of claim 11 wherein the electrodeposition of the coating is carried out using a cathodic current density in the range of about 1.6 to about 4 A/dm 2 .
Claim 17
Dependent Claim
59 words
A metallic article provided with an electrodeposited coating according to the methods of claim 11, said coating comprising about 70% to about 99.5% by weight of zinc, about 0.1% to about 10% by weight of silicon, and about 0.5% to about 20% by weight of phosphorus, thus providing a coating with improved corrosion, galling, wear and stress corrosioncracking resistance.
Claim 18
Dependent Claim
39 words
A metallic article according to claim 13, wherein the coating comprises about 90% to about 96% by weight of zinc, about 2% to about 5% by weight of silicon, and about 2% to about 5% by weight of phosphorus.
Claim 19
Dependent Claim
31 words
A metallic article according to claim 13, wherein the coating comprises zinc, silicon, phosphorus with the weight ratio of zinc: silicon: phosphorus in the range of about 90:5:5 to about 96:2:2.
Claim 20
Dependent Claim
138 words
A method of producing a solution suitable for electrodepositing the coating of claim 15, the method comprising: (a) contacting metallic zinc with phosphoric acid and sodium hydroxide until 0.7 moles of sodium hydroxide per mole of phosphoric acid has been added; (b) allowing the reaction to proceed until the pH is in the range of about 2.0 to 2.3; (c) removing the residual metallic zinc from the solution; (d) contacting metallic silicon with phosphoric acid and sodium hydroxide until 0.3 moles of phosphoric acid per mole of sodium hydroxide has been added; (e) allowing the reaction to proceed until the pH reaches 11; (f) removing residual metallic silicon from the solution; (g) adding the silicon-containing solution of the zinc-containing solution such that the ratio of zinc to silicon is 14:1; and (h) adjusting the solution pH to 2.8.
Claim 21
Dependent Claim
30 words
A metallic article according to claim 13, wherein the coating comprises about 93% by weight of zinc, about 4% by weight of silicon, and about 3% by weight of phosphorus.
Claim 22
Dependent Claim
25 words
A metallic article according to claim 13, wherein the coating comprises zinc, silicon and phosphorus wherein the weight ratio of zinc: silicon: phosphorus is 93:4:3.
Claim 23
Independent Claim
104 words
A method to provide a solution suitable for electrodepositing a coating comprising at least about 70% by weight of zinc, at least about 0.1% by weight of silicon, and at least about 0.5% by weight of phosphorus on a metallic substrate, the method comprising: (a) contacting metallic zinc and silicon with phosphoric acid and an aqueous solution of ammonia until between 0.4 and 1.3 moles of ammonia per mole of phosphoric acid has been added; (b) allowing the reaction to proceed until gas evolution ceases; (c) removing residual metallic zinc and silicon from the solution; and (d) adjusting the pH to 2.5 or greater.
Claim 24
Independent Claim
104 words
A method to provide a solution suitable for electrodepositing a coating comprising at least about 70% by weight of zinc, at least about 0.1% by weight of silicon, and at least about 0.5% by weight of phosphorus on a metallic substrate, the method comprising: (a) contacting metallic zinc and silicon with phosphoric acid and an aqueous solution of ammonia until between 0.4 and 1.3 moles of ammonia per mole of phosphoric acid has been added; (b) allowing the reaction to proceed until gas evolution ceases; (c) removing residual metallic zinc and silicon from the solution; and (d) adjusting the pH to 2.5 or greater.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-08-05 | 1989-02-04 | 1989-08-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-08-05 | 1993-02-04 | 1993-08-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-08-05 | 1997-02-04 | 1997-08-06 | $7700.00 | Window Closed / Lapsed |