Method of coating ceramics
Assignee: Vapor Technologies Inc
•
Filing: 1984-06-29
•
Granted: 1985-08-27
•
Expires: 2004-06-29
Abstract
Abstract The adhesion of conductive layers to ceramic substrates in the application of such layers by low-energy techniques is improved by interposing between the high-conductivity metal layer and the substrate a layer of a refractory metal which is preferably also applied by low-energy vaporization. The metal layers can be provided in succession by reversing the polarity of electrodes composed of the metals of these layers which strike an arc vaporizing the metal to be deposited.
Inventors
- 👤 Eduard Pinkhasov
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 13:39
CPC Classifications
F; F03; F03H; F03H99/00; C; C04; C04B; C04B41/00; C04B41/80; C04B41/81; C23; C23C; C23C14/00; C23C14/22; C23C14/24; C23C14/32; C23C14/325; H; H01; H01J; H01J37/00; H01J37/32; H05; H05K; H05K1/00; H05K1/02; H05K1/03; H05K1/0306; H05K3/00; H05K3/38
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
133 words
A method of bonding a high conductivity metal to a ceramic which comprises the steps of: applying to a ceramic substrate a thin bonding layer of a refractory metal; and thereafter applying said high conductivity metal to said layer, each of said metals being applied by striking an arc between a pair of electrodes to vaporize the respective metal from one of said electrodes in an evacuated chamber, an electrode of said refractory metal being juxtaposed with an electrode of said high-conductivity metal, said electrodes being brought into contact and drawn apart to strike said arc, and said electrodes being initially energized with positive and negative polarities in one sense to initially deposit said refractory metal on said substrate and the polarity being thereafter reversed to deposit said high-conductivity metal upon said substrate.
Claim 2
Independent Claim
133 words
A method of bonding a high conductivity metal to a ceramic which comprises the steps of: applying to a ceramic substrate a thin bonding layer of a refractory metal; and thereafter applying said high conductivity metal to said layer, each of said metals being applied by striking an arc between a pair of electrodes to vaporize the respective metal from one of said electrodes in an evacuated chamber, an electrode of said refractory metal being juxtaposed with an electrode of said high-conductivity metal, said electrodes being brought into contact and drawn apart to strike said arc, and said electrodes being initially energized with positive and negative polarities in one sense to initially deposit said refractory metal on said substrate and the polarity being thereafter reversed to deposit said high-conductivity metal upon said substrate.
Claim 3
Dependent Claim
18 words
The method defined in claim 1 wherein said high-conductivity metal is copper, gold, silver or an alloy thereof.
Claim 4
Dependent Claim
21 words
The method defined in claim 2 wherein said refractory metal is tungsten, molybdenum, titanium, zirconium or an alloy or combination thereof.
Claim 5
Dependent Claim
39 words
The method defined in claim 3 wherein said refractory metal is applied to said substrate to a thickness of the order of microns and said high conductivity metal is applied in a thickness of substantially 0.001 to 0.02 inch.
Claim 6
Dependent Claim
36 words
The method defined in claim 4 wherein said high conductivity metal is applied in a thickness of substantially 0.001 to 0.002 inch and said refractory metal is applied in a layer of 5 to 10 microns.
Claim 7
Dependent Claim
18 words
The method defined in claim 5 wherein said high-conductivity metal is copper and said refractory metal is tungsten.
Claim 8
Independent Claim
122 words
A method of bonding a multilayer coating to a substrate which comprises the steps of: juxtaposing electrodes of two different metals with said substrate; bringing said electrodes into contact and drawing them apart to strike an arc while initially energizing said electrodes with positive and negative polarities in one sense to initially deposit metal from one of said electrodes on said substrate; thereafter reversing the polarity applied to said electrodes and bringing them into contact and drawing them apart to strike an arc to vaporize metal from the other of said electrodes and deposit same upon said substrate; and evacuating a chamber in which said arcs are struck to enable deposit of metal from said electrodes upon said substrate in respective layers.
Claim 9
Independent Claim
122 words
A method of bonding a multilayer coating to a substrate which comprises the steps of: juxtaposing electrodes of two different metals with said substrate; bringing said electrodes into contact and drawing them apart to strike an arc while initially energizing said electrodes with positive and negative polarities in one sense to initially deposit metal from one of said electrodes on said substrate; thereafter reversing the polarity applied to said electrodes and bringing them into contact and drawing them apart to strike an arc to vaporize metal from the other of said electrodes and deposit same upon said substrate; and evacuating a chamber in which said arcs are struck to enable deposit of metal from said electrodes upon said substrate in respective layers.
Claim 10
Dependent Claim
12 words
The method defined in claim 7 wherein said substrate is a ceramic.
Claim 11
Dependent Claim
35 words
The method defined in claim 7 wherein said metal of said one of said electrodes is a refractory metal selected from the group which consists of tungsten, molybdenum, titanium, zirconium and alloys and combinations thereof.
Claim 12
Dependent Claim
27 words
The method defined in claim 7 wherein said metal of said other electrode is selected from the group which consists of copper, gold, silver and alloys thereof.
Claim 13
Dependent Claim
55 words
The method defined in claim 7 wherein the metal of said second electrode is applied in a thickness of substantially 0.001 to 0.02 inch to said layer of said metal of said first electrode and said metal of said first electrode is applied to said substrate in a thickness of substantially 5 to 10 microns.
Claim 14
Independent Claim
187 words
A method of applying a multilayer metal coating to a ceramic substrate which comprises the steps of: juxtaposing a pair of electrodes with a ceramic substrate in an evacuated chamber, said electrodes including a first electrode composed of a refractory metal selected from the group which consists of tungsten, molybdenum, titanium, zirconium and alloys and combinations thereof, and a second electrode composed of a high conductivity metal selected from the group which consists of copper, gold, silver and alloys thereof; striking an arc between said electrodes and energizing same electrically initially with positive and negative polarities in a sense so as to vaporize metal from said one of said electrodes in said evacuated chamber and deposit the vaporized metal from said one of said electrodes on said substrate in a layer of a thickness of substantially 5 to 10 microns; and thereafter reversing the polarity of said electrodes and striking an arc between them to vaporize metal from said second electrode in said evacuated chamber thereby depositing said high conductivity metal on said refractory metal on said substrate in a thickness of substantially 0.001 to 0.02 inch.
Claim 15
Independent Claim
187 words
A method of applying a multilayer metal coating to a ceramic substrate which comprises the steps of: juxtaposing a pair of electrodes with a ceramic substrate in an evacuated chamber, said electrodes including a first electrode composed of a refractory metal selected from the group which consists of tungsten, molybdenum, titanium, zirconium and alloys and combinations thereof, and a second electrode composed of a high conductivity metal selected from the group which consists of copper, gold, silver and alloys thereof; striking an arc between said electrodes and energizing same electrically initially with positive and negative polarities in a sense so as to vaporize metal from said one of said electrodes in said evacuated chamber and deposit the vaporized metal from said one of said electrodes on said substrate in a layer of a thickness of substantially 5 to 10 microns; and thereafter reversing the polarity of said electrodes and striking an arc between them to vaporize metal from said second electrode in said evacuated chamber thereby depositing said high conductivity metal on said refractory metal on said substrate in a thickness of substantially 0.001 to 0.02 inch.
References Cited (Backward Citations)
FR822793A
Cited
US2588421A
Cited
FR979772A
Cited
GB889018A
Cited
US3010009A
Cited
US3340084A
Cited
FR1400961A
Cited
GB1061949A
Cited
US3491015A
Cited
DE1648968A1
Cited
GB1322670A
Cited
GB1392583A
Cited
GB1447224A
Cited
GB1452720A
Cited
US4197175A
Cited
GB2010919A
Cited
GB2055403A
Cited
GB2058843A
Cited
GB2106545A
Cited
GB2093484A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-08-26 | 1989-02-25 | 1989-08-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-08-26 | 1993-02-25 | 1993-08-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-08-26 | 1997-02-25 | 1997-08-27 | $7700.00 | Window Closed / Lapsed |