Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for producing magnetic powder and product
Assignee: Ishihara Sangyo Kaisha Ltd
•
Filing: 1983-04-05
•
Granted: 1985-09-03
•
Expires: 2003-04-05
Abstract
Abstract A process for producing a magnetic powder which comprises coating the particle surfaces of a magnetic iron oxide with a cobalt compound or a cobalt compound and a ferrous compound and further coating with a compound of at least one metal selected from the group consisting of manganese, vanadium and zinc. There is obtained a magnetic powder having high coercivity and excellent dispersibility in organic binders. This magnetic powder is useful as a material for recording media such as magnetic tapes.
Inventors
- 👤 Kazuo Nakata
- 👤 Masatsuyo Maruo
- 👤 Kiyoshi Asano
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 23:23
CPC Classifications
C; C09; C09C; C09C1/00; C09C1/22; C09C1/24; G; G11; G11B; G11B5/00; G11B5/62; G11B5/68; G11B5/70; G11B5/706; G11B5/70626; G11B5/70642; G11B5/70652; G11B5/70657; C01; C01P; C01P2006/00; C01P2006/12; C01P2006/42; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2982; Y10T428/2991
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
69 words
A process for producing a magnetic powder which comprises the two steps of first coating the particle surfaces of a magnetic iron oxide with a cobalt compound or a cobalt compound and a ferrous compound and subsequently coating the cobalt compound or cobalt and ferrous compounds-coated surfaces with a compound of at least one metal selected from the group consisting of manganese, vanadium and zinc under a non-oxidizing atmosphere.
Claim 2
Dependent Claim
69 words
A process for producing a magnetic powder which comprises the two steps of first coating the particle surfaces of a magnetic iron oxide with a cobalt compound or a cobalt compound and a ferrous compound and subsequently coating the cobalt compound or cobalt and ferrous compounds-coated surfaces with a compound of at least one metal selected from the group consisting of manganese, vanadium and zinc under a non-oxidizing atmosphere.
Claim 3
Dependent Claim
34 words
The process of claim 1, wherein the coated amount of the cobalt compound is 0.5 to 10% by weight calculated as Co based on the total amount of Fe in said magnetic iron oxide.
Claim 4
Dependent Claim
48 words
The process of claim 1, wherein the coated amounts of the cobalt compound and the ferrous compound are 0.5 to 10% by weight calculated as Co and 1 to 20% by weight calculated as Fe, respectively, based on the total amount of Fe in said magnetic iron oxide.
Claim 5
Dependent Claim
33 words
The process of claim 1, wherein coating of a cobalt compound or a cobalt compound and a ferrous compound is accomplished under a non-oxidizing atmosphere at a temperature of 10° to 60° C.
Claim 6
Dependent Claim
35 words
The process of claim 1, wherein coating of a cobalt compound or a cobalt compound and a ferrous compound is accomplished under a non-oxidizing atmosphere at a temperature from 60° C. to the boiling point.
Claim 7
Dependent Claim
62 words
The process of claim 1, wherein the slurry of said magnetic iron oxide after coating of a cobalt compound or a cobalt compound and a ferrous compound is aged under a non-oxidizing atmosphere in an alkali concentration range from an around neutral pH value to 2 mol/1 of a free OH group concentration and at a temperature of 10° to 60° C.
Claim 8
Dependent Claim
80 words
The process of claim 1, wherein in the course of or after aging of the slurry of said magnetic iron oxide which has gone through coating of a cobalt compound or a cobalt compound and a ferrous compound, said slurry is added with a water-soluble compound of at least one metal selected from the group consisting of manganese, vanadium and zinc under a non-oxidizing atmosphere so that said compound is coated on the particle surfaces of said magnetic iron oxide.
Claim 9
Dependent Claim
90 words
The process of claim 1, wherein the slurry of said magnetic iron oxide after coating of a cobalt compound or a cobalt compound and a ferrous compound is filtered and washed with water to form wet cakes and said wet cakes are dispersed in water to form a slurry to which is added a water-soluble compound of at least one metal selected from the group consisting of manganese, vanadium and zinc under a non-oxidizing atmosphere to effect coating of said compound on the particle surfaces of said magnetic iron oxide.
Claim 10
Dependent Claim
55 words
The process of claim 1, wherein coating of a compound of at least one metal selected from the group consisting of manganese, vanadium, and zinc is made in an alkali concentration range from an around neutral pH value to 2 mol/1 of a free OH group concentration at a temperature of 10° to 60° C.
Claim 11
Dependent Claim
58 words
The process of claim 1, wherein coating of a compound of at least one metal selected from the group consisting of manganese, vanadium, and zinc is made in an alkali concentration range from an around neutral pH value to 2 mol/1 of a free OH group concentration at a temperature of from 60° C. to the boiling point.
Claim 12
Dependent Claim
33 words
The process of claim 1, containing magnanese compound and wherein the manganese compound is coated in an amount of 0.5 to 5% by weight, calculated as Mn, based on said magnetic iron oxide.
Claim 13
Dependent Claim
33 words
The process of claim 1, containing vanadium compound and wherein the vanadium compound is coated in an amount of 0.1 to 2% by weight, calculated as V, based on said magnetic iron oxide.
Claim 14
Dependent Claim
33 words
The process of claim 1, containing zinc compound and wherein the zinc compound is coated in an amount of 0.5 to 5% by weight, calculated as Zn, based on said magnetic iron oxide.
Claim 15
Dependent Claim
32 words
The process of claim 1, wherein a heat treatment follows the step of coating of a compound of at least one metal selected from the group consisting of manganese, vanadium and zinc.
Claim 16
Dependent Claim
25 words
The process of claim 14, wherein the heat treatment comprises heating in the presence of water vapor at a temperature of 60° to 200° C.
Claim 17
Dependent Claim
9 words
A product obtained by the process of claim 1.
Claim 18
Dependent Claim
9 words
A product obtained by the process of claim 6.
Claim 19
Dependent Claim
9 words
A product obtained by the process of claim 7.
Claim 20
Dependent Claim
9 words
A product obtained by the process of claim 8.
Claim 21
Dependent Claim
9 words
A product obtained by the process of claim 14.
Claim 22
Dependent Claim
10 words
A process consisting essentially of the steps of claim 1.
References Cited (Backward Citations)
US4125474A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-09-02 | 1989-03-04 | 1989-09-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-09-02 | 1993-03-04 | 1993-09-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-09-02 | 1997-03-04 | 1997-09-03 | $7700.00 | Window Closed / Lapsed |